This review discusses the main methods for producing spherical powder particles of corrosion-resistant steels as a material widely used in all industries. Also the examples of products made by modern additive methods are described. Currently, spherical powder particles of corrosion-resistant steels are used in the following additive methods: selective laser melting, selective laser sintering, direct laser sintering, and electron beam melting. Each of these methods has its own requirements for the characteristics of spherical powder particles of corrosion-resistant steels. The review provides a brief description of the principles of operation of each method and the requirements for spherical powder particles of corrosion-resistant steels. It also considers a detailed description of each method of additive manufacturing with a description of the principle of operation and specific examples of obtaining spherical particles of corrosion-resistant steel powders with indication of their properties (morphology, structural features, chemical composition, fluidity, bulk density). A comparative analysis was carried out with a description of disadvantages and advantages of each method. Examples of the use of spherical particles of corrosion-resistant steel powders for the manufacture of products by various additive methods (including post-processing) are given with description of the final products characteristics. Based on the data presented, a conclusion was made about the preferred methods for obtaining spherical particles of corrosion-resistant steel powders for specific additive methods used in modern industry. The review considers the following methods for producing spherical powder particles: water atomization (atomization of liquid metal with a jet of water under pressure); gas atomization (atomization of the melt with a jet of inert gas (argon or nitrogen) under pressure); centrifugal atomization (atomization of molten metal with a high-speed rotating disc); ultrasonic atomization (atomization of liquid metal by ultrasound); non-contact atomization (atomization of liquid metal with a powerful pulse of electric current); plasma wire spraying; plasma spraying of a rotating electrode; plasma spheroidization.

The work described in this article is aimed at investigating the properties of a group of Ti-Zr-Nb alloys. In modern orthopedics and traumatology, the use of materials for bone implants with a minimum modulus of elasticity is becoming increasingly important. This is due to a number of advantages that allow for better integration of the implants with the bone tissue, including the reduction in the detrimental effect of the load-shielding effect, a better load distribution, and stress distribution, which allows for increasing the life of the implant. It is known that the lowest modulus of elasticity in titanium alloys at normal temperature is achieved by the phase composition consisting of metastable β-phase. It is possible to achieve the desired structure by a combination of alloy composition selection and heat treatment. Quenching of titanium alloys allows for the high-temperature β-phase to be fixed. This paper provides justification of the choice of compositions of the studied alloys by calculation methods. The structure of alloys after melting in a vacuum electric arc furnace in an argon environment was studied. The ingots obtained had a dendritic structure. Homogenizing annealing in a vacuum furnace at 1000 °C for 4 h was used to equalize the composition. The structure of the alloyed sheets after hot rolling and hot rolling and quenching was investigated. The microstructure of the plates in both variants had uniform grains of polyhedral shape. X-ray phase analysis of the plates showed that the content of metastable β-phase was 100% before and after quenching. Microhardness testing of the plates showed no significant effect of quenching. The result of the mechanical properties study showed an increase in the plasticity of the material after quenching, with the tensile plots of the samples after quenching reflecting the area where the reverse phase transition of β’<-> α’’ occurs. Mechanical studies by cyclic loading showed the presence of a superelasticity effect. The Young’s modulus study gave a result of 51 GPa for one of the compositions studied. The combination of properties of the materials under investigation has the potential for promising use as a basis for bone implants.

Foodborne infections are an important global health problem due to their high prevalence and potential for severe complications. Bacterial contamination of meat during processing at the enterprise can be a source of foodborne infections. Polymeric coatings with antibacterial properties can be applied to prevent bacterial contamination. A composite coating based on fluoroplast and Ag₂O NPs can serve as such a coating. In present study, we, for the first time, created a composite coating based on fluoroplast and Ag₂O NPs. Using laser ablation in water, we obtained spherical Ag₂O NPs with an average size of 45 nm and a ζ-potential of −32 mV. The resulting Ag₂O NPs at concentrations of 0.001–0.1% were transferred into acetone and mixed with a fluoroplast-based varnish. The developed coating made it possible to completely eliminate damage to a Teflon cutting board. The fluoroplast/Ag₂O NP coating was free of defects and inhomogeneities at the nano level. The fluoroplast/Ag₂O NP composite increased the production of ROS (H₂O₂, OH radical), 8-oxogualnine in DNA in vitro, and long-lived active forms of proteins. The effect depended on the mass fraction of the added Ag₂O NPs. The 0.01–0.1% fluoroplast/NP Ag₂O coating exhibited excellent bacteriostatic and bactericidal properties against both Gram-positive and Gram-negative bacteria but did not affect the viability of eukaryotic cells. The developed PTFE/NP Ag₂O 0.01–0.1% coating can be used to protect cutting boards from bacterial contamination in the meat processing industry.

With the help of laser ablation, a technology for obtaining nanosized crystalline selenium particles (SeNPs) has been created. The SeNPs do not exhibit significant toxic properties, in contrast to molecular selenium compounds. The administration of SeNPs can significantly increase the viabilities of SH-SY5Y and PCMF cells after radiation exposure. The introduction of such nanoparticles into the animal body protects proteins and DNA from radiation-induced damage. The number of chromosomal breaks and oxidized proteins decreases in irradiated mice treated with SeNPs. Using hematological tests, it was found that a decrease in radiation-induced leukopenia and thrombocytopenia is observed when selenium nanoparticles are injected into mice before exposure to ionizing radiation. The administration of SeNPs to animals 5 h before radiation exposure in sublethal and lethal doses significantly increases their survival rate. The modification dose factor for animal survival was 1.2. It has been shown that the introduction of selenium nanoparticles significantly normalizes gene expression in the cells of the red bone marrow of mice after exposure to ionizing radiation. Thus, it has been demonstrated that SeNPs are a new gene-protective and radioprotective agent that can significantly reduce the harmful effects of ionizing radiation.

A new medical antibacterial corrosion-resistant steel alloyed with silver and titanium was smelted. The optimal conditions for homogenizing annealing were selected to obtain a uniform structure and give rise to equiaxed grains. The mechanical properties, microstructure, and phase composition were studied. X-ray powder diffraction analysis showed that the steel without alloying elements after rolling has an austenitic structure. The alloying gave rise to a small amount of ferrite in the steel structure. Spectral analysis showed a uniform silver distribution throughout the alloy. It was determined that a steel sample containing silver and titanium has an antibacterial effect on the bacterial strain Pseudomonas marginalis.

The additive technologies are gaining popularity due to the possibility of creating custom products for complex applications in many industries. Spherical metal powders are initial components for metal additive manufacturing. Initial materials are very important part of manufacturing, because their quality has an influence on stability of production process and quality of final product. In this work properties of spherical powders including 304L, 310, 316L and 17-4PH grade were determined using scanning electron microscopy, laser diffraction particle size analysis, reductive melting method and X-ray analysis.