Polylactide (PLA)/nano-TiO₂ and PLA/nano-TiO₂/nano-Ag blends films were prepared by a solvent volatilization method. Compared to pure PLA film, the nano-blend films have low water vapor permeability (WVP) and a poor transparency. With the increase of the NPs in the PLA, the tensile strength (TS) and elastic modulus (EM) decreased, while the elongation at break (ε) increased. SEM analysis indicated a rougher cross-section of the nano-blend films. According to the FTIR analysis, no new chemical bonds were formed in the nano-blend films. By using DSC to examine the crystallization and melting behavior, the result shows that the NPs have no effect on the glass transition (T_g) and melting temperature (T_m), but they caused an increase on the cold crystallization (T_c) and crystallinity (X_c). TGA results show that the addition of nanoparticles significantly improved the thermal stability. The PLA nano-blend films show a good antimicrobial activity against. E. coli and Listeria monocytogenes. Most important, we carried out migration tests, and verified that the release of NPs from the nano-blend films was within the standard limits.

Different percentages (0%, 1%, 5%, and 10%) of nano-Ag particles were added to polylactic acid (PLA) to make an active nanocomposite packaging film. Strawberries were packaged by the nanocomposite films and stored at 4 ± 1 °C for 10 days. The freshness of strawberries was assessed by regularly measuring the physicochemical properties of the strawberries in each packaging film. The difference in the freshness of strawberries was evaluated by determining the following parameter changes: weight loss, hardness, soluble solids, titratable acid, color, vitamin C, total phenol, free radical scavenging activity, peroxidase activity, and sensory evaluation. The results revealed that the active nanocomposite packaging film has better preservation effect when compared with pure PLA film. Its preservation effect is mainly reflected in the more effective reduction of vitamin C loss, delaying the decline of total phenols and 1-Diphenyl-2-picrylhydrazyl (DPPH) in strawberries. It also showed better physical properties. The results showed that the PLA nanocomposite packaging film could effectively preserve freshness of strawberries.

Effects of high pressure treatment (0, 200 and 400 MPa) on water vapour barrier, microstructure, thermal, and mechanical properties of poly (lactic acid) (PLA)/Ag nanocomposite films were investigated. The migration behavior of nano-Ag from the nanocomposite films in the presence of 50% (v/v) ethanol as a food simulant was also studied. The water vapour barrier properties increased as pressure was applied to film-forming solutions. High pressure treatment enhanced the mutual effect between PLA and nanoparticles, leading to a more compact network structure in PLA/Ag nanocomposite films. Furthermore, PLA/Ag nanocomposite films treated by high pressure were significantly affected by microstructure, thermal, and mechanical properties when, compared with untreated samples. High pressure treatment at 200 to 400 MPa significantly (p < 0.05) reduced the migration of nano-Ag from the films. Overall, high pressure treatment on film-forming solutions showed potential in improving the functional properties of nanocomposite films, especially in relation to water vapour barrier properties.

The microstructure, thermal properties, mechanical properties and oxygen and water vapor barrier properties of a poly(lactic acid) (PLA)/nano-TiO₂ composite film before and after high pressure treatment were studied. Structural analysis showed that the functional group structure of the high pressure treated composite film did not change. It was found that the high pressure treatment did not form new chemical bonds between the nanoparticles and the PLA. The micro-section of the composite film after high pressure treatment became very rough, and the structure was depressed. Through the analysis of thermal and mechanical properties, high pressure treatment can not only increase the strength and stiffness of the composite film, but also increase the crystallinity of the composite film. Through the analysis of barrier properties, it is found that the barrier properties of composite films after high pressure treatment were been improved by the applied high pressure treatment.