Epoxy composites play a crucial role in modern materials technologies, with their exceptional properties such as high strength and thermal and chemical resistance, making them ideal for a wide range of industrial applications, including aerospace, automotive, construction, and energy. This review article provides a comprehensive overview of the current trends and advancements in epoxy composites, focusing on mechanical properties and their optimization. Attention is given to technological innovations, including the use of nanotechnologies, hybrid reinforcement, and eco-friendly materials, which are key to enhancing the performance and sustainability of these materials. The analysis shows that the introduction of nanomaterials, such as graphene, titanium dioxide, and silicon dioxide, can significantly improve the strength, fatigue resistance, and electrical properties of epoxy composites, opening new possibilities in advanced technologies. Another significant contribution is the development of hybrid composites, which combine different types of fibers, such as carbon, aramid, and glass fibers, enabling the optimization of key properties, including interlayer strength and delamination resistance. The article also highlights the importance of environmental innovations, such as bio-based resins and self-healing mechanisms, which enable more sustainable and long-term effective use of composites. The combination of theoretical knowledge with practical applications provides valuable guidance for designing materials with precisely defined properties for future industrial use. This text thus offers a comprehensive view of the possibilities of epoxy composites in the context of increasing demands for performance, reliability, and environmental sustainability.

This article presents a comprehensive analysis of polyamide 6 (PA6) and polyamide 12 (PA12) composites fabricated using additive manufacturing technologies such as Selective Laser Sintering (SLS) and Multi Jet Fusion (MJF). It focuses on the mechanical properties, preparation processes, and the influence of technological parameters on the final material characteristics. PA6 is characterized by a higher degree of crystallinity, contributing to its strength and resistance to high temperatures, whereas PA12 exhibits a more amorphous structure, offering better dimensional stability and lower moisture absorption. The article examines these properties and their implications for the use of composites in various applications. Applications of PA6 and PA12 composites span a wide range of industries, including automotive, aerospace, and electronics, where they provide a combination of high strength, wear resistance, and chemical stability. Mechanical properties, such as tensile strength and toughness, are analyzed within the context of modern manufacturing processes, with MJF technology delivering more homogeneous properties compared to traditional methods. The preparation process of these composites involves optimizing temperature, cooling rates, and material layering, which significantly impact the final properties and the applicability of the composites.

The present review deals with the issues of ensuring and maintaining high reliability during the entire life cycle of a technical system in the engineering sector, i.e., determining the requirements, design, research, development, production, installation, operation, and disposal of the product. Owing to their reliability, special attention is given to the technical systems in companies for several reasons. These mainly include the need to achieve reliability and safety by using the product, but also in terms of economic, social, and ecological aspects. We understand reliability as a primary feature, and during the design of new products, it is necessary to predict its course and characteristics appropriately. Reliability needs to be analyzed with the help of partial reliability properties throughout the entire life cycle of the product. To achieve the required level of reliability, we use reliability analyses, which are successfully implemented to examine and predict reliability indicators. The present review provides a comprehensive overview of reliability analysis and offers a mathematical basis for individual sub-indicators. In the article, the analysis of system reliability is described as a process, the essence of which is the acquisition, examination, and organization of specific information. This information is significant for the given system and necessary for making decisions according to the specified goals, which ensure an objective assessment of the overall level of reliability.

The present article examines special steels used for the production of injection screws in the plastic industry, with a glass fiber content of up to 30%. Experimental materials, M390 and M398, are classified as tool steels, which are produced by powder metallurgy-HIP methods (hot isostatic pressing). The main goal of the presented paper is to propose the optimal tempered temperature of M398 steel and also to compare the tribological properties of both materials and to determine the degree of their wear depending on their final heat treatment. Partial results refer to the analysis of hardness, roughness, the overall wear mechanism, the change in the volume of retained austenite due to the tempering temperature, and the EDS analysis of the worn surfaces in individual contact pairs. A ceramic ball Al₂O₃ in the α phase was used as the contact material, which had a diameter of 6.35 mm. The ceramic ball performed a rotational movement on the experimental material surface at an elevated temperature of 200 °C using the dry ball-on-disk method. It was experimentally shown that the new M398 material can fully replace the M390 material because it exhibits significantly better tribological properties. The M398 material showed more than a 400% reduction in wear compared to the M390 material. The ideal heat treatment consisted of cryogenic quenching to −78 °C and a tempering temperature of 400 °C. At tempering temperatures of 200 and 400 °C, adhesive wear occurred, which was combined with abrasive wear at a tempered temperature of 600 °C. The averaged coefficient of friction (COF) results show that the M398 material presents less resistance in the friction process and its values are approximately 0.25, while the M390 material showed a COF value of 0.3 after the cryogenic hardening process. The friction surface roughness of the M398 materials also showed lower values compared to the M390 material by approximately 35%. Both of these results are related to the content of M₇C₃ and MC carbide particles based on Cr and V in the bulk of the material, which are in favor of the M398 material.

Experiments with changes in motion geometry can provide valuable data for engineering and development purposes, allowing a better understanding of the influence of tribological factors on the performance and service life of joints. The presented subject article focused on the experimental investigation of the influence of the geometry of the movement of the friction process on the change in the tribological properties of 30CrNiMo8 steel. The friction process was carried out without the use of a lubricant in contact with a steel ball of G40 material with a diameter of 4.76 mm. The steel ball performed two types of movement on the surface of the experimental material. The first method used was ball on disc, in which the ball moved reciprocally in an oval direction at an angle of 180° on a circumferential length of 35 mm at a speed of 5 mm/s. The second method consists of the same input parameters of the measurement, with the difference that the path along which the ball moved had a linear character. The load during the experiment was set at a constant value of 50 N with 1000 repetitions. The results show that with the ball on disc method, there was an increase in wear by 147% compared to the linear test method, which was approximately a coefficient of increase in wear of 2.468. EDS analysis pointed to the occurrence of oxidative wear that affected the resulting COF values, which were lower by 8% when using the ball on disc method due to a more uniform distribution of O and C on the surface of the friction groove where these elements acted as solid microlubricants. With the ball on disc method, defects in the form of microcracks occurred, which affected the reduction in the values of the depth of the affected area of microhardness.

The application of DCSBD (Diffuse Coplanar Surface Barrier Discharge) plasma is referred to as the surface modification/activation of materials. The exposure of material surfaces to DCSBD plasma is initiated by changes in their chemical composition, surface wettability and roughness. The given study presents the mentioned plasma application in the context of the modification of the material viscoelastic properties, namely the PVC polymer film. The measurement of viscoelastic properties changes of PVC was primarily examined by a sensitive thermal method of dynamic-mechanical analysis. This analysis allows identifying changes in the glass transition temperature of PVC, before and after DCSBD plasma application, Tangens Delta, supported by glass transition temperatures of Elastic and Loss modulus. The results of the present study prove that DCSBD plasma applied on both sides to PVC surfaces causes changes in its viscoelastic properties. In addition, these changes are presented depending on the variability of the material position, with respect to the winding of the electrodes in the ceramic dielectric generating the DCSBD plasma during modification. The variability of the PVC position holds an important role, as it determines the proportion of filamentous and diffuse components of the plasma that will interact with the material surface during modification. The application of DCSBD plasma must, therefore, be considered a complex modification of the material, and as a result, non-surface changes must also be considered.