The enormous pressures of energy consumption and the severe pollution produced by non-renewable resources have prompted researchers to develop various environmentally friendly energy-saving materials. Transparent bamboo represents an emerging result of biomass material research that has been identified and studied for its many advantages, including light weight, excellent light transmittance, environmental sustainability, superior mechanical properties, and low thermal conductivity. The present review summarizes methods for preparing transparent bamboo, including delignification and resin impregnation. Next, transparent bamboo performance is quantified in terms of optical, mechanical, and thermal conductivity characteristics and compared with other conventional and emerging synthetic materials. Potential applications of transparent bamboo are then discussed using various functionalizations achieved through doping nanomaterials or modified resins to realize advanced energy-efficient building materials, decorative elements, and optoelectronic devices. Finally, challenges associated with the preparation, performance improvement, and production scaling of transparent bamboo are summarized, suggesting opportunities for the future development of this novel, bio-based, and advanced material.

Compared with wood, bamboo has a special fiber gradient structure. Bamboo fibers have attracted attention as reinforced polymer composites. This study investigated the effects of lamination and fiber volume on the physical and mechanical properties of bamboo laminated composites (BLCs). Six types of BLC were derived by parallel and cross laminating bamboo veneers with high, middle, and low fiber volumes. The results indicated that the laminated structure and fiber volume significantly influenced the BLC properties. Microstructural analysis showed that parallel lamination and low fiber volume were more conducive to resin penetration and enhanced the bonding strength. Both the bending and tensile strengths of the cross lamination were lower than those of the parallel lamination. BLCs made of veneers with high and middle fiber volumes and parallel lamination had the maximum bending and tensile strengths (145.1 and 101.53 MPa, respectively). When tested for water resistance, parallel and cross lamination inhibited expansion in the thickness (TSR, 0.56–2.14%) and width (WSR, 0.07–1.61%) directions, respectively. Laminated structures and veneers with varying fiber volume contents should be chosen according to the specific application scenarios. This study provides a reference for selecting an appropriate BLC structure and fiber volume based on application.