Ambient energy harvesting has great potential to contribute to sustainable development and address growing environmental challenges. Converting waste energy from energy-intensive processes and systems (e.g. combustion engines and furnaces) is crucial to reducing their environmental impact and achieving net-zero emissions. Compact energy harvesters will also be key to powering the exponentially growing smart devices ecosystem that is part of the Internet of Things, thus enabling futuristic applications that can improve our quality of life (e.g. smart homes, smart cities, smart manufacturing, and smart healthcare). To achieve these goals, innovative materials are needed to efficiently convert ambient energy into electricity through various physical mechanisms, such as the photovoltaic effect, thermoelectricity, piezoelectricity, triboelectricity, and radiofrequency wireless power transfer. By bringing together the perspectives of experts in various types of energy harvesting materials, this Roadmap provides extensive insights into recent advances and present challenges in the field. Additionally, the Roadmap analyses the key performance metrics of these technologies in relation to their ultimate energy conversion limits. Building on these insights, the Roadmap outlines promising directions for future research to fully harness the potential of energy harvesting materials for green energy anytime, anywhere.

This paper reports on the deposition and characterization of piezoelectric AlN and Al_XSc_1-XN layers. Characterization methods include XRD, SEM, active thermo probe, pulse echo, and piezometer measurements. A special focus is on the characterization of AlN regarding the mechanical stress in the films. The stress in the films changed between -2.2 GPa (compressive) and 0.2 GPa (tensile) and showed a significant dependence on film thickness. The cause of this behavior is presumed to be the different mean grain sizes at different film thicknesses, with bigger mean grain sizes at higher thicknesses. Other influences on film stress such as the sputter pressure or the pulse mode are presented. The deposition of gradient layers using those influences allowed the adjustment of film stress while retaining the piezoelectric properties.

This paper reports on the deposition and characterization of piezoelectric Al_XSc_1-XN (further: AlScN) films on Si substrates using AlSc alloy targets with 30 at.% Sc. Films were deposited on a Ø200 mm area with deposition rates of 200 nm/min using a reactive magnetron sputtering process with a unipolar–bipolar hybrid pulse mode of FEP. The homogeneity of film composition, structural properties and piezoelectric properties were investigated depending on process parameters, especially the pulse mode of powering in unipolar–bipolar hybrid pulse mode operation. Characterization methods include energy-dispersive spectrometry of X-ray (EDS), X-ray diffraction (XRD), piezoresponse force microscopy (PFM) and double-beam laser interferometry (DBLI). The film composition was Al_0.695Sc_0.295N. The films showed good homogeneity of film structure with full width at half maximum (FWHM) of AlScN(002) rocking curves at 2.2 ± 0.1° over the whole coating area when deposited with higher share of unipolar pulse mode during film growth. For a higher share of bipolar pulse mode, the films showed a much larger c-lattice parameter in the center of the coating area, indicating high in-plane compressive stress in the films. Rocking curve FWHM also showed similar values of 1.5° at the center to 3° at outer edge. The piezoelectric characterization method revealed homogenous d_33,f of 11–12 pm/V for films deposited at a high share of unipolar pulse mode and distribution of 7–10 pm/V for a lower share of unipolar pulse mode. The films exhibited ferroelectric switching behavior with coercive fields of around 3–3.5 MV/cm and polarization of 80–120 µC/cm².

Although Sc doped AlN (ScAlN) has been used extensively in micro-electro-mechanical systems (MEMS) devices and more recently in optical devices, there have not been thorough studies of its intrinsic optical losses. Here we explore the optical losses of the Sc_0.30Al_0.70N waveguide system by observing racetrack resonator waveguide quality factors. Using a partial physical etch, we fabricate waveguides and extract propagation losses as low as 1.6 ± 0.3 dB/cm at wavelengths around 1550 nm, mostly dominated by intrinsic material absorption from the Sc_0.30Al_0.70N thin film layer. The highest quality factor of the resonators was greater than 87,000. The propagation loss value is lower than any value previously published and shows that this material can be broadly used in optical modulators without significant loss.