New oxychloride lead borate glasses in the xPbCl₂–(50-0.5x)PbO–(50-0.5x)B₂O₃ system were synthesized with a maximum lead chloride content of 40 mol%. The characteristic temperatures and mechanical and optical properties were studied. The incorporation of lead chloride led to a significant expansion of the transparency range in the UV (up to 355 nm) and IR regions (up to 4710 nm). Decreases in the Vickers hardness, density, and glass transition temperature were the consequences of a change in the structure. The studied glasses are promising materials for photonics and IR optics. The structure of the PbCl₂–PbO–B₂O₃ system was analyzed in detail using vibrational spectroscopy and X-ray diffraction.

The influence of the charge treatment by ultrahigh dilution (UHD) technology on oxide single crystals grown by the Czochralski technique was studied for monoclinic MgMoO₄ crystals doped by 1 at. % of Nd³⁺ ions. The series of 10 Nd:MgMoO₄ crystals was grown from the charges that were subjected to UHD treatment, as well as from the charges treated with two types of control or with no special treatment at all. The grown crystals were studied by X-ray powder diffraction analysis, inductively coupled plasma atomic emission spectroscopy, mass-spectrometry, optical absorption, emission spectroscopy and luminescence kinetic analysis. We found that: (i) wetting of MgO + MoO₃ mixture by a water-ethanol solution before calcining leads to some enrichment of the mixture with MoO₃, whereas the wetting of the charge after the calcining leads to some enrichment of it with MgO; (ii) congruent melting composition of MgMoO₄ crystal is in the field of some MoO₃ excess; (iii) the solid-phase solubility of the excess MoO₃ in MgMoO₄ probably does not depend on temperature, whereas the solid-phase solubility of the excess MgO in MgMoO₄ crystal depends on temperature. We suggest that the corresponding solidus line passes through the range of retrograde solubility; (iv) the crystals grown within this range are characterized by the enhanced Nd³⁺ segregation coefficient between the crystal and the melt (approximately 0.006 versus 0.004); (v) unit cell parameters of MgMoO₄ crystal with the excess of MoO₃ are larger than those of the crystal of the stoichiometric composition and of the crystal with the excess of MgO; (vi) the shapes of the optical absorption and luminescence spectra of Nd:MgMoO₄ crystal do not depend on the charge treatment; (vii) luminescence decay kinetics are single-exponential for all the studied crystals, the luminescence decay time being different for the crystals grown from the charges that underwent different types of treatment; (viii) the luminescence intensity of Nd:MgMoO₄ crystal grown from the charge that underwent UHD treatment before calcining (solid-phase synthesis) is reduced by an order of magnitude in comparison with the other studied crystals.