Recycled rubber (RR) and recycled spiral steel fiber (RSSF) were added to plain concrete (PC) to prepare recycled spiral steel fiber rubber concrete (SSFRC) with matrix strengths of C30, C40, and C50. Strength tests on the PC, rubber concrete (RC), and SSFRC were carried out, including the cube compressive strength, splitting tensile strength, and flexural strength. The effects of RSSF and RR on the mechanical properties of concrete were analyzed. Simultaneously, the stress–strain curve of the SSFRC was obtained through axial compressive testing, and the toughness of SSFRC was evaluated by three indexes: the tensile compression ratio, bending compression ratio, and toughness index. The results show that adding RR to PC results in a decrease in the mechanical properties of concrete with different matrix strengths, and the addition of RSSF can make up for the strength loss of the rubber. The mechanical strength of SSFRC with different matrix strengths increased first and then decreased with the increase in RSSF content. The cubic compressive strength reached its peak value when the content of RSSF was 1%, and the splitting tensile strength and flexural strength reach their peak values when the content of RSSF was 1.5%. RSSF works best with rubber particles at the right dosage to further increase the toughness of the concrete. When the rubber content is 10%, and the RSSF content is 1.5%, the mechanical strength enhancement effect of SSFRC is at its best, and the toughness is also at its best.

We sorted the waste from mechanical processing to form recycled steel fibers. In order to study the flexural mechanical properties of reinforced concrete beams after the addition of recycled steel fibers, four recycled steel fiber concrete beams (RSFCBs) and one normal concrete beam (NCB) were designed and poured using the volume fraction of steel fibers (0%, 0.5%, 1%, 1.5%, 2%) as the variables. Normal section bending tests were conducted on them under a concentrated load. We obtained experimental data such as the cracking load, ultimate load, mid-span deflection, and steel and concrete strain of the beam by gradually loading the test beam, and we observed and recorded the development of cracks. The results indicate that the NCB exhibits crushing failure, while the RSFCBs exhibit equilibrium failure. The addition of recycled steel fibers effectively controls the extension of cracks, resulting in a better bending toughness of the beam. The bending performance of RSFCBs with different volume additions shows a trend of first increasing and then decreasing with the increase in steel fiber content. The peak value was reached when the steel fiber content was 1.5%, which increased the bending bearing capacity by 54.72% compared with the NCB. With the increase in steel fiber content, the required load value for tensile steel bars to yield also increases, reaching a peak at a content of 1.5%, which increases the bending bearing capacity by 44.64% compared with the NCB. The addition of recycled steel fibers enables the beam to improve its bearing capacity while limiting the development of longitudinal reinforcement strain, allowing the longitudinal reinforcement to yield under higher loads and improving the overall bending performance of the beam.

The increasing incidence of urban fires poses significant threats to structural integrity, underscoring the urgent need for concrete materials with enhanced mechanical properties post-fire. Incorporating recycled waste steel fibers (WSF) from industrial byproducts into concrete not only bolsters its crack resistance but also advances circular economy principles by transforming industrial waste into valuable resources. Although a large amount of research has focused on native steel fiber-reinforced concrete, there is still a lack of systematic exploration on the optimal dosage and effectiveness of waste steel fibers in slowing down the strength degradation of concrete after high-temperature action. In this study, two grades of concrete (C40 and C60) containing 0%, 1%, and 2% WSF by volume were subjected to heating cycles ranging from 200 °C to 800 °C. Post-cooling evaluations encompassed mass loss quantification, cube compressive strength testing (using 100 mm³ specimens), and splitting tensile tests conducted at a loading rate of 0.1 MPa/s. Results indicated that mass loss escalated to 11% at 800 °C, with C60 experiencing a 12% higher loss compared to C40. Compressive strength decreased by 15% for every 200 °C increment; however, the inclusion of 1% WSF significantly minimized this degradation, preserving 44.5% (for C40) and 37.8% (for C60) of the original strength at 800 °C. Notably, the splitting tensile strength of 1% WSF-reinforced C60 concrete exceeded that of plain concrete by 39.4% after exposure to 800 °C, demonstrating its superior crack-bridging capabilities.

The scrap steel fibers (SSF) produced by mechanical processing are processed and added to rubber concrete (RC) to make scrap steel fiber rubber concrete (SSFRC), so as to enhance the strength of the rubber concrete. SSFRC with a concrete strength grade of C30, a rubber dosage of 10%, and SSF dosages of 0, 0.5, 1.0, 1.5, 2.0, and 2.5% were prepared. Cubic compressive tests and drop hammer impact tests were conducted respectively on cubic and cylindrical specimens, and the influence of different weights of the drop hammer, different heights of the drop hammer, and different dosages of SSF on the results was analyzed. The results show that adding SSF to RC can effectively improve the compressive performance and impact resistance. When the fiber dosage is 1%, the compressive performance reaches the optimal level. With the increase of the weight and height of the drop hammer, the impact resistance of the specimens decreases significantly. With the increase of the dosage of SSF, the impact resistance of the specimens significantly improves. When the dosage of SSF is 1.5%, the impact resistance performance is the best. The finite element model was established using ABAQUS, and the simulation results were compared with the test results. The error was within an acceptable range.

To explore the axial compressive mechanical properties of steel tube recycled steel fiber reinforced concrete short columns (STRSFRCSCs), axial compression tests were conducted on ten STRSFRCSCs and two steel tube reinforced concrete short columns (STRCSCs), mainly analyzing the effects of recycled steel fiber (RSF) content, steel content, and concrete strength grade on their mechanical properties. The results showed that different RSF contents had no significant effect on the failure mode of the specimens, while the concrete strength grade and steel content had a significant effect on the failure mode. When the steel content was 2.84%, the specimens experienced shear failure, while when the steel content was 4.24%, they experienced waist drum failure. As the RSF content increased, the peak strain during the loading process of the specimens decreased, and the transverse deformation coefficient at the peak decreased. The addition of RSF significantly improved the ductility performance of the specimens. When the volume fraction of RSF was 2%, the bearing capacity of the specimens increased the most, reaching 13.4%, and the ductility coefficient gradually increased. The axial compressive bearing capacity and combined elastic modulus of the specimens increased with the increase in concrete strength grade, RSF content, and steel content.

Polypropylene (EPP) concrete offers advantages such as low density and good thermal insulation properties, but its relatively low strength limits its engineering applications. Waste steel fibers (WSFs) obtained during the sorting and processing of machining residues can be incorporated into EPP concrete (EC) to enhance its strength and toughness. Using the volume fractions of EPP and WSF as variables, specimens of EPP concrete (EC) and waste steel fiber-reinforced EPP concrete (WSFREC) were prepared and subjected to cube compressive strength tests, splitting tensile strength tests, and four-point flexural strength tests. The results indicate that EPP particles significantly improve the toughness of concrete but inevitably lead to a considerable reduction in strength. The incorporation of WSF substantially enhanced the splitting tensile strength and flexural strength of EC, with increases of at least 37.7% and 34.5%, respectively, while the improvement in cube compressive strength was relatively lower at only 23.6%. Scanning electron microscopy (SEM) observations of the interfacial transition zone (ITZ) and WSF surface morphology in WSFREC revealed that the addition of EPP particles introduces more defects in the concrete matrix. However, the inclusion of WSF promotes the formation of abundant hydration products on the fiber surface, mitigating matrix defects, improving the bond between WSF and the concrete matrix, effectively inhibiting crack propagation, and enhancing both the strength and toughness of the concrete.