In the present work, the effect of divinylbenzene (DVB) on the kinetics of post-radiation chemical graft polymerization styrene (St) on polyethylene (PE) film and its structural and morphological features were investigated. It has been found that the dependence of the degree of polystyrene (PS) grafting on the DVB concentration in the solution is extreme. An increase in the rate of graft polymerization at low concentrations of DVB in the solution is associated with a decrease in the mobility of the growing chains of PS. A decrease in the rate of graft polymerization at high concentrations of DVB is associated with a decrease in the rate of diffusion of St and iron(II) ions in the cross-linked network structure of macromolecules of graft PS. A comparative analysis of the IR transmission and multiple attenuated total internal reflection spectra of the films with graft PS shows that graft polymerization of St in the presence of DVB leads to the enrichment of the film surface layers in PS. These results have been confirmed by the data on the distribution of sulfur in these films after sulfonation. The micrographs of the surface of the grafted films show the formation of cross-linked local microphases of PS with fixed interfaces.

The hydration of ions and charge groups controls electro mass transfer through ion exchange systems. The self-diffusion and local mobility of water molecules as well as lithium cations in poly (4-styrenesulfonic acid) and its lithium, sodium and cesium salts were investigated for the first time using pulsed-field gradient NMR (PFG NMR) and NMR relaxation techniques. The temperature dependences of the water molecule and Li⁺ cation self-diffusion coefficients exhibited increasing self-diffusion activation energy in temperature regions below 0 °C, which is not due to the freezing of parts of the water. The self-diffusion coefficients of water molecules and lithium cations, as measured using PFG NMR, are in good agreement with the self-diffusion coefficients calculated based on Einstein’s equation using correlation times obtained from spin-lattice relaxation data. It was shown that macroscopic water molecules’ and lithium cations’ transfer is controlled by local particles jumping between neighboring sulfonated groups. These results are similar to the behavior of water and cations in sulfonic cation exchanger membranes and resins. It was concluded that polystyrenesulfonic acid is appropriate model of the ionogenic part of membranes based on this polymer.