Bobbin tool friction stir welding (BTFSW) utilizes a special tool that possesses two shoulders interconnected by a pin instead of one: the top shoulder and the pin in the conventional FSW tool. This greatly simplifies the kinematics in the otherwise complicated setup of FSW since the bottom shoulder forms the bottom surface of the weld, without the need for a backing plate. Moreover, the tool enters the base metal sideways and travels, forming the joint in a straight line while rotating, without the need for downward and upward motion at the beginning and end of the process. This paper presents a study on the BTFSW tool geometry and parameters on the risk of wormhole defect formation in the AA5005 aluminum–magnesium alloy and the wormhole effect on mechanical properties. It was shown that higher stress imposed by the tool geometry on the joint has a significant influence on heating, an effect similar to the increased rotational speed. Optimal kinematic and geometrical tool properties are required to avoid wormhole defects. Although weld tensile strengths were lower (between ~111 and 115 MPa) compared with a base metal (137 MPa), the ductile fracture was obtained. Furthermore, all welds had a higher impact strength (between ~20.7 and 27.8 J) compared with the base material (~18.5 J); it was found that the wormhole defect only marginally influences the mechanical properties of welds.

Bobbin tool friction stir welding (BTFSW) is a variant of the FSW process which uses the special two-shoulder tool that forms the top and bottom of a weld surface. As such, a significant simplification of the welding setup is achieved. One of the dominant parameters of the BTFSW process is the interference between the tool shoulder pinch gap and the weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact, and bend performance were studied, and appropriate correlations were devised. The base metal was an aluminum–magnesium alloy in which the interference varied in the range of 0.1 to 0.5 mm. Wormhole defects and irregularities were found in all specimens except in the specimen welded with 0.4 mm interference. An optimal interference of 0.4 mm resulted in the best mechanical properties, which, in terms of tensile strength and reduction of area, were similar to the base metal. Furthermore, the impact strength was significantly higher, which was attributed to the grain refinement effect in the nugget zone.

As far as machine parts are concerned, accuracy can be defined in many aspects. In order for a workpiece to be functional, dimensional and surface roughness requirements are not enough. Accuracy of geometric elements and position...

The aim of this paper is to examine the metrological characteristics of some of the most commonly used coordinate measurement systems in industry in a case study of the flatness error. The accuracy and measurement uncertainty of the coordinate measur...

Bobbin Tool Friction Stir Welding (BTFSW) is a variant of FSW process using the special two shoulder tool that forms the top and bottom weld surface. As such, a significant simplification of welding setup is achieved. One of the dominant parameters of BTFSW process is the interference between tool shoulder pinch gap and weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact and bend performance were studied, and appropriate correlations were devised. The base metal was aluminum-magnesium alloy, with the interference varied in the range of 0.1 to 0.5 mm. The worm defects and irregularities were found in all specimens except in specimen welded with 0.4 mm interference. Optimal interference of 0.4 mm resulted in the highest mechanical properties, which, in terms of tensile strength and reduction of area were similar to the base metal. Furthermore, impact strength was significantly higher, which was attributed to grain refinement effect in the nugget zone.