We designed, manufactured and characterized two birefringent microstructured fibers that feature a 5-fold increase in polarimetric sensitivity to hydrostatic pressure compared to the earlier reported values for microstructured fibers. We demonstrate a good agreement between the finite element simulations and the experimental values for the polarimetric sensitivity to pressure and to temperature. The sensitivity to hydrostatic pressure has a negative sign and exceeds −43 rad/MPa × m at 1.55 μm for both fibers. In combination with the very low sensitivity to temperature, this makes our fibers the candidates of choice for the development of microstructured fiber based hydrostatic pressure measurement systems.

In this Letter, we demonstrate an all-polarization-maintaining, stretched-pulse Tm-doped fiber laser generating $\sim 200\mathrm{fs}$ pulses centered at 1945 nm. As a saturable absorber, a graphene/poly(methyl methacrylate) composite was used. To the best of our knowledge, this is the first demonstration of stretched-pulse operation of a graphene-based fiber laser at 2 μm.

We demonstrate a broadband mid-infrared (MIR) frequency comb source based on difference frequency generation (DFG) in periodically poled lithium niobate crystal. MIR radiation is obtained via mixing of the output of a 125 MHz repetition rate Yb-doped fiber laser with Raman-shifted solitons generated from the same source in a highly nonlinear fiber. The resulting idler is tunable in the range of 2.7–4.2 μm, with average output power reaching 237 mW and pulses as short as 115 fs. The coherence of the MIR comb is confirmed by spectral interferometry and heterodyne beat measurements. Applicability of the developed DFG source for laser spectroscopy is demonstrated by measuring absorption spectrum of acetylene at 3.0–3.1 μm.

In this letter, we report for the first time, a chirped fiber Bragg grating photo-inscribed in undoped PMMA polymer optical fibre (POF). The chirped polymer optical fiber Bragg gratings (CPOFBGs) were inscribed using an UV KrF excimer laser operating at 248 nm and a 25-mm long chirped phase mask customized for 1550-nm grating inscription. The used laser pulsing frequency was 1 Hz with an energy of 5 mJ per exposure and only few shots for each grating inscription were employed. The reflection amplitude spectrum evolution of a CPOFBG is investigated as a function of the applied strain, temperature, and pressure. These results can potentiate further developments in different sensing fields, such as liquid level monitoring, splits, and transverse cracks in structural health monitoring by local pressure analysis or even biomedical field. Furthermore, CPOFBGs could present some critical advantages preferably replacing their silica counterparts as well as the uniform polymer FBGs.

In this work, fibre Bragg gratings (FBGs) were inscribed in two different undoped poly- (methyl methacrylate) (PMMA) polymer optical fibres (POFs) using different types of UV lasers and their inscription times, temperature and strain sensitivities are investigated. The POF Bragg gratings (POFBGs) were inscribed using two UV lasers: a continuous UV HeCd @325 nm laser and a pulsed UV KrF @248 nm laser. Two PMMA POFs are used in which the primary and secondary preforms (during the two-step drawing process) have a different thermal treatment. The PMMA POFs drawn in which the primary or secondary preform is not specifically pre-treated need longer inscription time than the fibres drawn where both preforms have been pre-annealed at 80 °C for 2 weeks. Using both UV lasers, for the latter fibre much less inscription time is needed compared to another homemade POF. The properties of a POF fabricated with both preforms thermally well annealed are different from those in which just one preform step process is thermally treated, with the first POFs being much less sensitive to thermal treatment. The influence of annealing on the strain and temperature sensitivities of the fibres prior to FBG inscription is also discussed, where it is observed that the fibre produced from a two-step drawing process with well-defined pre-annealing of both preforms did not produce any significant difference in sensitivity. The results indicate the impact of preform thermal pre-treatment before the PMMA POFs drawing, which can be an essential characteristic in the view of developing POF sensors technology.

Fiber Bragg gratings written in highly birefringent microstructured optical fiber with a dedicated design are embedded in a composite fiber-reinforced polymer. The Bragg peak wavelength shifts are measured under controlled axial and transversal strain and during thermal cycling of the composite sample. We obtain a sensitivity to transversal strain that exceeds values reported earlier in literature by one order of magnitude. Our results evidence the relevance of using microstructured optical fibers for structural integrity monitoring of composite material structures.