Modifiers such as fibers, fillers, natural and synthetic polymer extenders, oxidants and anti-oxidants, and anti-stripping agents are added to produce modified asphalt. However, polymers are the most widely utilized modifiers to enhance the function of asphalt mixtures. The objective of this research was to evaluate the mechanical properties and durability of epoxidized natural rubber (ENR)-modified asphalt mix under short- and long-term aging conditions. The physical and rheological characteristics of the base asphalt and ENR-modified asphalt (ENRMA) were tested. In order to evaluate the mechanical properties and durability of the modified mixtures, the resilient modulus of the ENR–asphalt mixtures under unaged, and short- and long-term aging conditions at various temperatures and frequencies was obtained. Furthermore, the resistance to moisture damage of asphalt mixtures was investigated. The findings showed that the stiffness of the ENR–asphalt mixes increased because of the mutual influence of short- and long-term aging on the mixes. In addition, ENR reduced the susceptibility to moisture damage. The stiffness of the mixes was influenced by the temperature and frequencies. By using mathematical modelling via the multivariable power least squares method, it was found that temperature was the dominant factor among all other factors. The results suggested that the durability of asphalt pavements is improved by using ENR.

This study aimed to evaluate the effects of carbon nanofibers (CNFs) on the performance of liquid epoxidized natural rubber (LENR)-modified asphalt. The physical, adhesion and rheological properties were determined by several tests such as penetration, elastic recovery, ring and ball softening point, Brookfield rotational viscometer, AFM and dynamic shear rheometer. LENR was used at concentrations of 3, 6, and 9%, while CNFs were used at contents of 0.3, 0.4, and 0.5% by weight of asphalt. Conventional test results showed that the increases in LENR and LENR/CNFs composite contents in binder leads to an increase in the hardness and consistency and a reduction in the temperature susceptibility of base asphalt. Adhesion results revealed that the addition of CNFs significantly increases the adhesion and bonding properties of base and rubberized binders. Rheological properties analysis exhibited that LENR improved the viscoelastic properties and permanent deformation resistance of asphalt at different temperatures and frequencies. On the other hand, it was found that the addition of CNFs significantly improves the stiffness, elasticity, and hardness of LENR-modified binders. The 6% LENR and 0.4% CNFs were found to be the optimum to enhance the physical, adhesion, and rheological properties of asphalt in this study. Thus, it can be stated that the addition of CNFs is promising to improve the performance of rubberized binders for high temperature applications.