In the present research diamond-like carbon (DLC) films containing 4–29 at.% of silicon were deposited by reactive magnetron sputtering of carbon target. Study by X-ray photoelectron spectroscopy revealed the presence of Si–C bonds in the films. Nevertheless, a significant amount of Si–O–C and Si–O_x bonds was present too. The shape of the Raman scattering spectra of all studied diamond-like carbon containing silicon (DLC:Si) films was typical for diamond-like carbon. However, some peculiarities related to silicon doping were found. Studies on the dependence of DLC:Si of the optical transmittance spectra on the Si atomic concentration have shown that doping by silicon affects linear, as well as nonlinear, optical properties of the films. It is shown that the normalized reflectance of DLC:Si films decreased with the increased exciting light fluence. No clear relation between the normalized reflectance and photoexcited charge carrier relaxation time was found. It was suggested that that the normalized reflectance decrease with fluence can be related to nonlinear optical properties of the hydrogenated diamond-like carbon phase in DLC:Si film.

In the current work, a new antibacterial bandage was proposed where diamond-like carbon with silver nanoparticle (DLC:Ag)-coated synthetic silk tissue was used as a building block. The DLC:Ag structure, the dimensions of nanoparticles, the silver concentration and the silver ion release were studied systematically employing scanning electron microscopy, energy dispersive X-ray spectroscopy and atomic absorption spectroscopy, respectively. Antimicrobial properties were investigated using microbiological tests (disk diffusion method and spread-plate technique). The DLC:Ag layer was stabilized on the surface of the bandage using a thin layer of medical grade gelatin and cellulose. Four different strains of Staphylococcus aureus extracted from humans’ and animals’ infected wounds were used. It is demonstrated that the efficiency of the Ag⁺ ion release to the aqueous media can be increased by further RF oxygen plasma etching of the nanocomposite. It was obtained that the best antibacterial properties were demonstrated by the plasma-processed DLC:Ag layer having a 3.12 at % Ag surface concentration with the dominating linear dimensions of nanoparticles being 23.7 nm. An extra protective layer made from cellulose and gelatin with agar contributed to the accumulation and efficient release of silver ions to the aqueous media, increasing bandage antimicrobial efficiency up to 50% as compared to the single DLC:Ag layer on textile.

A growing number of severe infections are related to antibiotic-resistant bacteria, therefore, in recent years, alternative antimicrobial materials based on silver nanoparticles (NPs) attracted a lot of attention. In the current research, we present a medical patch prototype containing diamond-like carbon nanocomposite thin films doped with silver nanoparticles (DLC:Ag), as a source of silver ions, and an aqueous mass of the gelatin/agar mixture as a silver ion accumulation layer. The DLC:Ag thin films with 3.4 at.% of silver were deposited on synthetic silk employing reactive unbalanced DC magnetron sputtering of the silver target with argon ions performed in the acetylene gas atmosphere. The average size of the silver nanoparticles as defined by scanning electron microscope was 24 nm. After the film deposition, the samples were etched with RF oxygen plasma, aiming at efficient silver ion release in aqueous media from the nanocomposite film. In the patch prototype, a mixture of agar and gelatin was applied in silicone carrier with cavities, acting as a silver ion accumulation layer that further enhanced the antimicrobial efficiency. It was found that the DLC:Ag thin film on the silk after soaking in water for 24 h was able to release up to 4 ppm of Ag. The microbiological experiments using S. aureus bacteria were performed with the patch prototype and the silver ion saturated water, demonstrated the inactivation of 99% and 79% of bacteria, respectively. Scanning electron microscopy analysis showed that silver NPs destroyed the bacteria cell and the bacteria affected by Ag ions had spots and perforated cell wall areas with cytoplasm leakage out was obtained. A preliminary preclinical study using the laboratory animals demonstrated that using the patch prototype, the methicillin-resistant S. aureus (MRSA)-infected wound on skin surface healed faster compared with control and was able to kill all MRSA bacteria strains in the wound’s bed after 72 h of treatment.

Graphene was synthesized directly on Si(100) substrates by microwave plasma-enhanced chemical vapor deposition (MW-PECVD). The effects of the graphene structure on the electrical and photovoltaic properties of graphene/n-Si(100) were studied. The samples were investigated using Raman spectroscopy, atomic force microscopy, and by measuring current–voltage (I-V) graphs. The temperature of the hydrogen plasma annealing prior to graphene synthesis was an essential parameter regarding the graphene/Si contact I-V characteristics and photovoltaic parameters. Graphene n-type self-doping was found to occur due to the native SiO₂ interlayer at the graphene/Si junction. It was the prevalent cause of the significant decrease in the reverse current and short-circuit current. No photovoltaic effect dependence on the graphene roughness and work function could be observed.

In the present research, hexagonal boron nitride (h-BN) films were deposited by reactive high-power impulse magnetron sputtering (HiPIMS) of the pure boron target. Nitrogen was used as both a sputtering gas and a reactive gas. It was shown that, using only nitrogen gas, hexagonal-boron-phase thin films were synthesized successfully. The deposition temperature, time, and nitrogen gas flow effects were studied. It was found that an increase in deposition temperature resulted in hydrogen desorption, less intensive hydrogen-bond-related luminescence features in the Raman spectra of the films, and increased h-BN crystallite size. Increases in deposition time affect crystallites, which form larger conglomerates, with size decreases. The conglomerates’ size and surface roughness increase with increases in both time and temperature. An increase in the nitrogen flow was beneficial for a significant reduction in the carbon amount in the h-BN films and the appearance of the h-BN-related features in the lateral force microscopy images.