It has been found that a high electrical conductivity of 63.1%, the International Annealed Copper Standard (IACS), and high mechanical properties are achieved by the initial aluminum alloy after undergoing four cycles of the severe plastic deformation (SPD) process. It has been found that when TiB₂ particles are introduced into aluminum and the samples are subject to SPD, the mechanical characteristics of the aluminum alloy are improved. Microhardness (HV) increases from 329 to 665 MPa, yield strength (YS) increases from 38 to 103 MPa, and ultimate tensile strength (UTS) increases from 73 to 165 MPa while maintaining the initial electrical conductivity of cast aluminum without reinforcing particles (53.9–54.1% IACS).

The paper explores the influence of planetary milling on the temperature and velocity of Al-Ti-B powder mixture combustion and also on the structure and phase composition of the reaction products. It is found that the time increase of planetary milling modifies the structure of the powder particles, improves the density of compacted specimens, and increases the temperature and velocity of their combustion. These time dependences are extreme, with maximum values during 180 s planetary milling. Experiments show that the reaction products consist of an aluminum matrix with uniformly distributed particles of titanium diboride of not over 1 µm in size. The average particle size changes with the increase in the time of the planetary milling of the initial powder mixture.

Currently, metal–matrix composite materials are some of the most promising types of materials, and they combine the advantages of a metal matrix and reinforcing particles/fibres. Within the framework of this article, the high-temperature synthesis of metal–matrix composite materials based on the (Ni-Ti)-TiB2 system was studied. The selected approaches make it possible to obtain composite materials of various compositions without contamination and with a high degree of energy efficiency during production processes. Combustion processes in the samples of a 63.5 wt.% NiB + 36.5 wt.% Ti mixture and the phase composition and structure of the synthesis products were researched. It has been established that the synthesis process in the samples proceeds via the spin combustion mechanism. It has been shown that self-propagating high-temperature synthesis (SHS) powder particles have a composite structure and consist of a Ni-Ti matrix and TiB2 reinforcement inclusions that are uniformly distributed inside it. The inclusion size lies in the range between 0.1 and 4 µm, and the average particle size is 0.57 µm. The obtained metal-matrix composite materials can be used in additive manufacturing technologies as ligatures for heat-resistant alloys, as well as for the synthesis of composites using traditional methods of powder metallurgy.