Super duplex stainless steel has a microstructure consisting of equal proportions of austenite and ferrite. However, welding with Nd:YAG pulsed laser results in an imbalanced microstructure that compromises the steel’s properties. This paper studied the effects of preheating the base metal on pulsed Nd:YAG laser welding. Four conditions were evaluated (no preheating and heating at 100 °C, 200 °C, and 300 °C). The analysis included studying the microstructure, microhardness, and corrosion resistance. Preheating the base metals was found to be an effective method for increasing the volume fractions of austenite. The preheated samples showed an improvement in corrosion resistance compared to the untreated sample. The microhardness varied, with the ferrite amount being higher in the untreated sample.

This paper reports an experimental study of laser welding on duplex stainless steel UNS S32205 employed in the oil and natural gas industries. A pulsed Nd:YAG laser was used to weld the specimens. Bead on plate condition was used. Scanning Electron and Optical microscopy was applied to measure and analyze the cross-sectional of the weld bead. From the experimental results, it was found that the shape and size of the welded spot depend not only on the laser energy, but also on the pulse duration and the focus position. Metallographic observations showed that the microstructure of the weld metal was characterized by large ferrite grains with intra and inter-granular austenite. Large voids delimited by the molten zone boundary were observed in weld beads with low pulse duration. The heat affected zone resulting from the welding is pretty much absent and no cracks were detected.

Anais do Congresso Internacional de Engenharia Mecânica e Industrial (2764-4294) - Otimização E Caracterização Da Soldagem A Laser Pulsada Nd:Yag Em Aços Inoxidáveis Duplex Utilizando Topsis