Tantalum oxynitride thin films have been deposited by reactive magnetron sputtering, using a fixed proportion reactive gas mixture (85% N₂ + 15% O₂). To produce the films, the partial pressure of the mixture in the working atmosphere was varied. The characteristics of the produced films were analyzed from three main perspectives and correspondent correlations: the study of the bonding states in the films, the efficiency of photo-degradation, and the antibacterial/antibiofilm capacity of the coatings against Salmonella. X-ray Photoelectron Spectroscopy results suggest that nitride and oxynitride features agree with a constant behavior relative to the tantalum chemistry. The coatings deposited with a higher reactive gas mixture partial pressure exhibit a significantly better antibiofilm capacity. Favorable antibacterial resistance was correlated with the presence of dominant oxynitride contributions. The photocatalytic ability of the deposited films was assessed by measuring the level of degradation of an aqueous solution containing methyl orange, with or without the addition of H₂O₂, under UV or VIS irradiation. Degradation efficiencies as high as 82% have been obtained, suggesting that tantalum oxynitride films, obtained in certain configurations, are promising materials for the photodegradation of organic pollutants (dyes).

In this contribution, based on the detailed understanding of the processes’ characteristics during reactive high-power impulse magnetron sputtering (HiPIMS), we demonstrated the deposition of silicon oxide (SiO₂) thin films with improved optical and mechanical performances. A strategy for stabilizing the arc-free HiPIMS of Si target in the presence of oxygen was investigated. Arcing was suppressed by suitable pulse configurations, ensuring good process stability without using any feedback control system. It was found that arcing can be significantly alleviated when ultra-short HiPIMS pulses are applied on the target. The optical and mechanical properties of SiO₂ coatings deposited at various pulsing configurations were analyzed. The coatings prepared by ultra-short pulse HiPIMS exhibited better optical and mechanical performance compared to the coatings prepared by long pulse HiPIMS. The optimized SiO₂ coatings on quartz substrates exhibited an average transmittance of 98.5% in the 190–1100-nm wavelength range, hardness of 9.27 GPa, hardness/Young’s modulus ratio of 0.138, and critical adhesion load of 14.8 N. The optical and mechanical properties are correlated with the film morphology, which is inherently related to energetic conditions and process stability during film growth.