In the present work, the state of the art of the most common additive manufacturing (AM) technologies used for the manufacturing of complex shape structures of graphene-based ceramic nanocomposites, ceramic and graphene-based parts is explained. A brief overview of the AM processes for ceramic, which are grouped by the type of feedstock used in each technology, is presented. The main technical factors that affect the quality of the final product were reviewed. The AM processes used for 3D printing of graphene-based materials are described in more detail; moreover, some studies in a wide range of applications related to these AM techniques are cited. Furthermore, different feedstock formulations and their corresponding rheological behavior were explained. Additionally, the most important works about the fabrication of composites using graphene-based ceramic pastes by Direct Ink Writing (DIW) are disclosed in detail and illustrated with representative examples. Various examples of the most relevant approaches for the manufacturing of graphene-based ceramic nanocomposites by DIW are provided.

The development of dental implantology is based on the detailed study of the interaction of implants with the surrounding tissues and methods of osteogenesis stimulation around implants, which has been confirmed by the increasing number of scientific publications presenting the results of studies related to both the influence of the chemical composition of dental implant material as well as the method of its surface modification on the key operational characteristics of implants. The main materials for dental implant manufacturing are Ti and its alloys, stainless steels, Zr alloys (including ceramics based on ZrO₂), and Ta and its alloys, as well as other materials (ceramics based on Al₂O₃, Si₃N₄, etc.). The review presents alloy systems recommended for use in clinical practice and describes their physical–mechanical and biochemical properties. However, when getting into the body, the implants are subjected to various kinds of mechanical influences, which are aggravated by the action of an aggressive biological environment (electrolyte with a lot of Cl⁻ and H⁺); it can lead to the loss of osteointegration and to the appearance of the symptoms of the general intoxication of the organism because of the metal ions released from the implant surface into the biological tissues of the organism. Since the osteointegration and biocompatibility of implants depend primarily on the properties of their surface layer (it is the implant surface that makes contact with the tissues of the body), the surface modification of dental implants plays an important role, and all methods of surface modification can be divided into mechanical, physical, chemical, and biochemical methods (according to the main effect on the surface). This review discusses several techniques for modifying dental implant surfaces and provides evidence for their usefulness.

Coatings with a thickness from ~40 to ~50 µm on Ti6Al4V titanium alloys were formed by plasma electrolytic oxidation (PEO) in a silicate-hypophosphite electrolyte with the addition of graphene oxide. The PEO treatment was carried out in the anode–cathode mode (50 Hz) at a ratio of anode and cathode currents of 1:1; their sum density was 20 A/dm², and the treatment’s duration was 30 min. The effect of the graphene oxide’s concentration in the electrolyte on the thickness, roughness, hardness, surface morphology, structure, composition, and tribological characteristics of the PEO coatings was studied. Wear experiments, under dry conditions, were carried out in a ball-on-disk tribotester with an applied load of 5 N, a sliding speed of 0.1 m·s⁻¹, and a sliding distance of 1000 m. According to the obtained results, the addition of graphene oxide (GO) into the base silicate-hypophosphite electrolyte leads to a slight decrease in the coefficient of friction (from 0.73 to 0.69) and a reduction in the wear rate by more than 1.5 times (from 8.04 to 5.2 mm³/N·m), with an increase in the GO’s concentration from 0 to 0.5 kg/m³, respectively. This occurs due to the formation of a GO-containing lubricating tribolayer upon contact with the coating of the counter-body in the friction pair. Delamination of the coatings during wear occurs due to contact fatigue; with an increase in the concentration of GO in the electrolyte from 0 to 0.5 kg/m³, this process slows down by more than four times.

Coatings with a thickness from ~40 to ~50 µm on Ti6Al4V titanium alloy were formed by micro-arc oxidation in a silicate-hypophosphite electrolyte with additions of graphene oxide. Micro-arc oxidation treatment was carried out in the anode–cathode mode (50 Hz) with a ratio of anode to cathode currents of 1:1, a total density of 20 A/dm², and a treatment duration of 30 min. The effect of the graphene oxide concentration in electrolytes on the thickness, roughness, hardness, surface morphology, structure, composition of micro-arc oxidation coatings, and its electrochemical corrosion behavior in 3.5% NaCl solution was studied. The input of graphene oxide additives into the base silicate hypophosphite electrolyte led to an increase in the hardness of micro-arc oxidation coatings. Electrochemical polarization studies and impedance data showed that the best characteristics in terms of corrosion-protective ability among coatings formed in electrolytes with graphene oxide additives were those formed in the electrolyte with a graphene oxide concentration of 0.1 g·L^−l. A further increase in the graphene oxide concentration in the electrolyte did not improve the protective properties of micro-arc oxidation coatings.

In this work, we report an available technique for the effective reduction of graphene oxide (GO) and the fabrication of nanostructured zirconia reduced graphene oxide powder via a hydrothermal method. Characterization of the obtained nano-hybrid structure materials was carried out using a scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FTIR). The confirmation that GO was reduced and the uniform distribution of zirconia nanoparticles on graphene oxide sheets during synthesis was obtained due to these techniques. This has presented new opportunities and prospects to use this uncomplicated and inexpensive technique for the development of zirconia/graphene nanocomposite powders.

Coatings with a thickness from 27 to 62 µm on electron beam melted Ti-6Al-4V have been formed by micro-arc oxidation (MAO) in a silicate-hypophosphite electrolyte. MAO tests in the anode-cathode mode (50 Hz) with an anode-to-cathode current ratio of 1:1 and sum current densities 10 and 20 A/dm² were carried out. The duration of the MAO treatment was 30 and 60 min. The effect of the processing parameters on the structural properties of the MAO treated coatings was studied. The current density and treatment time significantly affect the coating thickness and surface roughness. The values of these characteristics increase as the current density increases. The effect of thermal cycling tests on surface morphology, thickness and roughness, and elemental and phase composition of MAO coatings was analyzed. After 50 cycles of thermal cycling from +200 °C to −50 °C, no cracking or delamination of coatings was observed. Coatings formed in 30 min at a current density of 20 A/dm² turned out to be the best in terms of such indicators as surface morphology, thickness, and roughness.