The objective of this study was to evaluate the glossiness of black alder wood (Alnus glutinosa L.) samples coated with two varnish types as a function of exposure to dry heat and artificial aging. The chemical resistance of the coated samples to cold liquids was also evaluated. Based on the findings in this work, it appears that the varnish types and their structural differences influenced the overall glossiness of the coated samples. The UV varnish exhibited higher gloss values than those coated with the water-borne product within the range of silky gloss and silky matte grades. The heat exposure influenced the surface glossiness of the UV-coated samples more than the samples coated with water-borne varnish. The overall gloss values of the samples decreased with the exposure time to artificial aging, resulting in no layer cracks. The cold household liquids left less visible traces on the surfaces and alcohol was found to be the strongest agent. This study could have practical applications in the furniture industry to produce value-added furniture units according to their specific conditions of indoor use.

Thermo-mechanical densification of wood is performed to improve physical and mechanical properties of wood. During this treatment aesthetic properties of wood, including gloss, also change. Therefore, the purpose of this study was to determine the effect of short-term thermo-mechanical (STTM) densification in different wood species (alder (Alnus glutinosa Goertn.), beech (Fagus sylvatica L.), birch (Betula verrucosa Ehrh.), and pine (Pinus sylvestris L.)) on their gloss changes. Commercial wood veneers were densified in a hot plate press for 4 min at temperatures of 100, 150 and 200 °C, pressures of 4, 8 and 12 MPa. Gloss was evaluated at 20°, 60° and 85° angles of incident light using PICO GLOSS 503. Gloss measurements showed an enhancement of aesthetic properties of densified wood. Findings of this study indicated that both densification temperature and pressure have a significant effect on wood gloss. Gloss values of densified wood increased with increasing densification temperature and pressure for all investigated species. Compared to non-densified wood, gloss (85°) values (across/along the grain) for alder, beech, birch and pine increased after treatment to 2109.1/2376.9, 1728.6/2311.1, 2787.5/3000, and 2591.7/1216.7 %, respectively. The greatest gloss values were recorded at 200 °C and pressure of 12 MPa for all tested angles of incident light and for all densified wood samples. Gloss changes for birch were the highest, but the glossiest surface was observed for pine among all investigated species after wood densification.

Some Coating Properties of Black Alder Wood as a Function of Varnish Type and Application Method

The objective of this study was to optimize the sanding and coating processes of black alder wood to promote and support its use in furniture manufacturing. Two criteria have been applied for process optimization, namely, the minimum surface roughness of the samples and power consumption during sanding as a function of various sanding systems. The surface roughness of the sanded specimens and the power consumption during sanding strongly depends on the grit size used. Two eco-varnishes were applied to the samples by spraying. Moreover, the effect of the surface preparation and varnish type on the coating properties expressed by the varnish layer adherence to the substrate and surface glossiness was evaluated. For better glossiness values, the UV-cured varnish was preferred. The sanding with a grit sequence of 60, 120, and 150 grit size abrasives was found to be optimal when applied to black alder wood, and it is recommended to obtain performant UV-coated wood surfaces for furniture products.

One of the most important properties of the surface of wood-based panels is their roughness. This property determines the way of working with the material in the processes of gluing and surface varnishing. The aim of this study was to determine the effect of various sanding belt configurations and the feeding speed of the conveyor belt during grinding on the surface roughness of high-density fiberboards (HDF). The research material was prepared under industrial conditions. Three types of boards were selected for the tests. After grinding, the roughness parameters were measured both transversely and longitudinally relative to the grinding direction, using a Mitutoyo SJ-210 profilometer and the optical method. Based on ANOVA analysis of the data, it was found that the type of HDF boards used and the configuration of the abrasive belts had a statistically significant impact on the roughness. The samples for which the grinding process was performed with sanding belts of the highest grain size had the lowest roughness. For the amplitude roughness parameters, the direction of roughness measurement had a significant influence. These results may provide valuable guidance for the furniture industry in the preparation of HDF for furniture production.