Calcium alginate capsules within asphalt concrete can gradually release interior asphalt rejuvenator under cyclic loading to repair micro cracks and rejuvenate aged asphalt in-situ. However, asphalt pavement will become aged due to environmental and traffic factors during the service period. In view of this, this paper investigated the effect of ageing on the healing properties of asphalt concrete containing calcium alginate/attapulgite composite capsules under cyclic loading. The capsules were fabricated using the orifice-bath method and the morphological structure, mechanical strength, thermal stability, oil release ratios and healing levels of capsules in fresh, short-term ageing and long-term ageing asphalt concrete were explored. The results indicated that the different ageing treatments would not damage the multi-chamber structure nor decrease the mechanical strength of capsules but would induce the capsules release oil prematurely. The premature oil released from capsules in turn can offset the ageing effect owing to ageing treatment. The short-term ageing and long-term ageing plain asphalt mixtures gained strength recovery ratios of 39.3% and 34.2% after 64,000 cycles of compression loading, while the strength recovery ratios of short-term ageing and long-term ageing asphalt mixtures containing capsules were 63.5% and 54.8%, respectively.

Calcium alginate capsules encapsulating rejuvenator are a promising self-healing technology for asphalt pavement, but the effects of different healing agents on the self-healing performance of asphalt concrete has not been considered. In view of this, this paper aimed at exploring the effects of calcium alginate capsules containing different healing agents on the self-healing properties of asphalt concrete. Three types of capsules with sunflower oil, waste cooking oil and commercial rejuvenator were fabricated via the orifice-coagulation bath method and the interior structure, mechanical strength, thermal stability and oil content of the prepared capsules were characterized. The healing levels of asphalt mixtures with different capsules under different loading cycles and stress levels were evaluated. Furthermore, the saturates, aromatics, resins and asphaltenes (SARA) fractions and rheological property of extracted asphalt binder within test beams with different capsules after different loading conditions were assessed. The results indicated that all the three types of capsules meet the mechanical and thermal requirement of mixing and compaction of asphalt mixtures. The healing levels of test beams containing vegetable oil capsules were higher than that of waste cooking oil capsules and industrial rejuvenator capsules. The strength recovery ratio and fracture energy recovery ratio of test beams with vegetable oil capsules reached 82.8% and 96.6%, respectively, after 20,000 cycles of compressive loading at 1.4 MPa. The fracture energy recovery ratio of the waste cooking oil capsules also reached as high as 90%, indicating that waste cooking oil can be used as the healing agent of calcium alginate capsules to improve the self-healing property of asphalt mixture. This work provides a significant guide for the selection of healing agent for self-healing capsules in the future.

Calcium alginate capsules containing rejuvenators represent a promising method for asphalt concrete premaintenance, but their healing capacities under lower temperature conditions are still unknown. This paper investigated the healing performance of asphalt concrete containing calcium alginate capsules at low service temperatures. The Ca-alginate capsules were synthesized, and their morphology, compressive strength, thermal resistance, and relative oil content were evaluated. Besides, evaluations for the healing of asphalt concrete and the rejuvenator-release ratio of the capsules were determined via fracture-healing-refracture testing and Fourier-transform infrared spectrum experiments. Meanwhile, the glass transition temperature and rheological property of asphalt binder after compressive loading under different temperatures were explored via a differential scanning calorimeter and dynamic shear rheometer. The results showed that the capsules had good thermal resistance and mechanical strength. The capsules released less oil under −15, −10, and −5 °C than at 20 °C, and the healing ratios of the asphalt concrete with the capsules at −15, −10, and −5 °C were obviously lower than that at 20 °C. The released rejuvenator from the capsules could decrease the complex modulus and glass transition temperature of the asphalt binder. When compared with low service temperatures, the asphalt binder containing the capsules and serving at a high temperature has a better softening effect and low-temperature performance due to more oil being released.

Induction healing technology can effectively repair microcracks in asphalt mixtures and is a promising maintenance technology for asphalt pavements. However, it requires the addition of steel wool fibers to asphalt mixtures and cannot be directly used to repair existing pavements. In order to improve the practicality of the induction healing technology, this article designs a wearing course asphalt mixture with induction healing function that is going to be paved above the existing road surface. The AC-10 asphalt wearing course for induction heating was prepared by adding steel fiber (SF). Analysis of the overall temperature of the surface revealed the unevenness of the temperature distribution, and the healing properties were investigated through protective heating that controlled the maximum temperature of the upper surface. The results show that the addition of SF can improve the high-temperature stability, low-temperature and intermediate-temperature crack resistance, and moisture stability of asphalt wearing courses; however, it has adverse effects on volumetric performance and skid resistance. The heating temperature increases with the increase in SF content, but higher maximum temperature heating rate causes worse heating uniformity and lower healing effect. The maximum heating rate of the sample with 10% SF reaches 3.92 °C/s, while its heating rate at minimum temperature is similar to that of the sample with 6% SF, which is only 0.7 °C/s, indicating the worst heating uniformity. The best healing effect occurs when the maximum temperature of the upper surface reaches 160 °C. The recommended optimal SF content is 6% of the asphalt volume. The asphalt mixture with 6% SF has an appropriate volume performance, moisture stability, and skid resistance; additionally, it has the best high-temperature stability, as well as low-temperature and intermediate-temperature crack resistance. Meanwhile, it also has uniform temperature distribution and efficient healing efficiency.

Polymer Ca-alginate capsules with rejuvenator bring a high healing level for asphalt concrete under dry healing environments; however, the healing levels of bituminous mixtures containing capsules under water healing conditions are still unknown. In view of this, this study aimed at exploring the healing levels of asphalt concrete containing polymer capsules under various solution healing conditions following cyclic loads. This study involved the preparation of capsules, followed by the evaluation of their morphological characteristics, resilience to compression, thermal endurance, and rejuvenator content. The assessment of the healing properties of asphalt concrete utilizing capsules was conducted through a fracture–heal–refracture examination. This study conducted Fourier transform infrared spectrum experiments to determine the rejuvenator release ratio of capsules under dry conditions and the remaining rejuvenator content in extracted bituminous binder from capsule–asphalt concrete after solution treatment. Meanwhile, a dynamic shear rheometer was utilized to investigate the rheological characteristics of asphalt binder. Results revealed that the healing ratios of capsule–asphalt concrete beams under a dry healing environment were significantly higher than that of beams under various solution healing conditions, and the alkali solution has the worst effect on the improvement in healing ratio. The coupled impact of moisture intrusion and ion erosion resulted in an enhancement of complex modulus of asphalt binder while concurrently reducing its phase angle. Consequently, the restorative capacity of the asphalt binder was weakened.