Nanofluids as an EOR technique are reported to enhance oil recoveries. Among all the nanomaterial silica with promising lab results, economic and environmental acceptability are an ideal material for future applications. Despite the potential to enhance recoveries, understanding the two-fold impact of parameters such as concentration, salinity, stability, injection rate, and irreproducibility of results has arisen ambiguities that have delayed field applications. This integrated study is conducted to ascertain two-fold impacts of concentration and salinity on recovery and stability and evaluates corresponding changes in the recovery mechanism with variance in the parameters. Initially, silica nanofluids’ recovery potential was evaluated by tertiary flooding at different concentrations (0.02, 0.05, 0.07, 0.1) wt. % at 20,000 ppm salinity. The optimum concentration of 0.05 wt. % with the highest potential in terms of recovery, wettability change, and IFT reduction was selected. Then nano-flooding was carried out at higher salinities at a nanomaterial concentration of 0.05 wt. %. For the mechanism’s evaluation, the contact angle, IFT and porosity reduction, along with differential profile changes were analyzed. The recovery potential was found at its highest for 0.05 wt. %, which reduced when concentrations were further increased as the recovery mechanisms changed and compromised stability. Whereas salinity also had a two-fold impact with salinity at 30,000 ppm resulting in lower recovery, higher salinity destabilized the solution but enhanced recoveries by enhancing macroscopic mechanisms of pore throat plugging.

The Chiltan formation is a potential hydrocarbon-producing reservoir in the Indus Basin, Pakistan. However, its diagenetic alterations and heterogeneous behavior lead to significant challenges in accurately characterizing the reservoir and production performance. This manuscript aims to utilize six carbonate core samples of the Chiltan limestone to conduct an in-depth analysis of the diagenetic impacts on reservoir quality. The comprehensive formation evaluation was carried out through thin-section analysis, SEM-EDS, and FTIR investigation, as well as plug porosity and permeability measurements under varying stress conditions. In result, petrography revealed three microfacies of intraclastic packestone (MF1), bioclastic pelliodal packestone (MF2), and bioclastic ooidal grainstone (MF3), with distinct diagenetic features and micro-nano fossil assemblages. The MF1 microfacies consist of bioclasts, ooids, pellets, and induced calcite, while the MF2 microfacies contain micrite cemented peloids, algae, and gastropods. Although, the MF3 grainstone microfacies contains key features of bioclasts, milliods, bivalves, echinoderms, and branchiopods with intense micritization. Diagenesis has a significant impact on petrophysical properties, leading to increased reservoir heterogeneity. The specified depositional environment exposed the alteration of the Chiltan formation during distinct diagenetic phases in marine, meteoric, and burial settings. Marine diagenesis involves biogenic carbonates and micro-nano fossils, while meteoric diagenesis involves mineral dissolution, reprecipitation, secondary porosity, compaction, cementation, and stylolite formation. Pore morphology and mineralogy reveal a complex pore network within the formation, including a micro-nano pore structure, inter–intra particle, moldic, vuggy, and fenestral pores with variations in shape, connectivity, and distribution. Various carbonate mineral phases in the formation samples were analyzed, including the calcite matrix and dolomite crystals, while silica, calcite, and clay minerals were commonly observed cement types in the analysis. The core samples analyzed showed poor reservoir quality, with porosity values ranging from 2.02% to 5.31% and permeability values from 0.264 mD to 0.732 mD, with a standard deviation of 1.21. Stress sensitivity was determined using Klinkenberg-corrected permeability at increasing pore pressure conditions, which indicated around 22%–25% reduction in the measured gas permeability and 7% in Klinkenberg permeability due to increasing the net confining stress. In conclusion, the Chiltan formation possesses intricate reservoir heterogeneity and varied micropore structures caused by diagenesis and depositional settings. The formation exhibits nonuniform pore geometry and low petrophysical properties caused by the diverse depositional environment and various minerals and cement types that result in a low-quality reservoir. Stress sensitivity further decreases the permeability with varying stress levels, emphasizing the need of stress effects in reservoir management. The results of this study provide a solid foundation in reservoir characterization and quality assessment that has implications for predicting fluid flow behavior, providing insight into geological evolution and its impact on reservoir quality and leading to improving resource exploration and production strategies.

