The effects of short-term thermomechanical (STTM) densification temperature and pressure on the changes in surface roughness, wettability, mass loss (ML), thickness and density of alder, beech, birch, and pine wood veneer with low moisture content (~5%) were investigated. The anatomical structure of veneers was also observed. Veneer sheets were densified using pressure levels of 4, 8 and 12 MPa at three temperatures: 100°C, 150°C and 200°C for 4 min. The results were compared with those of the non-densified veneers. The obtained results show that STTM densification of veneers similarly to long-term densification of solid wood causes irreversible changes in their properties. The STTM-densified veneer surfaces became smoother and more hydrophobic, ML increased slightly while roughness and thickness values decreased significantly, the cell lumens collapsed and a certain amount of fractures in cell walls developed with increasing densification temperature and pressure. All of the investigated wood species showed higher density values after densification. It was found that an even STTM densification of veneers provides stable properties under normal atmosphere conditions; in particular, the thickness and contact angle values were stable for 24 hours after densification, which is an important consideration for industrial applications.

The objective of this study was to evaluate the glossiness of black alder wood (Alnus glutinosa L.) samples coated with two varnish types as a function of exposure to dry heat and artificial aging. The chemical resistance of the coated samples to cold liquids was also evaluated. Based on the findings in this work, it appears that the varnish types and their structural differences influenced the overall glossiness of the coated samples. The UV varnish exhibited higher gloss values than those coated with the water-borne product within the range of silky gloss and silky matte grades. The heat exposure influenced the surface glossiness of the UV-coated samples more than the samples coated with water-borne varnish. The overall gloss values of the samples decreased with the exposure time to artificial aging, resulting in no layer cracks. The cold household liquids left less visible traces on the surfaces and alcohol was found to be the strongest agent. This study could have practical applications in the furniture industry to produce value-added furniture units according to their specific conditions of indoor use.