Experiments with changes in motion geometry can provide valuable data for engineering and development purposes, allowing a better understanding of the influence of tribological factors on the performance and service life of joints. The presented subject article focused on the experimental investigation of the influence of the geometry of the movement of the friction process on the change in the tribological properties of 30CrNiMo8 steel. The friction process was carried out without the use of a lubricant in contact with a steel ball of G40 material with a diameter of 4.76 mm. The steel ball performed two types of movement on the surface of the experimental material. The first method used was ball on disc, in which the ball moved reciprocally in an oval direction at an angle of 180° on a circumferential length of 35 mm at a speed of 5 mm/s. The second method consists of the same input parameters of the measurement, with the difference that the path along which the ball moved had a linear character. The load during the experiment was set at a constant value of 50 N with 1000 repetitions. The results show that with the ball on disc method, there was an increase in wear by 147% compared to the linear test method, which was approximately a coefficient of increase in wear of 2.468. EDS analysis pointed to the occurrence of oxidative wear that affected the resulting COF values, which were lower by 8% when using the ball on disc method due to a more uniform distribution of O and C on the surface of the friction groove where these elements acted as solid microlubricants. With the ball on disc method, defects in the form of microcracks occurred, which affected the reduction in the values of the depth of the affected area of microhardness.

The aim of this work is to perform a detailed dilatometric analysis of the decomposition of austenite during the cooling process using experimentally derived continuous cooling transformation (CCT) diagrams for two specific tool steels, X153CrMoV12 Bohdan Bolzano, Bratislava, Slovakia and 100MnCrW4. The dilatometric curves were compared with metallographic evaluations using scanning electron microscopy (SEM). In addition, hardness measurements were performed to obtain additional information about the mechanical properties of the materials. All experimental work was performed using a DIL 805A. The accuracy of the resulting CCT diagrams was verified by comparing them with those calculated with the JMatPro software v12.4. The cooling rates ranged from 20 °C/s to 0.01 °C/s, depending on the specific type of steel tested. The novelty of this research is the combination of experimental and simulation methods to analyze the influence of alloying elements on the kinetics of phase transformations in tool steels. It was found that one of the most significant factors affecting the CCT diagrams is the weight percentage of alloying elements in the steels. These results clearly show that increasing the weight percentage of the content of alloying elements has a significant impact on the accuracy of the simulation results derived from the JMatPro software.

The paper deals with the dilatometric study of high-alloy martensitic tool steel with the designation M398 (BÖHLER), which is produced by the powder metallurgy process. These materials are used to produce screws for injection molding machines in the plastic industry. Increasing the life cycle of these screws leads to significant economic savings. This contribution focuses on creating the CCT diagram of the investigated powder steel in the range of cooling rates from 100 to 0.01 °C/s. JMatPro^® API v7.0 simulation software was used to compare the experimentally measured CCT diagram. The measured dilatation curves were confronted with a microstructural analysis, which was evaluated using a scanning electron microscope (SEM). The M398 material contains a large number of carbide particles that occur in the form of M₇C₃ and MC and are based on Cr and V. EDS analysis was used to evaluate the distribution of selected chemical elements. A comparison of the surface hardness of all samples in relation to the given cooling rates was also carried out. Subsequently, the nanoindentation properties of the formed individual phases as well as the carbides, where the nanohardness and reduced modulus of elasticity (carbides and matrix) were evaluated.

In connection with the growing importance of the efficiency and reliability of tools in industrial sectors, our research represents a key step in the effort to optimize production processes and increase their service life in real conditions. The study deals with the comparison of the tribological properties of three tool steels, two of which were produced by the powder metallurgy method—ASP2017 and ASP2055—and the last tool steel underwent the conventional production method—X153CrMoV12. The samples were mechanically machined with the finishing technology of turning and, finally, heat treated (Q + T). The study focused on the evaluation of hardness, resulting microstructure, wear resistance, and coefficient of friction (COF). The ball-on-disc method was chosen as part of the COF and wear resistance test. The tribological test took place at room temperature with dry friction to accelerate surface wear. The pressing material was a hardened steel ball G40 (DIN 100Cr6). Measurements were performed at loads of 10 N, 6 N, and 2 N and turning radii of 13 mm, 18 mm, and 23 mm, which represents a peripheral speed of 0.34, 0.47, and 0.60 m/s. The duration of the measurement for each sample was 20 min. The results showed that the COF of powder steels showed almost the same values, while a significant difference occurred with the increase of the radius rotation in the case of conventional steel. The results within the friction mechanism showed two types of wear, namely, adhesive and abrasive wear, depending on the Q + T process. From a tribological point of view in terms of wear, it was possible to state that the material ASP2055 after Q + T showed the lowest rate of wear of all the tested steels.

The presented work deals with the study of the effect of increasing the doses of irradiation by accelerated electrons on the sliding properties of polymer materials. Due to the influence of radiation, surface roughness changes occur on the surface of the experimental materials, which lead to changes in the properties of the coefficient of friction on the selected polymer materials. Three types of polymer materials PET, PTFE and PE2000C were used for the experimental research, which, due to their properties, are used for different types of sliding products. A steel ball of G40 material was used as a pressure material, which moved along a linear path on which the load was increased from 10 N to 100 N. Electron beam accelerators with the conversion of electrons to X-rays combine the advantages of a high ability to penetrate gamma photons sources and high performance of electron beam devices. The application possibilities of the device are wide due to the dual mode of operation (electron beam or Xray beam) and a wide range of applicable doses and also dose rates.

Article deals with processing of intermetallic materials produced by powder metallurgy M390 and M398 Microclean® produced by Böhler. Main interest is the analysis & measurement of their surface roughness and topography after the processing by DNMG and WNMG geometry of cutting inserts with 0.4 and 0.8 mm radius after hard turning at the same process parameters for both materials and all types of cutting inserts. The comparative studies were carried out for the microgeometrical and chip formation research on the machined surfaces and the technological processes were assessed, including chip diagrams. Spectral analysis was used to verify the composition of investigated materials by spectral analysis measuring device. In order to examine the surfaces in detail, in addition to the standard roughness measurement, surface topography was performed by the coherent correlation interferometric microscope. The results of surface roughness as well as topography show higher wear resistance of M398 material compared to M390. This was confirmed indirectly by the fact that it is primarily shown by the higher surface roughness of M398 after machining under the same conditions. These properties are obtained by a higher content of additive elements, respectively of their carbides. Based on the conclusions of these experiments, additional knowledge and recommendations for the processing of these materials were created.