In addition to filtering some sediments, hydrophobic wood sponges can also absorb many organic solvents, particularly crude oil. The leakage of crude oil poses a serious threat to the marine ecosystem, and oil mixed with water also generates great danger for its use. From the perspective of low cost and high performance, wood sponges exhibit great potential for dealing with crude oil pollution. Wood sponge is a renewable material. With a highly oriented layered structure and a highly compressible three-dimensional porous frame, wood sponges are extremely hydrophobic, making them ideal for oil–water separation. Currently, the most common approach for creating wood sponge is to first destroy the wood cell wall to obtain a porous-oriented layered structure and then enhance the oil–water separation ability via superhydrophobic treatment. Wood sponge prepared using various experimental methods and different natural woods exhibits distinctive properties in regards to robustness, compressibility, fatigue resistance, and oil absorption ability. As an aerogel material, wood sponge offers multi-action (absorption, filtration) and reusable oil–water separation functions. This paper introduces the advantages of the use of wood sponge for oil–water separation. The physical and chemical properties of wood sponge and its mechanism of adsorbing crude oil are explained. The synthesis method and the properties are discussed. Finally, the use of wood sponge is summarized and prospected.

Due to a large number of harmful chemicals flowing into the water source in production and life, the water quality deteriorates, and the use value of water is reduced or lost. Biochar has a strong physical adsorption effect, but it can only separate pollutants from water and cannot eliminate pollutants fundamentally. Photocatalytic degradation technology using photocatalysts uses chemical methods to degrade or mineralize organic pollutants, but it is difficult to recover and reuse. Woody biomass has the advantages of huge reserves, convenient access and a low price. Processing woody biomass into biochar and then combining it with photocatalysts has played a complementary role. In this paper, the shortcomings of a photocatalyst and biochar in water treatment are introduced, respectively, and the advantages of a woody biochar-based photocatalyst made by combining them are summarized. The preparation and assembly methods of the woody biochar-based photocatalyst starting from the preparation of biochar are listed, and the water treatment efficiency of the woody biochar-based photocatalyst using different photocatalysts is listed. Finally, the future development of the woody biochar-based photocatalyst is summarized and prospected.

Transparent films with excellent antibacterial properties and strong mechanical properties are highly sought after in packaging applications. In this study, Ag/SiO₂ nanoparticles were introduced into a mixed solution of chitosan (CS) and polyvinyl alcohol (PVA) and a Ag/SiO₂-CS-PVA transparent film was developed. The excellent properties of the film were confirmed by light transmittance, water contact angle tests and tensile tests. In addition, for the antibacterial test, the antibacterial properties of the sample against Gram-negative bacteria (Escherichia coli) and Gram-positive bacteria (Staphylococcus aureus) were explored, and the average size of the bacteriostatic circle was measured by the cross method. The final results show that Ag/SiO₂-CS-PVA transparent film has the advantages of good antibacterial properties, high transparency and high mechanical strength.

The efficient exploitation of planted fast-growing wood is crucial for enhancing wood resource utilization. In this study, the fast-growing poplar wood was modified by in situ impregnation through vacuum impregnation with polyvinyl alcohol and nano-silica sol as impregnation modifiers, combined with delignification–freezing pretreatment. The samples were characterized by FTIR, XRD, SEM, and the universal mechanical testing machine. The results showed that the wrinkle deformation and cracking of the wood blocks were greatly alleviated after the delignification–freezing pretreatment and the polyvinyl alcohol and nano-silica sol were successfully integrated into the wood. The resulting polyvinyl alcohol–silica sol poplar composites exhibited about 216%, 80% and 43% higher compressive strength with respect to delignified wood, natural wood and impregnated natural wood, respectively, thereby demonstrating superior mechanical properties and potential opportunities for value-added and efficient utilization of low-quality wood.