Ten percent of patients undergoing total hip arthroplasty (THA) require revision surgery. One of the reasons for THA are wear particles released from the implants that can activate the immune defense and cause osteolysis and failure of the joint implant. The discrepancies between reports on toxicity and immunogenicity of the implant materials led us to this study in which we compared toxicity and immunogenicity of well-defined nanoparticles from Al₂O₃, zirconia-toughened alumina (ZTA), and cobalt chrome (CoCr), a human THP-1 macrophage cell line, human PBMCs, and therefrom-derived primary macrophages. None of the tested materials decreased the viability of THP-1 macrophages nor human primary macrophages at the 24 h time point, indicating that at concentrations from 0.05 to 50 µm³/cell the tested materials are non-toxic. Forty-eight hours of treatment of THP-1 macrophages with 5 µm³/cell of CoCr and Al₂O₃ caused 8.3-fold and 4.6-fold increases in TNF-α excretion, respectively, which was not observed for ZTA. The comparison between THP-1 macrophages and human primary macrophages revealed that THP-1 macrophages show higher activation of cytokine expression in the presence of CoCr and Al₂O₃ particles than primary macrophages. Our results indicate that ZTA is a non-toxic implant material with no immunogenic effects in vitro.

Gross taper failure (GTF) is a rare but catastrophic failure mode of the head-stem-taper junction of hip prostheses, facilitated by massive material loss. GTF is a two stage process initiated by corrosion leading to head bottoming out, followed by abrasive wear due to the head rotating on the stem. The purpose of this study was to reproduce the clinical failure patterns and to determine the material loss during simulated gait. Six cobalt-chromium alloy heads (36 mm, 12/14 taper) with three different head lengths (short / medium / extra long) were combined with stem taper replicas made from titanium alloy sized to achieve bottoming out. A hip simulator was used to simulate gait loading after (ISO 14242-1 for 2 million cycles). Wear patterns from in-vitro testing match the clinical failure patterns. Stem taper wear increased linearly with time (p< 0.001). After two million cycles the material loss of short / medium / extra long heads was (M+-STD) 1168±242 mg / 400±23 mg / 94±12 mg on the stem side and 46±36 mg / 46±24 mg / 70±8 mg on the head side. Stem taper wear decreased with increasing head length (p=0.01), whereas clinical failures are mostly seen for long and extra long heads.

We report a case of extended osteolysis, requiring a third revision of the left hip in an 85-year-old man 46 years after index operation. Major polyethylene (PE) wear occurred due to a missmatched combination of a bipolar Hastings head with a PE liner and head damage of the originally maintained stem. This case demonstrates that bipolar heads should not be used with PE cup liners since the respective bearing diameters cannot be guaranteed to match due to missing specifications. Furthermore, putting a Hastings head on an already damaged head of the stem should be omitted and rather the stem should initially be revised.