The article presents the results of obtaining a composite material by sintering nickel-containing raw materials mixed with carbon-containing materials, namely using coke and semi-coke. The sintering process was performed at a charge layer height of 240 mm and the temperature of the lower layer was T = 1200 °C. The results of the sieve analysis showed (a fraction of 10 mm) that the yield of a suitable composite material using coke was 68.3% and with semi-coke 67.0%. The average nickel and chromium content in the composite materials was 1.42% and 3.07%, accordingly. As a result of determining the strength characteristics of the obtained composite materials with various reducing agents by dropping from a height of 2 m onto a steel pallet, it was found that the obtained composite materials have high mechanical properties in terms of strength of 81% and 89.2%. The results of the elemental composition at the studied points and the thermal analysis of the studied composite material are presented. The mineralogical composition of the composite material is presented in the form of serpentine and nontronite, and the empty rock is made of quartz and talc. The activation energy of thermal analysis by the method of non-isothermal kinetics were calculated. The results of experiments on the production of composite materials from nickel-containing raw materials will be recommended for obtaining the optimal composition of composite materials at the stage of pilot tests and industrial development of the developed technology for processing nickel ores of the Republic of Kazakhstan. For the processing of nickel-poor nickel ores, it is of great importance to obtain optimal technological and technical and economic indicators that ensure low cost of nickel in the resulting product.

This study presents the results of laboratory experiments on the processing of lateritic nickel ores mixed with coal and CaO, followed by the use of the obtained product for the smelting of nickel-containing ferroalloy by the metallothermic method. The study analyzed the thermodynamic effects of complex reductant concentration (silicon- and aluminum-containing alloy) on the reduction degree of nickel and iron. An experimental process resulted in a product containing Ni_total (2.60%) and Fe_total (60.52%), obtained through reduction roasting of lateritic nickel ore mixed with coal and an addition of 20 g of CaO at a temperature of 1150 °C. Under laboratory conditions, a nickel-containing ferroalloy was successfully obtained using the product after reduction roasting and a complex alloy as the reducing agent. The following optimal process parameters were determined: reductant consumption of 20 g per 100 g of the reduction roasting product, smelting temperature of 1600 °C, and slag basicity (CaO/SiO₂) of 0.5. In this case, a nickel-containing ferroalloy with 72% iron, 15% nickel, and up to 5% chromium was successfully obtained through silicon and aluminum reduction using a complex alloy. A microstructural analysis of the nickel-containing alloy was conducted using an electron probe microanalyzer (JXA-8230) in combination with scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The results showed that silicon and iron were the dominant elements in all particles. Nickel was detected at concentrations of up to 15.02 wt. %, while chromium reached 3.47 wt. %. Depending on the silicon concentration, the nickel-containing ferroalloy is recommended for corrosion-resistant steel production (Si < 5%) and as a reducing agent for ferronickel production (Si > 5%).

This article presents the results of laboratory studies on the smelting of nickel–chromium-containing ferroalloys from low-grade nickel ores from Kazakhstan. X-ray phase analysis was performed on raw materials, which included quartz, nontronite, chromium metahydroxide, goethite, magnetite, iron chromite, and nickel (II) silicate. The reduction reactions of metal oxides with carbon and carbon monoxide were studied as the temperature increased. Experimental smelting was carried out in a Tammann furnace at 1500–1550 °C using three types of reducing agent: RK coke, as well as its mixtures with low-ash Shubarkol coal, in ratios of 75:25 and 50:50. The second option demonstrated the highest economic efficiency, achieving a 91% nickel recovery rate, reduced coke consumption, and a slag-to-metal ratio of 3.07. Chemical analysis showed that the nickel content in the obtained alloys ranged from 2.5% to 6.5%, while chromium content ranged from 2.6% to 4.5%. X-ray phase analysis confirmed the presence of Fe₂Ni_0.6Si, Fe₅Si₃, and Fe₂CrSi phases in the alloy structure. Local element concentrations varied within the following ranges: Fe—55–59%, Ni—2–10%, Cr—2–7%, and Si—29–35%. The results of this study confirmed the feasibility of producing a nickel–chromium-containing alloy with a nickel content of 2–10% and a chromium content of 2–7%.

