Natural and bio-based construction materials such as bamboo, cork, or natural fiber composites offer a promising solution for enhancing the environmental sustainability of buildings. In this sense, the paper presents an experimental thermo-acoustic characterization of four common Ecuadorian natural fibers, abaca (Musa textilis), cabuya (Furcraea andina), coir (Cocos nucifera), and totora (Schoenoplectus californicus). Different densities were considered, from 85 kg/m³ (Cabuya) to 244 kg/m³ (totora), to thermo-acoustically characterize the samples built with these fibers, by means of the guarded-hot-plate (GHP) and impedance tube methods in-lab experimental benches. The exhaustive original characterization of the evaluated natural fiber composites showed a promising overall thermo-acoustic behavior. The thermal conductivity of the fibers was around 0.04–0.06 W/m·K and, therefore, comparable to other materials such as polystyrene, polyurethane, or aerogel that are already utilized for similar applications. On the other hand, the sound-absorption properties of the evaluated fibers are also very competitive, but strongly affected by the thickness of the sample, with noise reduction coefficient NRC ranging from 0.12 to 0.53. Consequently, the production and distribution of these materials in the Ecuadorian market for thermal insulation and acoustic conditioning constitute an alternative characterized by good technical performance, which, compared to synthetic composites used in the construction industry for similar duties, is ecological, sustainable, and has low built-in energy consumption.

This study is dedicated to advancing practical and experimental knowledge within sustainable construction and enhancing community productivity, focusing on cattail schoenoplectus californicus, Cyperaceae fibers in Imbabura, Ecuador. The research aims to meticulously analyze and understand cattail fibers’ physical and mechanical properties, characteristics, and potential applications through extensive laboratory testing. The study strives to contribute significantly to the ongoing discussions surrounding sustainable building materials by offering a rich repository of scientific data and insights from our in-depth investigations. Furthermore, we delve into biotechnology and biomimicry, seeking inspiration from the natural world to innovate our construction methodologies. Our exploration also encompasses the technical dimensions of a building, artisanal craftsmanship, eco-conscious design principles, and the evaluation of seismic strength within architectural, structural, and acoustical design frameworks. Through this comprehensive approach, we aspire to illuminate new pathways for employing cattail in sustainable construction practices.

The growing demand for sustainable materials has driven significant interest in composites reinforced with organic fibers, due to their mechanical performance, availability, and reduced environmental impact. This study investigates the mechanical behavior of two composite configurations: a cross-woven fabric and a sandwich-type panel, both made from totora (Schoenoplectus californicus) and low-density polyethylene–aluminum (LDPE–Al). Our experimental results show that the cross-woven variant achieved higher impact resistance (2.51 J), tensile strength (5.82 MPa), and greater deformation capacity (6.76%), making it more suitable for applications requiring energy absorption and flexibility, such as interior cladding and modular furniture. In contrast, the sandwich configuration exhibited superior stiffness (910 MPa), favoring structural panels and low-load roofing uses. This research distinguishes itself by integrating biodegradable totora fibers with recycled LDPE–Al to fabricate sustainable construction components, advancing circular economy principles while addressing limitations in previous composite formulations through improved mechanical balance and application-specific performance.

Fused deposition modeling (FDM) of carbon fiber-reinforced polycarbonate (PC-CF) is increasingly used in medical applications due to its excellent strength-to-weight ratio and adaptability for custom geometries. However, sterilization is a critical step that may compromise the structural integrity of polymer composites. This study investigates the effects of two low-temperature sterilization methods—ethylene oxide (EO) and hydrogen peroxide vapor (HP)—on the mechanical, thermal, and viscoelastic properties of FDM-printed PC-CF parts. Characterization included tensile, impact, and hardness tests; thermomechanical analysis (TMA); and dynamic mechanical analysis (DMA). EO sterilization resulted in approximately 20% reduced elongation at break and lower glass transition temperature, indicating a loss of ductility and thermal stability. HP-treated samples showed reduced stiffness (16% in Young modulus) but increased Tg and reduced thermal expansion, suggesting improved dimensional stability. DMA results confirmed distinct viscoelastic behavior between treatment types. These findings provide evidence for selecting appropriate sterilization protocols for FDM-manufactured PC-CF components used in functional medical devices.