Laser cladding is a promising surface treatment for refurbishing worn-out cast-iron brake rotors. Previous studies on laser-cladded brake rotors have demonstrated their extensively higher wear and greater airborne particle emissions, compared with traditional cast iron rotors. In order to overcome this, a commercial non-asbestos organic (NAO) brake material is tested against Fe-based laser-cladded and traditional cast-iron brake rotors. Two low-metallic brake pad materials are also tested as references. The materials’ coefficients of friction, specific wear rates and particle number concentrations are evaluated. The results indicate that the NAO brake material showed lower wear and had fewer particle emissions than the low-metallic brake materials when deployed against both cast iron and laser-cladded brake rotors. The NAO/laser-cladding friction pairing showed wear, particle concentration and fraction of fine particles (sub 1 μm) equivalent to those of the low-metallic/cast-iron friction pairing, creating significant potential for application in refurbishing worn-out cast-iron brake rotors.

In this study, graphitic carbon nitride (g-C₃N₄, labelled as gCN) was tested in the formulation of copper-free (Cu-free) friction mixtures, which are potentially interesting for brake pad manufacturing. Three formulations of friction composites were prepared starting from a common Cu-free master batch: (i) without graphite, (ii) with graphite and (iii) with gCN. The mixtures were pressed in the form of pins by hot-press moulding. The friction-wear performance of the prepared pins was investigated using a pin-on-disc (PoD) test at room temperature (RT), high temperature (HT) (400 °C) and, again, at room temperature (H-RT). The values of the friction coefficient (µ) for the composites with gCN (or graphite) were as follows: (i) RT test, µ_RT = 0.52 (0.47); (ii) HT test, µ_HT = 0.37 (0.37); (iii) RT after the HT tests, µ_H-RT = 0.49 (0.39). With respect to wear resistance, the samples with graphite performed better than the samples without this solid lubricant. To the best of our knowledge, this is the first report regarding the evaluation of the role of gCN in friction composites designed for automotive brake lining applications. The results indicate the main role of gCN as a soft abrasive.

The aim of our research was to indicate the suitability of metallurgical slags (two blast furnace slags and one steel furnace slag) as the components of Cu-free friction materials. The base mixture consisted of nine components including phenolic resin, graphite, tin sulphide, steel and aramid fibers, iron powder, a mixture of barite with calcite, and vermiculite. To this base mixture, the slags with a particle size below 0.1 mm were added individually in the amount of 20 wt.%. A base friction mixture with alumina in the amount of 20 wt.% represented the reference. Samples for the friction-wear tests were produced in the form of pins by hot press molding. The prepared pins were tested using a pin-on-disc tester in a drag mode at the pressure of 1 MPa and a constant sliding speed of 1.51 m/s for 90 min. The samples with slags exhibited slightly lower values of steady-state friction coefficient compared to the reference composite with alumina, and at the same time produced lower wear particle emissions. The particle concentration was reduced for the samples with slowly cooled blast furnace and steel furnace slag. The results obtained indicated steel furnace slag as a promising component of Cu-free friction composites.

With recycling and reuse in mind, this study explores the possibility of the utilization of waste generated during the plasma cutting operations to produce aluminum products in a commercial friction material formulation for car braking applications. The as-received waste, analyzed in the form of a powder, was subjected to various characterization techniques to obtain its composition and phase constituents. The friction, wear, and emission analyses were organized in two ways: the first part focused on the selection of the most suitable waste content in the friction material formulation—10, 15, and 20 wt.%—tested in the form of pins, using a pin-on-disc tribometer. The second part evaluated the most suitable content in the formulation in the form of coupons on a subscale dynamometer to comprehend its friction and emission characteristics in a more complex scenario. Through the pin-on-disc analysis, it was seen that the 10 wt.% of waste in the formulation provided permissible friction and wear behavior, and similar emission magnitude and secondary plateau characteristics were seen, as compared to the reference composition. Similar results were recorded on the subscale dynamometer at mild braking conditions. At ‘severe’ testing conditions, a different trend was observed. Through this analysis, the possibility of the addition of this kind of waste in friction material composition has been evaluated deeply, paving a path for further analysis and possible implementation.