The influence of plant fillers on the flammability and smoke emission of natural composites was investigated. Epoxy composites with 15, 25, and 35 wt % of walnut and hazelnut shell, as well as sunflower husk, were prepared and examined. The ground organic components were characterized by grain size distribution, thermogravimetric analysis (TGA) and microstructure observations (SEM). The composite materials were subjected to dynamic mechanical analysis (DMA) and structural evaluation with scanning electron microscopy. Cone calorimeter tests and TGA determined the influence of plant waste filler addition on thermal stability and flammability. Moreover, the semi-volatile and volatile compounds that evolved during the thermal decomposition of selected samples were identified using a steady state tube furnace and a gas chromatograph with a mass spectrometer. The intensity of the degradation reduced as a function of increasing filler content, while the yield of residue corresponded to the amount of lignin that is contained in the tested plants. Moreover, the incorporation of agricultural waste materials resulted in the formation of a char layer, which inhibits the burning process. The yield of char depended on the amount and type of the filler. The composites containing ground hazelnut shell formed swollen char that was shaped in multicellular layers, similar to intumescent fire retardants.

Using one-step method, rigid polyurethane foams were made, modified with developed fire retardant systems containing halogen-free flame retardants and nanofillers in the form of multi-walled carbon nanotubes or nanoscale titanium dioxide. The materials were subjected to a test using a cone calorimeter and smoke-generating chamber, and selected samples were further analyzed via thermogravimetry and oxygen index. Moreover, the products of thermal degradation of selected samples were identified using gas chromatography with mass spectrometer. Conducted flammability tests confirmed the presence of a synergistic effect between the used nanofillers and halogen-free flame retardants. It has been observed that the carbonized layer, the formation of which favored the presence of nanoadditives, inhibits the combustion process. Furthermore, nanofillers influenced favorably reduction in the amount and the number of occurring products of thermal degradation.

This study provides valuable data on the specific toxic products that could be released from the commercially used, flexible polyurethane foams (FPUFs) during a fire. The steady-state tube furnace (Purser furnace) was used to generate combustion and thermal degradation products under different fire conditions. The concentrations of asphyxiates and irritant gases were determined using a Fourier transform infrared spectroscopy gas analyser. The volatile and semi-volatile organic compounds released in the fire effluents were collected using the solid-phase microextraction technique and identified by gas chromatography with a mass selective detector. In addition, the thermal stability of the FPUFs was evaluated by simultaneous thermal analysis. The cone calorimetry test was used to determine the flame retardancy of the selected materials. The obtained results show that the emission of carbon monoxide and hydrogen cyanide during the thermal degradation and combustion of the tested foams exceeded the permissible values and pose a serious threat to human life and health. Moreover, substituted benzenes, aldehydes, and polycyclic hydrocarbons were found in the released gases during all of the test conditions.

Thermal degradation and combustion of pesticides lead to the emission of chemicals that are harmful and dangerous for humans and the environment. The aim of the work was to study thermal decomposition of triadimenol and analyze organic compounds, in particular dioxins precursors released during that process. The thermogravimetry and differential scanning calorimetry method was used to examine the physical and chemical processes occurring under high temperatures in air atmosphere. The application of a simultaneous thermal analyzer combined with an infrared spectrometer allowed to identify substances generated during the experiments. To generate the fire effluents contained in thermal degradation products, the steady-state tube furnace was also used. The gas samples were taken using solid-phase microextraction method. Meanwhile for the detection and identification of released chemicals, the gas chromatograph with mass spectrometer was adopted. The obtained results showed that tested pesticides undergo both thermal decomposition and oxidation during thermal degradation in air. In the gases emitted during thermal decomposition, carbon oxides, hydrogen cyanide and many aliphatic and aromatic compounds were found. However, the main toxic substances identified under all tested conditions were: hydrogen cyanide, 4-chlorophenol and many substituted benzenes and polycyclic hydrocarbons.