An experimental and theoretical investigation of the strength properties of aluminum alloys strengthened by dispersed nanoparticles, as well as the determination of the significance of various mechanisms responsible for the strengthening of the material, was carried out. Results of experimental investigation demonstrate that the hardening of aluminum alloy A356 by Al₂O₃ and ScF₃ nanoparticles leads to an increase in the yield strength, ultimate tensile strength, and plasticity. Despite the similar size of Al₂O₃ and ScF₃ nanoparticles, the physicomechanical properties of nanoparticles significantly affect the possibility of increasing the mechanical properties of the A356 aluminum alloy. A physicomathematical model of the occurrence of thermal stresses was developed caused by the mismatch of the coefficients of thermal expansion (CTEs) of the matrix and strengthening particles on the basis of the fundamental principles of mechanics of a deformable solid and taking into account the elastic properties of not only the matrix, but also the particle. The forming of thermal stresses induced due to the mismatch of the coefficients of thermal expansion of the matrix and the strengthening particle in aluminum-based composites was investigated. In the case of thermal deformation of dispersion-hardened alloys, when the CTE of the matrix and particles noticeably differ, an additional stress field is created in the vicinity of the strengthening particle. Thermal stresses increase the effective particle size. This phenomenon can significantly affect the result of the assessment of the yield strength. The strengthening caused by thermal mismatch makes the largest contribution to the yield strength improvement. The yield strength increments due to Nardon×Prewo and Orowan mechanisms are much lower.

A series of casting experiments was conducted with A356 aluminum alloys by applying vibration treatment and using Al-TiB₂ composite master alloys. The main vibration effects include the promotion of nucleation and a reduction in as-cast grain size. Using composite master alloys with titanium diboride microparticles allows further reduction in the average grain size to 140 µm. The reasons for this behavior are discussed in terms of the complex effect on the melt, considering the destruction of dendrites, and the presence of additional crystallization centers. Tensile tests were performed on the samples obtained during the vibration treatment and with titanium diboride particles. The tensile strength increased from 182 to 227 MPa after the vibration treatment for the alloys containing titanium diboride.

It has been found that a high electrical conductivity of 63.1%, the International Annealed Copper Standard (IACS), and high mechanical properties are achieved by the initial aluminum alloy after undergoing four cycles of the severe plastic deformation (SPD) process. It has been found that when TiB₂ particles are introduced into aluminum and the samples are subject to SPD, the mechanical characteristics of the aluminum alloy are improved. Microhardness (HV) increases from 329 to 665 MPa, yield strength (YS) increases from 38 to 103 MPa, and ultimate tensile strength (UTS) increases from 73 to 165 MPa while maintaining the initial electrical conductivity of cast aluminum without reinforcing particles (53.9–54.1% IACS).

This paper examines dispersion hardened alloys based on commercial-purity aluminum obtained by permanent mold casting with the addition of aluminum oxide nanoparticles. Ultrasonic treatment provides a synthesis of non-porous materials and a homogeneous distribution of strengthening particles in the bulk material, thereby increasing the mechanical properties of pure aluminum. It is shown that the increase in the alloy hardness, yield stress, ultimate tensile strength, and lower plasticity depend on the average grain size and a greater amount of nanoparticles in the alloy.

In the present study, aluminum alloys of the Al-Mg system with titanium diboride particles of different size distribution were obtained. The introduction of particles in the alloy was carried out using master alloys obtained through self-propagating high-temperature synthesis (SHS) process. The master alloys consisted of the intermetallic matrix Al-Ti with distributed TiB₂ particles. The master alloys with TiB₂ particles of different size distribution were introduced in the melt with simultaneous ultrasonic treatment, which allowed the grain refining of the aluminum alloy during subsequent solidification. It was found that the introduction of micro- and nanoparticles TiB₂ increased the yield strength, tensile strength, and plasticity of as-cast aluminum alloys. After pass rolling the castings and subsequent annealing, the effect of the presence of particles on the increase of strength properties is much less felt, as compared with the initial alloy. The recrystallization of the structure after pass rolling and annealing was the major contributor to hardening that minimized the effect of dispersion hardening due to the low content of nanosized titanium diboride.