Seawater mixed (SW) concrete lessens the freshwater (FW) demand and eases the stress on the already depleting FW resources. The use of SW concrete is a sustainable solution that mitigates the environmental impact of concrete production, especially in coastal regions and islands vulnerable to FW scarcity. This study investigated the influence of polypropylene (PP) fiber incorporation on high-performance-SW concrete’s long-term mechanical and durability performance. The findings indicate that the incorporation of seawater in the production of concrete containing ground granulated blast furnace slag (GGBFS) has a beneficial effect on its early strength. This is due to the fact that SW accelerates the hardening process. SW concrete mixes showed an improvement in strength with aging. The difference between the strength of SW and FW concretes reduced with aging. The PP fiber showed phenomenal improvements in the tensile properties of SW and FW concretes. At the addition of 0.3% PP fiber, SW yielded 56% and 48% higher splitting tensile and flexural strength than plain FW concrete at 28 days, respectively. The use of 0.15% of PP fiber caused notable reductions of around 20% in the water absorption (WA) capacity and a 12–20% reduction in chloride ion permeability (CIP) of SW concrete. The incorporation of PP fiber increases the number of drying–wetting cycles to initiate the erosion of SW and FW concretes in a simulated environment. The use of 0.15% PP fiber is beneficial, as compared to 0.3% PP fiber to control the tidal erosion of SW and FW concretes. After exposure to 126 drying–wetting cycles (stimulated tidal erosion), the mass loss of SW concrete was reduced from 0.56% to 0.22%.

Steel fibers are widely extracted from scrap tyres, causing environmental concerns. This paper presents the use of steel fibers in variable proportions extracted from scrap tyres. The enhancement of the confinement was envisaged through the addition of steel fibers obtained from scrap tyres. The study included an experimental program for the development of constitutive material models for ordinary Portland cement (OPC) concrete and concrete with added steel fibers. A mix design was carried out for OPC, targeting a compressive strength of 3000 psi. Steel fibers were added to OPC in ratios of 1.0% to 3.0%, with an increment of 0.5%. Concrete columns, with cross-sectional dimensions of 6 × 6 inches and a length of 30 inches, were cast with both OPC and fiber-reinforced concrete. The column confinement was evaluated with a different spacing of ties (3- and 4-inch center-to-center). Compression tests on the concrete columns indicate that the addition of steel fibers to a concrete matrix results in an appreciable increase in strength and ductility. Overall, increasing the percentage of steel fibers increased the compression strength and the ductility of concrete. The maximum strain in the concrete containing 2.5% steel fibers increased by 285% as compared to the concrete containing 1% of steel fibers. An optimum percentage of 2.5% steel fibers added to the concrete resulted in a 39% increase in compressive strength, accompanied by a significant improvement in ductility. The optimum content of steel fibers, when used in confined columns, showed that confined compression strength increased with the addition of steel fibers. However, it is recommended that additional columns on the basis of the optimum steel fiber content shall be tested to evaluate their effectiveness in reducing the stirrup spacing.