Due to the recent surge in silicon demand for solar modules, thin-film photovoltaic (PV) modules have a potential to penetrate the market in significant numbers. As an alternate candidate, thin film technologies in PVs have the ability to achieve better performance. The competing thin-film PV technologies have the flexibility to adapt to any sort of curvature compared to rigid solar cells (SCs). Due to the peculiar characteristics of newer solar materials, stability issues, reflection losses, advancements in electrode materials and dopant materials with a photoactive layer are current challenges driving the industrial-academic voyage of development of solar materials for the betterment of Photo-conversion Efficiency (PCE). Based on the photoactive materials used over time, SC evolution was broadly classified into first, second and third generation SCs. In this review, the basic working mechanisms, various materials used, drawbacks and stability issues of different SCs are discussed extensively. Thin film SCs tend to absorb certain elastic deformations due to their flexible nature and to a certain extent. According to the NREL efficiency chart, multi-junctional SCs exhibit enhanced efficiency as compared to the other SCs. Among the third-generation SCs, the perovskite/Si tandem architecture shows a maximum efficiency of approximately 29%. Thin film flexible SCs find application in various sectors such as automobile, defense and/or energy storage devices

For comparison, the drilling behaviour of abaca fiber‐reinforced polymer (AFRP) composites and Kevlar‐reinforced epoxy polymer (KFRP) composites has been studied in the specified experimental condition. The different geometrical drilling tools have been used for the investigation, namely, candlestick (T1), core (T2), standard twist drill (T3), and step cone (T4). The tool feed of 30, 45, and 60 m/min and rotational speed of 1000, 1500, and 2000 rpm have been used for the investigation. The thrust force is chosen as a response parameter for this study. The results revealed that, at lesser rotational speed and tool feed, the thrust force has declined. The result obtained correlates with the abaca fiber‐based systems. However, the thrust force of KFRP is higher compared to AFRP composite systems. The axial force generated by candlestick drill is minimal compared to the other drill bits. The following may be responsible for lower thrust force: (1) the axial force distributes circumferential of the cutting tool instead of focusing at the center and (2) the interfacial adhesiveness between the matrix and the fiber is higher. The optimization of drilling process parameters, namely, tool feed and rotational speed on thrust force, has been studied. The results reveal that the tool feed contributed more to axial force compared to rotational speed.

The drilling process is the most essential in the final assembly of the mechanical parts. Natural fiber based composites replace traditional materials due to their advantages, such as strength to weight ratio, availability, and environmental hazards. In this work, an attempt has been made to find the minimum thrust force produced by the drill tool at specified drilling process parameters. The drilling process parameters used for the investigation are rotational speed, tool feed, and resins. The spindle speed and feed rate are selected with three levels. Three resin materials were used, namely, epoxy, polyester, and vinyl ester. Taguchi’s L₂₇ orthogonal array was implemented. The result shows that the candlestick drill bit generated lesser thrust force at the specified drilling process parameters, followed by the twist and step cone drill bits.