Bamboo is a naturally occurring composite material, which exhibits a decomposable structure with varying composition. The distinct structural features of bamboo contribute to its exceptional strength and flexibility, making it an excellent choice for construction purposes. However, only a limited portion of bamboo species has been studied for its mechanical properties, and research on Bambusa arundinaceae has primarily focused on its pharmaceutical values. Therefore, we investigated the relationship between the structural characteristics of B. arundinaceae and its mechanical properties using axial compression experiments and tangential bending experiments. The results showed that the distribution density of vascular bundles (VBs) of B. arundinaceae ranged from 1.98 to 4.34 pcs/mm²,while the volume fraction of fiber sheaths (FSs) ranged from 35.82 to 42.58%. The average compressive strength, flexural strength, and flexural elasticity modulus were 113.99 MPa, 239.07 MPa, and 17.39 GPa, which were 97.56%, 64.07%, and 66.09% higher than those of moso bamboo (Phyllostachys edulis), respectively. The compressive strength, flexural strengths, and elasticity modulus of B. arundinaceae were positively correlated with both the distribution density of VBs and the volume fraction of FSs. These insights are crucial for the advancement of durable and efficient materials in diverse sectors including construction and manufacturing.

Calamus caesius is one of the most well-known commercial climbing palm species across the world. A comprehensive understanding of the growth-dependent variation in microstructure and polymer distribution can provide fundamental information to guide its end-use applications. In this study, we investigated the age-wise characteristics of rattan stems and the ultrastructure of fibers using electron microscopy, light microscopy, and FTIR. The results showed that the frequency of vascular bundles with a diameter of 0.55∼0.62 mm in C. caesius was 3.49∼3.97 pieces/mm${}^2$. The diameter and length of the metaxylem vessel were 0.32∼0.34 mm and 2.86∼3.00 mm, respectively. Cellulose, lignin, xylan, and HCA are mainly concentrated in the fiber sheath of vascular bundles. The distribution of major polymers in positions other than the top was relatively stable. The tissue proportion of parenchyma, xylem, and phloem did not differ significantly at different positions. The proportion of fibers from 22.27%∼25.33% showed significant differences. The fiber length was 1.43∼1.76 mm, and the diameter was 10.78∼12.63 $\mathsf{\mu }$m. During the growth process of the rattan stem, the secondary wall of fiber cells continued to accumulate inward towards the cell cavity from 2 to 6 layers. The unique fiber properties and stable vascular bundle composition of C. caesius may have potential in fields such as composite materials or renewable energy.

Unlike the culm hollow structure of most bamboo species, Oxytenanthera abyssinica has a unique solid or semi-solid culm, which may endow it with superior mechanical performance. In this study, the variation in fiber morphology and micro-mechanical properties across the radial regions of bamboo culm was examined by optical microscopy, scanning electron microscopy, X-ray diffraction, and nanoindentation. Results showed that the mean values of vascular bundle frequency and fiber tissue proportion were 1.76 pcs/mm${}^2$ and 21.04%, respectively, both of which increased gradually from inner to outer. The mean length, diameter, and length-diameter ratio of the fiber were 2.10 mm, 21.54 $\mathsf{\mu }$m, and 101.41 respectively. The mean indentation modulus of elasticity (IMOE) and hardness were 21.34 GPa and 545.88 MPa. The IMOE exhibited a significant increase from the inner to the middle region, and little change was observed from the middle to the outer region. There were slight fluctuations in hardness along the radial direction. The mean crystallinity and microfibril angle(MFA) of the fibers was 68.12% and 11.26 degrees, respectively. There is a positive correlation between cellulose crystallinity and the IMOE and hardness, while there is a negative correlation between the MFA and the IMOE and the hardness.

Calamus caesius, one of the most valuable high-quality rattans, has emerged as an economical material for use in commercial products. This study systematically investigated the anatomical and microstructural characteristics of Calamus caesius in terms of the frequency, radial diameter, tangential diameter, and form factor of the vascular bundles in both inner and outer regions, as well as the frequency, proportion, length, diameter, and length-diameter ratio of the vessel elements, and the size, double wall thickness, lumen diameter, and ultrastructure of the fibers. The results revealed that the sizes of both vascular bundles and vessel elements in the inner regions were larger than the outer regions, while the fiber proportions and morphological features remained relatively constant. The fibers have a multi-layered structure, most of which exhibited a four-layered structure in their secondary walls. The properties of various tissue structures reflect rattan’s desirable characteristics for use as high-quality commercial timber.

The structure of vascular bundles and the mechanical properties of fibers are crucial factors determining the utilization of bamboo. This study investigated the structure of vascular bundles and evaluated the morphological and micromechanical properties of the fibers in Oligostachyum sulcatum. The results showed that the fiber length and width of O. sulcatum meet the requirements of raw materials for the papermaking process. However, the fiber content in O. sulcatum is relatively low, which may increase the cost of papermaking. The vascular bundle growth exhibited non-uniformity, especially at the top part, with no discernible pattern in bundle area changes. The nanoindentation testing demonstrated that the bamboo’s indentation modulus of elasticity (IMOE) and hardness values were comparable to those of moso bamboo (Phyllostachys edulis), suggesting its potential as a substitute in engineering applications.

The relationship between the structure and mechanical properties of materials has been a hot topic. However, there is a lack of research on the relationship between the structure of rattan and its mechanical properties. This study investigated the anatomical structure and bending properties of Calamus zollingeri, a commercially important rattan species. Samples were collected from different radial positions of the stem and analyzed for their microstructural features and mechanical properties. The distribution and morphology of vascular bundles (VBs), parenchyma cells (PCs), vessels, and fibers were examined using light microscopy. Bending tests were conducted to determine the modulus of rupture (MOR) and modulus of elasticity (MOE). Stepwise linear regression analysis was employed to explore the relationship between structural features and mechanical properties. The results showed that the diameters, lengths and distribution densities of the vessel elements were 280.32 μm, 2163.56 μm, and 3.68 pcs/mm², respectively; the double wall thickness, lumen diameter, diameter, length, length–width ratio were 7.55 μm, 4.30 μm, 11.85 μm, 1569.39 μm, and 134.08, respectively; the tissue ratios of the vessel elements, fibers, sieve elements, and PCs were 22.76%, 20.5%, 4.83%, and 51.87%, respectively. The MOR of C. zollingeri was 55.77 MPa, while the MOE was 2669.11 MPa. The MOR of C. zollingeri was mainly affected by a double wall thickness of fiber and the tissue ratio of PCs, while the MOE was mainly affected by a double arm thickness of fiber and the tissue ratio of the vessel elements. This research provides valuable insights into the structure–property relationships of rattan, which can inform its optimal utilization in various applications.