In this study, two biodegradable Mg-Zn-Ca alloys with alloy content of less than 1 wt % were strengthened via high pressure torsion (HPT). A subsequent heat treatment at temperatures of around 0.45 T_m led to an additional, sometimes even larger increase in both hardness and tensile strength. A hardness of more than 110 HV and tensile strength of more than 300 MPa were achieved in Mg-0.2Zn-0.5Ca by this procedure. Microstructural analyses were conducted by scanning and transmission electron microscopy (SEM and TEM, respectively) and atom probe tomography (APT) to reveal the origin of this strength increase. They indicated a grain size in the sub-micron range, Ca-rich precipitates, and segregation of the alloying elements at the grain boundaries after HPT-processing. While the grain size and segregation remained mostly unchanged during the heat treatment, the size and density of the precipitates increased slightly. However, estimates with an Orowan-type equation showed that precipitation hardening cannot account for the strength increase observed. Instead, the high concentration of vacancies after HPT-processing is thought to lead to the formation of vacancy agglomerates and dislocation loops in the basal plane, where they represent particularly strong obstacles to dislocation movement, thus, accounting for the considerable strength increase observed. This idea is substantiated by theoretical considerations and quenching experiments, which also show an increase in hardness when the same heat treatment is applied.

In this study, nickel oxide–Y₂O₃-doped ZrO₂ (NiO-YSZ) composite powder as an anode material was synthesized using a cost-effective combustion method for high-temperature solid oxide fuel cell (SOFC). Further, the effects of sintering temperatures (1200, 1300, and 1400 °C) were studied for its properties in relation to the SOFC performance. The prepared and sintered NiO-YSZ materials were characterized for their surface morphology, composition, structure, and conductivity. The cubic crystalline nature of NiO and YSZ was sufficed by X-ray diffraction, and SEM images revealed an increase in the densification of microstructure by an increase in the sintering temperature. EDX spectrum confirmed the presence of nickel, yttrium, and zirconia without any impurity. Conductivity measurements, under a hydrogen environment, revealed that NiO-YSZ, sintered at 1400 °C, exhibits better conductivity compared to the samples sintered at lower temperatures. Electrochemical performance of button-cells was also evaluated and peak power density of 0.62 Wcm⁻² is observed at 800 °C. The citrate combustion method provided peak performance for cells containing anode sintered at 1200 °C, which was previously reported at higher sintering temperatures. Therefore, the citrate combustion method is found to be a suitable route to synthesize NiO-YSZ at low sintering temperature.