Polylactide (PLA)/nano-TiO₂ and PLA/nano-TiO₂/nano-Ag blends films were prepared by a solvent volatilization method. Compared to pure PLA film, the nano-blend films have low water vapor permeability (WVP) and a poor transparency. With the increase of the NPs in the PLA, the tensile strength (TS) and elastic modulus (EM) decreased, while the elongation at break (ε) increased. SEM analysis indicated a rougher cross-section of the nano-blend films. According to the FTIR analysis, no new chemical bonds were formed in the nano-blend films. By using DSC to examine the crystallization and melting behavior, the result shows that the NPs have no effect on the glass transition (T_g) and melting temperature (T_m), but they caused an increase on the cold crystallization (T_c) and crystallinity (X_c). TGA results show that the addition of nanoparticles significantly improved the thermal stability. The PLA nano-blend films show a good antimicrobial activity against. E. coli and Listeria monocytogenes. Most important, we carried out migration tests, and verified that the release of NPs from the nano-blend films was within the standard limits.

A novel nanopackaging film was synthesized by incorporating ZnO nanoparticles into a poly-lactic acid (PLA) matrix, and its effect on the quality of fresh-cut apple during the period of preservation was investigated at 4 ± 1 °C for 14 days. Six wt % cinnamaldehyde was added into the nano-blend film. Scanning electron microscope (SEM) analysis showed a rougher cross-section of the nano-blend films and an X-ray diffraction (XRD) was carried out to determine the structure of the ZnO nanoparticles. Compared to the pure PLA film, the nano-blend film had a higher water vapor permeability (WVP) and lower oxygen permeability. With the increase of the nanoparticles (NPs) in the PLA, the elongation at break (ε) and elastic modulus (EM) increased, while tensile strength (TS) decreased. Thermogravimetric analysis (TGA) presented a relatively good thermostability. Most importantly, the physical and biochemical properties of the fresh-cut apple were also measured, such as weight loss, firmness, polyphenol oxidase (PPO), total phenolic content, browning index (BI), sensory quality, and microbiological level. The results indicated that nano-blend packaging films had the highest weight loss at the end of storage compared to the pure PLA film; however, nanopackaging provided a better retention of firmness, total phenolic countent, color, and sensory quality. It also had a remarkable inhibition on the growth of microorganisms. Therefore, Nano-ZnO active packaging could be used to improve the shelf-life of fresh-cut produce.

Different percentages (0%, 1%, 5%, and 10%) of nano-Ag particles were added to polylactic acid (PLA) to make an active nanocomposite packaging film. Strawberries were packaged by the nanocomposite films and stored at 4 ± 1 °C for 10 days. The freshness of strawberries was assessed by regularly measuring the physicochemical properties of the strawberries in each packaging film. The difference in the freshness of strawberries was evaluated by determining the following parameter changes: weight loss, hardness, soluble solids, titratable acid, color, vitamin C, total phenol, free radical scavenging activity, peroxidase activity, and sensory evaluation. The results revealed that the active nanocomposite packaging film has better preservation effect when compared with pure PLA film. Its preservation effect is mainly reflected in the more effective reduction of vitamin C loss, delaying the decline of total phenols and 1-Diphenyl-2-picrylhydrazyl (DPPH) in strawberries. It also showed better physical properties. The results showed that the PLA nanocomposite packaging film could effectively preserve freshness of strawberries.

Effects of high pressure treatment (0, 200 and 400 MPa) on water vapour barrier, microstructure, thermal, and mechanical properties of poly (lactic acid) (PLA)/Ag nanocomposite films were investigated. The migration behavior of nano-Ag from the nanocomposite films in the presence of 50% (v/v) ethanol as a food simulant was also studied. The water vapour barrier properties increased as pressure was applied to film-forming solutions. High pressure treatment enhanced the mutual effect between PLA and nanoparticles, leading to a more compact network structure in PLA/Ag nanocomposite films. Furthermore, PLA/Ag nanocomposite films treated by high pressure were significantly affected by microstructure, thermal, and mechanical properties when, compared with untreated samples. High pressure treatment at 200 to 400 MPa significantly (p < 0.05) reduced the migration of nano-Ag from the films. Overall, high pressure treatment on film-forming solutions showed potential in improving the functional properties of nanocomposite films, especially in relation to water vapour barrier properties.