Ferrous metallurgy has been and remains one of the main types of production activities that enables humanity to extract, process and produce basic equipment for all types of activities. The growth of ore production as well as the reduction in world reserves of the raw material base have lead to the search for effective methods of processing and preparation of waste for metallurgical processing. The mining and metallurgical sector of the Republic of Kazakhstan, which has its an integrated mining and metallurgical complex with its own coal, iron ore, and energy base, uses iron ores from several deposits. It also includes ash and sludge storage tanks, which store valuable metallurgical waste, such as converter production sludge, rolling scale, and others, the use of which is hindered by the presence of certain harmful impurities in the composition (a rather high content of non-ferrous metals, especially zinc, a high content of oils, etc.). These valuable technological wastes require additional research that may contribute to their use as a charge or as iron-containing components of the charge. Based on the urgency of the tasks of dephosphorylation of iron ores and utilization of human-made waste (converter sludge and rolling scale), studies were conducted to try to eliminate existing problems. The results of the research work make it possible to obtain metals based on prepared pellets with a significantly low phosphorus content; this will enable the use of an oiled rolling scale and converter sludge for the production of a metalized product for steel smelting. The resulting metalized products make it possible to dispose of scale and converter sludge by 70%, and the degree of iron extraction exceeds existing methods by 1–3.5% (92.1–94% vs. 95.6%).

The research presented in the article is devoted to the study of the influence of phase compounds on the friability of the Fe-Si-Mn-Al complex alloy. The urgency of the problem lies in the development of technology for producing a non-scatterable alloy from manganese-containing ores and high-ash coals. The main goal of this work is to determine the range of alloy compositions and the resulting phases that affect the dispersibility of the alloy, which is critically important for its industrial implementation. Research methods include thermodynamic diagram analysis (TDA) using data on the standard enthalpy of formation of intermetallic compounds, as well as experimental tests in an ore-thermal electric furnace with a capacity of 200 kV*A. The results show that Fe-Si-Mn-Al complex alloys form a variety of silicide and aluminide phases, including intermetallic compounds and ternary systems, which is critical for understanding and controlling their physicochemical properties. When melting a complex alloy, the content of leboite (Fe₃Si₇) in the Fe-Si-Mn-Al system plays a significant role. The development of melting process technology will be aimed at avoiding the FeSi₂-Fe₃Si₇-F₂(FeAl₃Si₂)-Mn₁₁Si₁₉ tetrahedron area. This approach to controlling the composition of a complex alloy is critical to ensuring its consistent friability properties in industrial applications. Thus, this work represents an important step in understanding the physical properties and stability of Fe-Si-Mn-Al complex alloys, which have potential for widespread use in metallurgical and other industrial applications.

The research presented in the article is devoted to the study of the influence of phase compounds on the friability of the Fe-Si-Mn-Al complex alloy. The urgency of the problem lies in the development of technology for producing a non-scatterable alloy from manganese-containing ores and high-ash coals. The main goal of the work is to determine the range of alloy compositions and the resulting phases that affect the dispersibility of the alloy, which is critically important for its industrial implementation. Research methods include thermodynamic diagram analysis (TDA) using data on the standard enthalpy of formation of intermetallic compounds, as well as experimental tests in an ore-thermal electric furnace with a capacity of 200 kV*A. The results show that Fe-Si-Mn-Al complex alloys form a variety of silicide and aluminide phases, including intermetallic compounds and ternary systems, which is critical for understanding and controlling their physicochemical properties. When smelting a complex alloy, the content of leboite (Fe3Si7) in the Fe-Si-Mn-Al system plays a significant role. The development of smelting technology will be aimed at avoiding the FeSi2-Fe3Si7-F2(FeAl3Si2)-Mn11Si19 tetrahedron area. This approach to controlling the composition of a complex alloy is critical to ensuring its consistent friability properties in industrial applications. Thus, this work represents an important step in understanding the physical properties and stability of Fe-Si-Mn-Al complex alloys, which have potential for widespread use in metallurgical and other industrial applications.