This material can be considered to be an interesting eco-friendly choice to be used in the photovoltaic field. In this work, we present the fabrication of Cu₃N thin films by reactive radio-frequency (RF) magnetron sputtering at room temperature, using nitrogen as the process gas. Different RF power values ranged from 25 to 200 W and gas pressures of 3.5 and 5 Pa were tested to determine their impact on the film properties. The morphology and structure were exhaustively examined by Atomic Force Microscopy (AFM), Fourier Transform Infrared (FTIR) and Raman Spectroscopies and X-ray Diffraction (XRD), respectively. The AFM micrographs revealed different morphologies depending on the total pressure used, and rougher surfaces when the films were deposited at the lowest pressure; whereas FTIR and Raman spectra exhibited the characteristics bands related to the Cu-N bonds of Cu₃N. Such bands became narrower as the RF power increased. XRD patterns showed the (100) plane as the preferred orientation, that changed to (111) with the RF power, revealing a worsening in structural quality. Finally, the band gap energy was estimated from transmission spectra carried out with a Perkin Elmer 1050 spectrophotometer to evaluate the suitability of Cu₃N as a light absorber. The values obtained demonstrated the capability of Cu₃N for solar energy conversion applications, indicating a better film performance under the sputtering conditions 5.0 Pa and RF power values ranged from 50 to 100 W.

Nowadays, the use of plasmonic metal layers to improve the photonic emission characteristics of several semiconductor quantum dots is a booming tool. In this work, we report the use of silicon quantum dots (SiQDs) embedded in a silicon nitride thin film coupled with an ultra-thin gold film (AuNPs) to fabricate light emitting devices. We used the remote plasma enhanced chemical vapor deposition technique (RPECVD) in order to grow two types of silicon nitride thin films. One with an almost stoichiometric composition, acting as non-radiative spacer; the other one, with a silicon excess in its chemical composition, which causes the formation of silicon quantum dots imbibed in the silicon nitride thin film. The ultra-thin gold film was deposited by the direct current (DC)-sputtering technique, and an aluminum doped zinc oxide thin film (AZO) which was deposited by means of ultrasonic spray pyrolysis, plays the role of the ohmic metal-like electrode. We found that there is a maximum electroluminescence (EL) enhancement when the appropriate AuNPs-spacer-SiQDs configuration is used. This EL is achieved at a moderate turn-on voltage of 11 V, and the EL enhancement is around four times bigger than the photoluminescence (PL) enhancement of the same AuNPs-spacer-SiQDs configuration. From our experimental results, we surmise that EL enhancement may indeed be due to a plasmonic coupling. This kind of silicon-based LEDs has the potential for technology transfer.