Epoxy composites play a crucial role in modern materials technologies, with their exceptional properties such as high strength and thermal and chemical resistance, making them ideal for a wide range of industrial applications, including aerospace, automotive, construction, and energy. This review article provides a comprehensive overview of the current trends and advancements in epoxy composites, focusing on mechanical properties and their optimization. Attention is given to technological innovations, including the use of nanotechnologies, hybrid reinforcement, and eco-friendly materials, which are key to enhancing the performance and sustainability of these materials. The analysis shows that the introduction of nanomaterials, such as graphene, titanium dioxide, and silicon dioxide, can significantly improve the strength, fatigue resistance, and electrical properties of epoxy composites, opening new possibilities in advanced technologies. Another significant contribution is the development of hybrid composites, which combine different types of fibers, such as carbon, aramid, and glass fibers, enabling the optimization of key properties, including interlayer strength and delamination resistance. The article also highlights the importance of environmental innovations, such as bio-based resins and self-healing mechanisms, which enable more sustainable and long-term effective use of composites. The combination of theoretical knowledge with practical applications provides valuable guidance for designing materials with precisely defined properties for future industrial use. This text thus offers a comprehensive view of the possibilities of epoxy composites in the context of increasing demands for performance, reliability, and environmental sustainability.

This article presents a comprehensive analysis of polyamide 6 (PA6) and polyamide 12 (PA12) composites fabricated using additive manufacturing technologies such as Selective Laser Sintering (SLS) and Multi Jet Fusion (MJF). It focuses on the mechanical properties, preparation processes, and the influence of technological parameters on the final material characteristics. PA6 is characterized by a higher degree of crystallinity, contributing to its strength and resistance to high temperatures, whereas PA12 exhibits a more amorphous structure, offering better dimensional stability and lower moisture absorption. The article examines these properties and their implications for the use of composites in various applications. Applications of PA6 and PA12 composites span a wide range of industries, including automotive, aerospace, and electronics, where they provide a combination of high strength, wear resistance, and chemical stability. Mechanical properties, such as tensile strength and toughness, are analyzed within the context of modern manufacturing processes, with MJF technology delivering more homogeneous properties compared to traditional methods. The preparation process of these composites involves optimizing temperature, cooling rates, and material layering, which significantly impact the final properties and the applicability of the composites.

Experiments with changes in motion geometry can provide valuable data for engineering and development purposes, allowing a better understanding of the influence of tribological factors on the performance and service life of joints. The presented subject article focused on the experimental investigation of the influence of the geometry of the movement of the friction process on the change in the tribological properties of 30CrNiMo8 steel. The friction process was carried out without the use of a lubricant in contact with a steel ball of G40 material with a diameter of 4.76 mm. The steel ball performed two types of movement on the surface of the experimental material. The first method used was ball on disc, in which the ball moved reciprocally in an oval direction at an angle of 180° on a circumferential length of 35 mm at a speed of 5 mm/s. The second method consists of the same input parameters of the measurement, with the difference that the path along which the ball moved had a linear character. The load during the experiment was set at a constant value of 50 N with 1000 repetitions. The results show that with the ball on disc method, there was an increase in wear by 147% compared to the linear test method, which was approximately a coefficient of increase in wear of 2.468. EDS analysis pointed to the occurrence of oxidative wear that affected the resulting COF values, which were lower by 8% when using the ball on disc method due to a more uniform distribution of O and C on the surface of the friction groove where these elements acted as solid microlubricants. With the ball on disc method, defects in the form of microcracks occurred, which affected the reduction in the values of the depth of the affected area of microhardness.

The application of DCSBD (Diffuse Coplanar Surface Barrier Discharge) plasma is referred to as the surface modification/activation of materials. The exposure of material surfaces to DCSBD plasma is initiated by changes in their chemical composition, surface wettability and roughness. The given study presents the mentioned plasma application in the context of the modification of the material viscoelastic properties, namely the PVC polymer film. The measurement of viscoelastic properties changes of PVC was primarily examined by a sensitive thermal method of dynamic-mechanical analysis. This analysis allows identifying changes in the glass transition temperature of PVC, before and after DCSBD plasma application, Tangens Delta, supported by glass transition temperatures of Elastic and Loss modulus. The results of the present study prove that DCSBD plasma applied on both sides to PVC surfaces causes changes in its viscoelastic properties. In addition, these changes are presented depending on the variability of the material position, with respect to the winding of the electrodes in the ceramic dielectric generating the DCSBD plasma during modification. The variability of the PVC position holds an important role, as it determines the proportion of filamentous and diffuse components of the plasma that will interact with the material surface during modification. The application of DCSBD plasma must, therefore, be considered a complex modification of the material, and as a result, non-surface changes must also be considered.

The presented study focuses on the study of polylactide acid (PLA) material, which is a frequently used material in 3D printing. Surface modification using DCSBD plasma discharge is proposed as a way to improve the adhesion between individual layers of material. Adhesion is a critical factor for achieving high-quality print output, as low adhesion can cause individual deposited layers of material to separate and ripple during printing. Dynamic Mechanical Analysis (DMA) is used to determine the glass transition temperature (Tg) of a material. Tg is important because it determines how difficult the material is to print, the closer the Tg is to room temperature, the easier the material is to print. However, after printing a layer of material and subsequently cooling it to room temperature, the material begins to shrink and wave due to the change in material expansion. This can have a negative effect on the adhesion between the layers of the material, which can lead to separation of the layers. The presented study tries to find a way to improve the adhesion of individual layers of material. Surface modification by plasma discharge appears to be a promising method that could improve the adhesion between individual layers of PLA material.

In connection with the growing importance of the efficiency and reliability of tools in industrial sectors, our research represents a key step in the effort to optimize production processes and increase their service life in real conditions. The study deals with the comparison of the tribological properties of three tool steels, two of which were produced by the powder metallurgy method—ASP2017 and ASP2055—and the last tool steel underwent the conventional production method—X153CrMoV12. The samples were mechanically machined with the finishing technology of turning and, finally, heat treated (Q + T). The study focused on the evaluation of hardness, resulting microstructure, wear resistance, and coefficient of friction (COF). The ball-on-disc method was chosen as part of the COF and wear resistance test. The tribological test took place at room temperature with dry friction to accelerate surface wear. The pressing material was a hardened steel ball G40 (DIN 100Cr6). Measurements were performed at loads of 10 N, 6 N, and 2 N and turning radii of 13 mm, 18 mm, and 23 mm, which represents a peripheral speed of 0.34, 0.47, and 0.60 m/s. The duration of the measurement for each sample was 20 min. The results showed that the COF of powder steels showed almost the same values, while a significant difference occurred with the increase of the radius rotation in the case of conventional steel. The results within the friction mechanism showed two types of wear, namely, adhesive and abrasive wear, depending on the Q + T process. From a tribological point of view in terms of wear, it was possible to state that the material ASP2055 after Q + T showed the lowest rate of wear of all the tested steels.