This paper discusses the structure morphology and the thermal and swelling behavior of physically crosslinked hydrogels, obtained from applying four successive freezing–thawing cycles to poly (vinyl alcohol) blended with various amounts of κ-carrageenan. The addition of carrageenan in a weight ratio of 0.5 determines a twofold increase in the swelling degree and the early diffusion coefficients of the hydrogels when immersed in distilled water, due to a decrease in the crystallinity of the polymer matrix. The diffusion of water into the polymer matrix could be considered as a relaxation-controlled transport (anomalous diffusion). The presence of the sulfate groups determines an increased affinity of the hydrogels towards crystal violet cationic dye. A maximum physisorption capacity of up to 121.4 mg/g for this dye was attained at equilibrium.

To enhance the sliding wear and corrosion behavior of steels with low carbon content, cermet composite coatings are usually deposited on their surface by various deposition processes. Laser cladding, compared to other deposition techniques such as electroplating, arc welding, and thermal spraying, has numerous advantages to produce such protective coatings. The paper presents the optimization of laser cladding deposition speed versus energy density in order to obtain WC-Co/NiCrBSi coatings with Ni-Al addition free of defects and reduced porosity deposited on low carbon steel substrate. The microstructure and chemical composition were investigated by SEM combined with EDX analysis while XRD was performed in order to examinate the phases within the coatings. In order to investigate the cladding speed influence on the coatings, hardness measurements, POD (pin on disk) wear tests and corrosion tests in 3.5% NaCl solution were carried out. The results showed that an optimal cladding speed has a crucial impact on the microstructure, composition, and hardness. It was found out that optimizing the cladding deposition speed proved to be effective in enhancing the sliding wear resistance and corrosion behavior by controlling the iron content within the coatings.

This paper presents an alternative approach to obtaining crack- and pore-free NiCrBSiFeCuMoC hard coatings on a low alloy steel substrate through coaxial laser cladding, by using Inconel 718 as a buffer layer between the hard coating and the base material. The presence of the buffer layer reduces the overall cracking susceptibility of the hardfacing material by reducing the compressive stresses developed during the cladding process and ensuring a more uniform heat distribution gradient at the surface of the material than the base metal alone, which provides an additional hardness and wear coefficient increase of 7% and improves the corrosion resistance of the obtained materials by 20%, in comparison with the reference sample obtained without an intermediate layer, by using the same operational parameters and minimizes elemental dilution with the substrate. Our method could prove useful in increasing the quality and life cycle of expensive high-performance hard-coated materials, especially those working under demanding operational and environmental conditions.