In this study, new composite materials of montmorillonite, biochar, or aerosil, containing metal–organic frameworks (MOF) were synthesized in situ. Overall, three different MOFs—CuBTC, UTSA-16, and UiO-66-BTEC—were used. Obtained adsorbents were characterized using powder X-ray diffraction, thermogravimetric analysis, nitrogen adsorption porosimetry, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and Fourier transform infrared spectrophotometry. Additionally, the content of metallic and nonmetallic elements was determined to investigate the crystalline structure, surface morphology, thermal stability of the obtained MOF-composites, etc. Cyclic CO₂ adsorption analysis was performed using the thermogravimetric approach, modeling adsorption from flue gasses. In our study, the addition of aerosil to CuBTC (CuBTC-A-15) enhanced the sorbed CO₂ amount by 90.2% and the addition of biochar (CuBTC-BC-5) increased adsorbed the CO₂ amount by 75.5% in comparison to pristine CuBTC obtained in this study. Moreover, the addition of montmorillonite (CuBTC-Mt-15) increased the adsorbed amount of CO₂ by 27%. CuBTC-A-15 and CuBTC-BC-5 are considered to be the most perspective adsorbents, capturing 3.7 mmol/g CO₂ and showing good stability after 20 adsorption-desorption cycles.

The purpose of this study was to reveal the effect of printing direction and post-printing conditions on static and fatigue bending characteristics of Ultem 9085 at two stress levels. Right after the printing, the Ultem samples were subjected to three cooling conditions: cooling in the printer from 180 to 45 °C for 4 h, rapid removal from the printer and cooling in the oven from 200 to 45 °C during 4 h, and removal from the printer and cooling at room temperature. Static 3-point bending tests were performed to estimate the flexural characteristics of Ultem 9085 samples after subjecting them to different post-printing conditions. The flexural strain was evaluated and applied for the stress ratios such as 75% and 50% of σ_max. Thus, displacement-controlled fatigue tests were carried out to reveal the effect of post-printing conditions on fatigue bending characteristics. The results obtained for the X and Y printing directions proved that the Ultem samples subjected to the cooling conditions in the printer and the oven had a similar static and fatigue behavior, while a lower performance was obtained for the samples cooled at room temperature. Regardless of the cooling regime, significantly lower bending performance was revealed for the samples printed in the Z-direction since they have intra-layer filaments parallel to the stress plane, and, accordingly, intra-layer adhesion has a crucial influence on mechanical performance.

This article presents an examination of well-controlled patterns created using a Ga⁺-based focused ion beam (FIB) on glass, while silicon substrates were used to evaluate the FIB performance by its achievable feature size versus time constraints. The pattern creation on glass was developed with the aim of studying potential surface-enhanced Raman spectroscopy (SERS) applications. Furthermore, the FIB was used to create dimer systems of periodically and randomly positioned dumbbell-shaped pits on the glass (each dimer occupies an area of 203 × 87 nm²). By following the bitmap pattern files, the FIB ensured there was 3000 dimer fabrication over a 20 × 20 μm² large area, with a pit size and position variation below 10 nm. The article highlights that FIB can be used for precise large-area nano-fabrication. The gold nanoparticle dimers were formed on the prepatterned surface via capillary force-assisted deposition. The fabricated nanostructures were tested in SERS measurements. The enhancement factor for Rhodamine B molecule reached ~10⁵, demonstrating the potential application of the method to create nanostructures in the sensor domain.

This paper presents new thermo-reflective coatings with different properties. Basic, anti-corrosion and self-extinguishing coatings were analyzed. The coatings were obtained with a thickness varying from 1 to 3 mm. The coatings were subjected to detailed tests assessing their physical-mechanical properties, i.e., tensile strength, abrasion, pull-off test, water absorption, vapor permeability and thermal properties, i.e., the thermal performance of the reflective coatings, thermal transmittance, thermogravimetric analysis, differential scanning calorimetry, as well as thermomechanical analysis and thermal conductivity. In addition, the possibility of using such coatings in a wide range of temperatures and during application to various materials used as a substrate, i.e., concrete, metal and rigid polyurethane foam, was tested. The thermal analysis of coatings revealed that materials are stable to temperatures above 200 °C, there are no thermal transitions in the negative temperature region and shrinking in low temperatures is minimal (less than 0.5%). From the data obtained within the framework of this study, it can be concluded that anticorrosive, basic and self-extinguishing coatings are eligible for thermo-insulation applications in temperatures up to 200 °C.