In this work, the mechanism of the corrosion behavior of laser‐treated aluminum is studied. Two different laser techniques are used to fabricate the samples, direct laser interference patterning (DLIP) and direct laser writing (DLW), using nanosecond laser sources. The DLIP treatment uses a two‐beam optical configuration producing line‐like periodic structures. The DLW technique is employed to produce non‐periodic structures on the Al‐surface with the same cumulated fluences as in DLIP. The surface topography is analyzed by confocal microscopy, and the formation of oxide layers is investigated by scanning electron microscopy of cross‐sections produced using a focused ion beam. Wetting measurements performed on the laser‐treated samples exhibit a contrasting behavior, leading to either superhydrophobic or superhydrophilic states. In the case of the DLIP treatment, the static water contact angle is increased from 81° up to 158°, while for DLW, it decreases to 3°. Electrochemical tests demonstrate a decreased corrosion rate after laser treatment. Additionally, findings indicate no correlation between wettability and corrosion reduction. Therefore, the improvement in corrosion resistance is mainly attributed to the oxide layer formed by laser treatment. Although similar corrosion rates are achieved for both treatments, surfaces produced with DLIP can be beneficial when additional surface properties are required.

In times of societal development, sustainability has become a major concern for many manufacturers in the metal industries. In this context, surface texturing of cutting tools offers a promising approach in terms of reducing energy consumption and material waste. In this work, direct laser interference patterning is utilized for producing periodic line-like structures with spatial periods of 2.0 µm and 5.5 µm on rake-flank faces of cemented tungsten carbide cutting inserts. Structure depths up to 1.75 µm are reached by controlling the applied number of laser pulses. Turning experiments under lubricated conditions carried out on Al 6061 T6 parts with textured and untreated tools are performed to determine their tribological performances. The used textured cutting tools can effectively decrease machining forces up to 17% due to the corresponding improvement in frictional behavior at the tool/chip interface. Furthermore, the laser-processed tools produce thinner chips and decrease the surface roughness by 31% of the aluminum work piece.

Nowadays, the demand for surface functionalized plastics is constantly rising. To address this demand with an industry compatible solution, here a strategy is developed for producing hierarchical microstructures on polyethylene terephthalate (PET) by hot embossing using a stainless steel stamp. The master was structured using three laser-based processing steps. First, a nanosecond-Direct Laser Writing (DLW) system was used to pattern dimples with a depth of up to 8 µm. Next, the surface was smoothed by a remelting process with a high-speed laser scanning at low laser fluence. In the third step, Direct Laser Interference Patterning (DLIP) was utilized using four interfering sub-beams to texture a hole-like substructure with a spatial period of 3.1 µm and a depth up to 2 µm. The produced stamp was used to imprint PET foils under controlled temperature and pressure. Optical confocal microscopy and scanning electron microscopy imaging showed that the hierarchical textures could be accurately transferred to the polymer. Finally, the wettability of the single- and multi-scaled textured PET surfaces was characterized with a drop shape analyzer, revealing that the highest water contact angles were reached for the hierarchical patterns. Particularly, this angle was increased from 77° on the untreated PET up to 105° for a hierarchical structure processed with a DLW spot distance of 60 µm and with 10 pulses for the DLIP treatment.