Additive manufacturing, including laser powder bed fusion, offers possibilities for the production of materials with properties comparable to conventional technologies. The main aim of this paper is to describe the specific microstructure of 316L stainless steel prepared using additive manufacturing. The as-built state and the material after heat treatment (solution annealing at 1050 °C and 60 min soaking time, followed by artificial aging at 700 °C and 3000 min soaking time) were analyzed. A static tensile test at ambient temperature, 77 K, and 8 K was performed to evaluate the mechanical properties. The characteristics of the specific microstructure were examined using optical microscopy, scanning electron microscopy, and transmission electron microscopy. The stainless steel 316L prepared using laser powder bed fusion consisted of a hierarchical austenitic microstructure, with a grain size of 25 µm as-built up to 35 µm after heat treatment. The grains predominantly contained fine 300–700 nm subgrains with a cellular structure. It was concluded that after the selected heat treatment there was a significant reduction in dislocations. An increase in precipitates was observed after heat treatment, from the original amount of approximately 20 nm to 150 nm.

This experimental study focuses on the assessment of mineral additives and their incorporation into cement composites (CC). The assessment was based on a holistic approach to the performance of the durability properties of CC. Environmental suitability was also taken into consideration. In the experiments, cement pastes with w/c ratios of 0.3, 0.4, and 0.5, respectively, were prepared. Natural zeolite (NZ) and densified silica fume (SF) at doses of 7.5 and 15.0 wt.% of cement were used as the investigated (replacement) materials. Their effects (including development over time) on density, strength (flexural and compressive), porosity by water absorption, permeability by rapid chloride penetration (RCP) test, phase content by thermal analysis, and hydration progression, were observed. The results were then used to propose an evaluation approach. Natural zeolite was used for its known pozzolanic activity and classification as a supplementary cementitious material (SCM). In contrast SF acted as a filler in cement pastes, and thus did not have a direct positive effect on durability. The concept of comprehensive analysis for unknown additive classification is proposed to expressly differentiate between SCM, inert, and improving mineral additive. This concept could be applied to the assessment of mineral additives with regards to the durability and suitability of cement composites.

SPD (several plastic deformations) methods make it possible to obtain an ultrafine-grained structure (UFG) in larger volumes of material and thus improve its mechanical properties. The presented work focuses on the structural and mechanical changes of aluminium alloy AlMgSi0.5 (EN AW 6060) during processing by repeated extrusion through the ECAP rectangular channel. After a four-pass extrusion, the samples’ microstructures were observed using an optical microscope, where refinement of the material grains was confirmed. Tensile tests determined the extrusion forces and allowed interpretation of the changes in the mechanical properties of the stressed alloy. The grain size was refined from 28.90 μm to 4.63 μm. A significant improvement in the strength of the material (by 45%) and a significant deterioration in ductility (to 60%) immediately after the first extrusion was confirmed. The third pass through the die appeared to be optimal for the chosen deformation path, while after the fourth pass, micro-cracks appeared, significantly reducing the strength of the material. Based on the measurement results, new analytical equations were formulated to predict the magnitude or intensity of the volumetric and shape deformations of the structural grain size and, in particular, the adequate increase in the strength and yield point of the material.

This paper is focused on the permeability of cement composite samples with various admixtures. Permeability was examined by the rapid chloride permeability test due to the simple and relatively quick performance among the many methods. Permeability is one of the durability parameters considering the pore system of the composite structure. Ion diffusion provides information about inner pore structure by passing a charge through the sample. In real-life conditions, not only chlorides but also other ions can penetrate into the structure and cause corrosion. Various cement supplements were used as admixtures. The reference sample consisted of cement, fine sand, and water, while the rest of the samples consisted of 20% blast furnace slag, bypass dust, eggshells or recycled glass instead of the cement. The results showed lower permeability in samples containing blast furnace slag and eggshells and a higher charge passage in samples with recycled glass and bypass dust than for the reference sample.

Biodegradable zinc-based alloys have recently emerged as promising candidates for temporary biomedical implants due to their favorable biocompatibility, appropriate degradation rate, and relatively simple processing. In this study, the Zn-0.1Mg alloy was investigated after being processed by means of a two-step equal-channel angular pressing (ECAP) route, consisting of the first pass at 150 °C followed by a second pass at room temperature. The mechanical properties were evaluated using uniaxial tensile tests at different strain rates, while the microstructure and phase composition were analyzed using synchrotron hard X-ray diffraction and transmission electron microscopy (TEM). The processed alloy exhibited a remarkable enhancement in both strength and ductility compared to the annealed state. At the lowest applied strain rate, a fracture elongation of up to 240% was achieved at room temperature, representing a unique manifestation of superplasticity under ambient conditions. Diffraction analysis confirmed the stability of the supersaturated Zn matrix with minor Mg₂Zn₁₁ intermetallic phase. TEM observations revealed an ultrafine-grained microstructure and activation of non-basal slip systems, which enabled efficient plastic flow. These findings demonstrate that controlled severe plastic deformation provides an effective pathway for tailoring Zn-Mg alloys, opening opportunities for their use in the next generation of bioresorbable low-to-moderate load orthopedic fixation devices, e.g., plates, screws, suture anchors and craniofacial miniplates.

Each acid mine drainage has a specific composition, but always contains sulphuric acid, dissolved heavy metals, sulphates, iron pre - cipitates and their pH can be very low. The elimination of metals form the acid mine drainage is a severe environmental problem and has been a long-standing major concern to scientists, engineers, industry and governments. Various methods are used for the metals removal from waters, but any of them have been applied under commercial-scale conditions. Mostly studied are chemical and biolog - ical-chemical methods. Main aim of the paper was to interpret the combination of chemical and biological-chemical methods for the heavy metals elimination from the synthetic solution of acid mine drainage, coming from the zinc mine located in Tùnel Kingsmill outlet of the Rio Yaulì (district of Yauli – Perù). The metals selective precipitation as hydroxides (chemical method) and sulphides (biological-chemical method) at the various values of pH acid mine drainage is the fundamental of the examined process. For the hydrogen sulphide production the sulphate-reducing bacteria of genus Desulfovibrio was used. The selective sequential precipitation process reaches the selective precipitation of chosen metals with 97–99% efficiency – Fe, As, Al and Mn in the form of metal hydroxides, Cu and Zn as metal sulphides.