The interaction of silane and water is discussed controversially in literature: some authors suggest monosilane and water react kinetically and sufficiently fast enough to remove water, while others state the reaction occurs only at elevated temperatures. This question is of technological interest for the removal of unavoidable water residues in Ar gases. Thermodynamic calculations show that virtually complete removal of water is expected with superstoichiometric silane addition. However, mass spectrometric and infrared spectroscopic experiments give evidence that the addition of monosilane to such an Ar gas at room temperature is unable to remove residual water, which disagrees with some current hypotheses in the literature. This holds even for very high SiH₄ concentrations up to 2 vol.-%. Silane reacts with water above temperatures of 555 °C, initiated by the thermal decomposition of silane. A cold dielectric barrier discharge-plasma used for silane and water dissociation enhances reactivity similar to elevated temperatures. Fourier-transformed infrared spectroscopy points toward silanol generation at temperatures between 400 and 550 °C, while quadrupole mass spectrometry indicates the creation of SiOH⁺, SiHOH⁺, SiH₂OH⁺, and SiH₃OH⁺. Cold plasmas generate smaller amounts of SiOH⁺, SiHOH⁺, and SiH₂OH⁺ compared to elevated temperatures. Reaction products are hydrogen and nanoscaled particles of non-stoichiometric silicon oxides. The silicon-oxide particles produced differ in elemental composition and shape depending on the prevailing water content during decomposition: SiO _x generated with residual water appears with relatively smooth surfaces, while the addition of water supports the formation of significantly rougher particle surfaces. Higher initial water contents correlate with higher oxygen contents of the particles.

Conventionally, thermal spraying processes are almost exclusively carried out in an air atmosphere. This results in oxidation of the particles upon thermal spraying, and thus, the interfaces of the splats within the coating are oxidized as well. Hence, a full material bond strength cannot be established. To overcome this issue, a mixture of monosilane and nitrogen was employed in the present study as the atomising and environment gas. With this approach, an oxygen partial pressure corresponding to an extreme-high vacuum was established in the environment and oxide-free coatings could be realized. It is shown that the oxide-free particles have an improved substrate wetting behaviour, which drastically increases the adhesive tensile strength of the wire arc sprayed copper coatings. Moreover, the altered deposition conditions also led to a significant reduction of the coating porosity.

Plasma in hydrogen-containing atmospheres is an efficient method for the reduction of iron oxides. Although a vast number of approaches were performed for the reduction of bulk Fe oxides with thermal hydrogen plasmas, there is almost no information about the non-thermal plasma reduction efficiency in the atmospheric pressure range. In the current article we present the reduction of natively oxidized iron surfaces applying a dielectric barrier discharge plasma in an Ar/H₂ atmosphere at 1000 hPa. By varying the surface temperature from 25 to 300 °C, we studied the plasma reduction efficiency, which was then compared with a thermal method. Whereas plasma treatments at 25 °C and 100 °C did not result in the significant reduction of iron oxidized species, experiments at 200 °C and 300 °C yielded a reduction of approximately 88% and 91% of initial oxidized components already after 10 s, respectively. Moreover, we observed an increase in the efficiency with a plasma-thermal reduction in comparison to a thermal method, which was attributed to the presence of atomic hydrogen in the plasma phase. Analysis of morphology revealed the formation of Fe–C structures on surfaces after thermal and plasma-thermal treatments at 200 °C and 300 °C that may be connected with the diffusion of bulk contaminations to the deoxidized surface and reactions between the reduced Fe with plasma-activated adventitious carbon. Conclusively, the plasma was characterized by analyzing the reactive species and the electron temperatures.

Conventional thermal spraying processes are almost exclusively carried out in an air atmosphere, resulting in the oxidation of the particle surfaces and interfaces within the coating and between the substrate and coating. Furthermore, the initial process of surface activation conventionally takes place in an air atmosphere, preventing an oxide-free interfacial transition. Consequently, the application of spraying materials with high oxygen affinity represents a major challenge. To overcome these issues, the present study utilized silane-doped inert gases to create an environment in which the oxygen concentration was equivalent to the residual oxygen content in an extreme high vacuum. By transferring the corundum blasting and coating process (wire arc spraying) to this environment, materials with a high oxygen affinity can be applied without oxidation occurring. For industrial use, this is an interesting prospect, e.g., for repair coatings, as the homogeneity of the composite is improved by a non-oxidized coating. Using the example of arc-sprayed copper coatings, the microstructure and mechanical properties of the coatings were analysed. The results showed that the oxide-free, wire arc sprayed copper coatings exhibited an improved wetting behaviour resulting in a significant reduction of the coating porosity. Moreover, the improved wetting behaviour and led to an increase in the bonding rate and apparent Young’s modulus. Contrary to expectations, the residual stresses decrease although relaxation mechanisms should be inhibited, and possible reasons for this are discussed in the paper.

Due to the high specific surface area of titanium aluminide powders, significant and unavoidable surface oxidation takes place during processing. The resulting oxides disrupt the conventional powder metallurgical process route (pressing and sintering) by reducing the green strength and sintered properties. Oxide-free particle surfaces offer the potential to significantly increase particle bond strength and enable the processing of difficult-to-press material powders. In this work, the effect of milling titanium aluminide powder in a silane-doped atmosphere on the component properties after pressing and the subsequent sintering was investigated. Ball milling was used to break up the oxide layers and create bare metal surfaces on the particles. With the help of silane-doped inert gas, the oxygen partial pressure was greatly reduced during processing. It was investigated whether oxide-free surfaces could be produced and maintained by milling in silane-doped atmospheres. Furthermore, the resulting material properties after pressing and sintering were analysed using density measurements, hardness tests, EDX measurements, and micrographs. It was concluded that ball milling in a silane-doped atmosphere produces and maintains oxide-free particle surfaces. These oxide-free surfaces and smaller particle sizes improve the component properties after pressing and sintering.

Due to the high specific surface area of titanium aluminide powders, significant and unavoidable surface oxidation takes place during processing. The resulting oxides disrupt the conventional powder metallurgical process route (pressing and sintering) by reducing green strength and sintered properties. Oxide-free particle surfaces offer the potential to significantly increase particle bond strength and enable the processing of difficult-to-press material powders. In this work, the effect of milling titanium aluminide powder in a silane-doped atmosphere on the component properties after pressing and subsequent sintering was investigated. Ball milling was used to break up the oxide layers and create bare metal surfaces on the particles. With the help of silane-doped inert gas, the oxygen partial pressure was greatly reduced during machining. It was investigated whether oxide-free surfaces could be produced and maintained by milling in silane-doped at-mospheres. Furthermore, the resulting material properties after pressing and sintering were an-alyzed using density measurements, hardness tests, EDX-measurements and micrographs. It was concluded, that ball milling in a silane-doped atmosphere produces and maintains oxide-free particle surfaces. These oxide-free surfaces and smaller particle sizes improve the component properties after pressing and sintering.