Reduction in viscosity at higher temperatures is the main limitation of utilizing cellulose ethers in high thermal reservoir conditions for petroleum industry applications. In this study, cellulose ether (hydroxyethyl methyl cellulose (HEMC)) is modified using organic carbonates, i.e., propylene carbonate (PC) and diethyl carbonate (DEC), to overcome the limitation of reduced viscosity at high temperatures. The polymer composites were characterized through various analytical techniques, including Fourier-transform infrared (FTIR), H-NMR, X-ray diffraction (XRD), scanning electron microscope (SEM), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), ζ-potential measurement, molecular weight determination, and rheology measurements. The experimental results of structural and morphological characterization confirm the modification and formation of a new organic carbonate-based cellulose ether. The thermal analysis revealed that the modified composites have greater stability, as the modified samples demonstrated higher vaporization and decomposition temperatures. ζ-potential measurement indicates higher stability of DEC- and PC-modified composites. The relative viscometry measurement revealed that the modification increased the molecular weight of PC- and DEC-containing polymers, up to 93,000 and 99,000 g/moL, respectively. Moreover, the modified composites exhibited higher levels of stability, shear strength and thermal resistance as confirmed by viscosity measurement through rheology determination. The observed increase in viscosity is likely due to the enhanced inter- and intramolecular interaction and higher molecular weight of modified composites. The organic carbonate performed as a transesterification agent that improves the overall properties of cellulose ether (HEMC) at elevated temperatures as concluded from this study. The modification approach in this study will open the doors to new applications and will be beneficial for substantial development in the petroleum industry.

The applications of cellulose ethers in the petroleum industry represent various limitations in maintaining their rheological properties with an increase in both concentration and temperature. This paper proposed a new method to improve the rheological properties of hydroxyethyl methyl cellulose (HEMC) by incorporating diethyl carbonate (DEC) as a transesterification agent and alkali base solutions. Fourier transform infrared (FTIR) analysis confirmed the grafting of both composites onto the HEMC surface. The addition of sodium hydroxide (NaOH) improved the stability of the polymeric solution as observed from zeta-potential measurement. Shear viscosity and frequency sweep experiments were conducted at concentrations of 0.25-1 wt % at ambient and elevated temperatures ranging from 80-110 degrees C using a rheometer. In the results, the increase in viscosity at specific times and temperatures indicated the activation of DEC through the saponification reactions with alkali solutions. All polymeric solutions exhibited shear-thinning behavior and were fitted well by the Cross model. NaOH-based modified solution exhibited low shear viscosity compared to the DEC-HEMC solution at ambient temperature. However, at 110 degrees C, its viscosity exceeded that of the DEC-HEMC solution due to the activation of DEC. In frequency sweep analysis, the loss modulus (G '') was greater than the storage modulus (G ') at lower frequencies and vice versa at higher frequencies. This signifies the viscoelastic behavior of modified solutions at 0.50 wt % and higher concentrations. The flow point (G ' = G '') shifted to a low frequency, indicating the increasing dominance of elastic behavior with the rising temperature. At 110 degrees C, the NaOH-based modified solution exhibited both viscous and elastic behavior, confirming the solution's thermal stability and flowability. In conclusion, modified HEMC solution was found to be effective in controlling viscosity under ambient conditions, enhancing solubility, and improving thermal stability. This modified composite could play a significant role in optimizing viscoelastic properties and fluid performance under challenging wellbore conditions.

Drilling bits are essential downhole hardware that facilitates drilling operations in high-pressure, high-temperature regions and in most carbonate reservoirs in the world. While the drilling process can be optimized, drilling operators and engineers become curious about how drill bits react during rock breaking and penetration. Since it is experimentally expensive to determine, the goal of the study is to maximize the rate of penetration by modeling fluid interactions around the roller cone drilling bit (RCDB), specifying a suitable number of jet nozzles and venturi effects for non-Newtonian fluids (synthetic-based muds), and examining the effects of mud particles and drill cuttings. Ansys Fluent k-epsilon turbulence viscous model, a second order upwind for momentum, turbulent kinetic energy, and dissipation rate, were used to model the specified 1000 kg/m³ non-Newtonian fluid around the roller cone drill bit. The original geometry of the nozzles was adapted from a Chinese manufacturer whose tricone had three jet nozzles. The results of our six redesigned jet nozzles (3 outer, 39.12 mm, and 3 proximal, 20 mm) sought to offer maximum potential for drilling optimization. However, at a pressure of 9.39 × 10⁴ Pa, the wellbore with particle sizes between 0.10 mm and 4.2 mm drill cuttings observed an improved rate of penetration with a rotation speed of 150 r/min.