Polylactide (PLA)/nano-TiO₂ and PLA/nano-TiO₂/nano-Ag blends films were prepared by a solvent volatilization method. Compared to pure PLA film, the nano-blend films have low water vapor permeability (WVP) and a poor transparency. With the increase of the NPs in the PLA, the tensile strength (TS) and elastic modulus (EM) decreased, while the elongation at break (ε) increased. SEM analysis indicated a rougher cross-section of the nano-blend films. According to the FTIR analysis, no new chemical bonds were formed in the nano-blend films. By using DSC to examine the crystallization and melting behavior, the result shows that the NPs have no effect on the glass transition (T_g) and melting temperature (T_m), but they caused an increase on the cold crystallization (T_c) and crystallinity (X_c). TGA results show that the addition of nanoparticles significantly improved the thermal stability. The PLA nano-blend films show a good antimicrobial activity against. E. coli and Listeria monocytogenes. Most important, we carried out migration tests, and verified that the release of NPs from the nano-blend films was within the standard limits.

A novel nanopackaging film was synthesized by incorporating ZnO nanoparticles into a poly-lactic acid (PLA) matrix, and its effect on the quality of fresh-cut apple during the period of preservation was investigated at 4 ± 1 °C for 14 days. Six wt % cinnamaldehyde was added into the nano-blend film. Scanning electron microscope (SEM) analysis showed a rougher cross-section of the nano-blend films and an X-ray diffraction (XRD) was carried out to determine the structure of the ZnO nanoparticles. Compared to the pure PLA film, the nano-blend film had a higher water vapor permeability (WVP) and lower oxygen permeability. With the increase of the nanoparticles (NPs) in the PLA, the elongation at break (ε) and elastic modulus (EM) increased, while tensile strength (TS) decreased. Thermogravimetric analysis (TGA) presented a relatively good thermostability. Most importantly, the physical and biochemical properties of the fresh-cut apple were also measured, such as weight loss, firmness, polyphenol oxidase (PPO), total phenolic content, browning index (BI), sensory quality, and microbiological level. The results indicated that nano-blend packaging films had the highest weight loss at the end of storage compared to the pure PLA film; however, nanopackaging provided a better retention of firmness, total phenolic countent, color, and sensory quality. It also had a remarkable inhibition on the growth of microorganisms. Therefore, Nano-ZnO active packaging could be used to improve the shelf-life of fresh-cut produce.

Different percentages (0%, 1%, 5%, and 10%) of nano-Ag particles were added to polylactic acid (PLA) to make an active nanocomposite packaging film. Strawberries were packaged by the nanocomposite films and stored at 4 ± 1 °C for 10 days. The freshness of strawberries was assessed by regularly measuring the physicochemical properties of the strawberries in each packaging film. The difference in the freshness of strawberries was evaluated by determining the following parameter changes: weight loss, hardness, soluble solids, titratable acid, color, vitamin C, total phenol, free radical scavenging activity, peroxidase activity, and sensory evaluation. The results revealed that the active nanocomposite packaging film has better preservation effect when compared with pure PLA film. Its preservation effect is mainly reflected in the more effective reduction of vitamin C loss, delaying the decline of total phenols and 1-Diphenyl-2-picrylhydrazyl (DPPH) in strawberries. It also showed better physical properties. The results showed that the PLA nanocomposite packaging film could effectively preserve freshness of strawberries.

The microstructure, thermal properties, mechanical properties and oxygen and water vapor barrier properties of a poly(lactic acid) (PLA)/nano-TiO₂ composite film before and after high pressure treatment were studied. Structural analysis showed that the functional group structure of the high pressure treated composite film did not change. It was found that the high pressure treatment did not form new chemical bonds between the nanoparticles and the PLA. The micro-section of the composite film after high pressure treatment became very rough, and the structure was depressed. Through the analysis of thermal and mechanical properties, high pressure treatment can not only increase the strength and stiffness of the composite film, but also increase the crystallinity of the composite film. Through the analysis of barrier properties, it is found that the barrier properties of composite films after high pressure treatment were been improved by the applied high pressure treatment.