To achieve exceptional recyclable DC cable insulation material using thermoplastic polypropylene (PP), we have introduced the organic polar molecule styrene-maleic anhydride copolymer (SMA) into PP-based insulation materials following the principles of deep trap modification. PP, PP/SMA, PP/ethylene-octene copolymer (POE), and PP/POE/SMA insulating samples were prepared, and their meso-morphology, crystalline morphology, and molecular structure were comprehensively characterized. The results indicate that SMA can be uniformly dispersed in PP with minimal impact on the crystalline morphology of PP. The DC electrical properties of the materials were tested at temperatures of 30, 50, and 70 °C. The findings demonstrate that the introduction of SMA can improve the DC properties of the material in both PP and PP/POE. The thermal stimulated depolarization current results reveal that SMA can introduce deep traps into the material, thereby improving its DC properties, which is in agreement with the quantum chemical calculation results. Subsequently, a bipolar carrier transport model was employed for coaxial cables to simulate the space charge distribution in the insulation layer of the four sets of insulation samples as well as the actual cable in service. The results highlight that SMA can significantly suppress space charge in PP and PP/POE systems, and it exhibits excellent electric field distortion resistance. In summary, the results illustrate that SMA is expected to be used as an organic deep trap modifier in PP-based cable insulation materials.

Polypropylene undergoes permanent alterations during the processing and manufacture of cables due to shear effects, which in turn affect all of its qualities. There are currently few research papers on the modulation of material structure and many performance parameters by the shear stress field. In this study, we examined the impact of various shear levels on the structural, mechanical, and electrical properties of polypropylene, as well as their relationships. The results indicated that shear strength decreased the material’s viscosity and oxidation resistance. As shear duration increased, crystallinity began to diminish. In the meantime, the crystallinity improved as the shear temperature rose. The thermal elongations of the sheared samples were all about 5%. Short-term shearing boosted the material’s toughness, but as the degree of shear continued to increase, the material’s toughness and rigidity steadily decreased. The storage modulus of the material decreased with increasing shear, the loss peak initially increased and subsequently decreased, the peak position shifted from low to high temperature, and the loss factor was relatively small. In samples sheared for brief periods, an accumulation of space charge and an increase in its nonlinear threshold field strength were observed. With increasing shear time, the material’s space charge accumulation was repressed, the current density initially grew and then reduced, and the nonlinear threshold field strength initially fell and then increased. Under shearing, the electrical strength of the material increased by approximately 2%. In addition, the presence of an antioxidant improved all of the aforementioned features.

Space charge injection in polypropylene (PP) significantly weakens the stability of HVDC cables. Impact polypropylene copolymer (IPC) is often used as insulation material for AC cables, but in the DC field, IPC has the problem of space charge accumulation. This is because there is a multi-phase structure inside the IPC to which ethylene monomer was added in the production process, and the difference in physicochemical properties of each phase is an important reason for the accumulation of space charge inside the material. In this work, the vinyl phases and propenyl phases of two types of IPC were separated. The film samples were prepared and tested at 30 °C and 50 °C for DC electrical conductivity, and at 30 °C, 50 °C, and 80 °C for space charge. The experimental results show that the DC conductivity of vinyl phases is significantly higher than that of propenyl phases in both types of IPC. The degrees of mismatch between the DC conductivity of vinyl phase and that of propenyl phase are different in the two types of IPC, and the mismatch degree of DC conductivity is from several times to hundreds of times. The conductivity of the two vinyl samples is ohmic. The conductivity of the two propenyl phases shows nonlinearity under different electric field intensity, and the mismatch degree of the two phases increases with temperature. Compared to untreated IPC, at all test temperatures, the maximum space charge density of the propenyl samples is much lower, which can be reduced by about 1/3 at 50 °C and by about 50% at 80 °C. The density of heteropolar charge produced by impurity ionization in the samples and the depth of electrode injection both decreased. At each temperature, the distortion rate of the electric field in propenyl samples is lower than that in IPC, the distortion rate can be reduced by more than 15%, and the distortion rate can be reduced by nearly half at 80 °C. The charge dissipation characteristic of propenyl samples during depolarization is also optimized compared with IPC samples, the time required for charge dissipation to reach stability is shortened, and the residual charge density in the sample is reduced at the end of depolarization. In addition, the relevance between the variation of DC conductivity of phases and space charge characteristics was discussed according to SCLC (space charge limited current) theory. This work provides a feasible reference for the manufacture of high-reliability polypropylene-based cable material with excellent insulation performance.