This article presents the results of a study on metallurgical slag reduction using biomass such as Spent Coffee Grounds (SCGs). The proposed solution is a new aspect of searching for alternatives to standard reducers used in pyrometallurgical processes of metal production. Its gasification yields significant amounts of hydrocarbons, which are excellent reducing agents in such processes. The research results of copper slag reduction with the use of SCG biomass indicate this process is characterised by lower carbon dioxide emissions compared with the process using solid fuels such as coke and coke breeze. The addition of SCG as the reducer ensures the decrease in copper content in the slag to 0.32 wt.%, which corresponds to the increase of so-called relative decopperisation degree even up to 96.9%. As the decopperisation degree of slag increases, significantly more intense reduction in lead oxides during the reduction process is observed. The smallest lead content in waste slag of 0.91 wt.% was obtained for the slag reduction process with 7.56 wt.% of SCG as the reducer and the process duration of 1.5 h.

A description of the process of metal evaporation from liquid alloys at an atmospheric pressure has a practical value for both the smelting and remelting of their scraps. The quantities of volatile components that are eliminated in these processes depend on many factors of which the type of melting device, the method and conditions of the process performance, the alloy composition and the kind of applied atmosphere are of the greatest importance. In this paper, the results of the research on zinc evaporation from brass scraps containing 10.53 wt% Zn are presented. The experiments were conducted using the thermogravimetric method at 1080 ÷ 1240 °C in a helium atmosphere. In the research, the levels of zinc removal from copper ranged between 82% and 99%. The values of the overall mass transfer coefficient for zinc k_Zn, determined based on the experimental data, ranged from 4.74 to 8.46 × 10⁻⁵ ms⁻¹. The kinetic analysis showed that the rate of the analysed process was determined by mass transfer in the gas phase.

Increasing the share of circulating scrap in produced castings is not only due to optimizing production costs, but also the need to protect the environment realized by reducing production energy intensity, generating less waste, mitigating greenhouse gas emissions, and consuming fewer natural resources. However, this is associated with maintaining the required properties of castings and considering the impact of impurities on the formation of the structure of aluminum alloys. This research concerns the AlSi10MnMg alloy, which introduces 50 to 75% (every 5%) of circulating scrap. This alloy is one of the most commonly used for producing gravity and pressure die-castings (HPDC), including engine parts and transport structural elements. Based on microscopic research, it was found that the increase in scrap content causes an increase in the share of iron, which results in pre-eutectic (from about 0.45 wt.% to 0.7 wt.% Fe) or even primary crystallization of iron phases (over 0.7 wt.% Fe), mainly the plate–needle phase β-Al₅FeSi. Its unfavorable morphology and size cause the formation of numerous shrinkage porosity areas, which has an impact on the reduction in mechanical properties (reduction in UTS and YS by approx. 16% and elongation by approx. 18%, compared to the AlSi10MnMg alloy with 50% scrap content). It was found that the increase in the share of recycled scrap (from 50 to 75%) can be used only when the manganese content is increased. Its effect is to change the morphology of the β-Al₅FeSi phase into α-Al₁₅(Fe,Mn)₃Si₂, whose crystallization occurs in the temperature range of 540 to 555 °C and increases slightly with increasing manganese addition. It is essential to consider the appropriate value of the Mn/Fe quotient, which should be about 1/2, because a higher value may cause the formation of a sludge factor. This work aimed to determine the limiting iron content (contained in the scrap) at which the sequence of the β-Al₅FeSi phase release (pre-eutectic or primary crystallization) changes. This sequence mainly affects the form of morphology, the dimensions of the β-Fe phase, and the proportion of shrinkage porosity.

In relation to the climate policy being introduced, the search for a replacement for solid fossil fuels with renewable raw materials is ongoing. In this study, a potential biomass (sunflower husk pellet) application in the process of copper slag reduction was assessed. For the purpose of raw material characterisation, thermogravimetric tests were carried out and characteristic temperature points were determined with the use of a high-temperature microscope. The slag reduction tests led to the recovery of 97% of copper and a decrease in this metal content in the slag to less than 0.5% Cu, which enables safe storage or use in other industrial branches.

The article presents the results of a study on metallurgical sludge reduction using electronic waste such as Printed Circuit Boards (PCBs). Two aspects were taken into account when selecting such a reducer, namely the environmental aspect and the technological aspect. The research was an attempt to use waste metal-bearing material of which the effective management causes many problems from an environmental point of view. In the technological aspect, the specific chemical composition of this waste was taken into account. Its gasification yields significant amounts of hydrocarbons, which are excellent reducing agents in such process. The separation of these compounds may additionally cause the mixing of the molten slag, which should result in faster separation of the formed metal droplets and the molten slag. In the case of the fragmented PCB (Printed Circuit Board) reducer used in this study, a significant degree of copper removal was achieved, as much as 92%. As the reduction-process time increased, the degree of copper removal also increased. For the 1 h process, the average value of copper removal was 60%, and for the 4.5 h process it was over 70%. The case was the same with the addition of reductant: as the amount of reductant added to the process increased, an increase in copper removal was observed. With the addition of 30 g of the reducing agent (per 65 g of slag), the degree of copper removal was over 90%.