This study focuses on the growth of Cu₂O/CuO nanowires by one-step thermal oxidation using a flexible copper mesh at oxidation temperatures in the range of 300 to 600 °C in a controlled atmosphere of mixed-flow Ar and O₂ gases. Thermal oxidation is one of the simplest used methods to obtain nanowires on a metal surface, offering advantages such as low production costs and the ability to produce metal oxides on a large scale without the use of hazardous chemical compounds. The growth of metal oxides on a conductive substrate, forming metal/oxide structures, has proven to be an effective method for enhancing charge-transfer efficiency. The as-synthesized Cu/Cu₂O/CuO (Nw) electrodes were structurally and morphologically characterized using techniques such as XRD and SEM/EDX analysis to investigate the structure modification and morphologies of the materials. The supercapacitor properties of the as-developed Cu/Cu₂O/CuO (Nw) electrodes were then examined using cyclic voltammetry (CV), galvanostatic charge–discharge (GCD) measurements, and electrochemical impedance spectroscopy (EIS). The CV curves show that the Cu/Cu₂O/CuO (Nw) structure acts as a positive electrode, and, at a scan rate of 5 mV s ⁻¹, the highest capacitance values reached 26.158 mF cm⁻² for the electrode oxidized at a temperature of 300 °C. The assessment of the flexibility of the electrodes was performed at various bending angles, including 0°, 45°, 90°, 135°, and 180°. The GCD analysis revealed a maximum specific capacitance of 21.198 mF cm⁻² at a low power density of 0.5 mA cm⁻² for the oxidation temperature of 300 °C. The cycle life assessment of the all of the as-obtained Cu/Cu₂O/CuO (Nw) electrodes over 500 cycles was performed by GCD analysis, which confirmed their electrochemical stability.

Due to population growth and global technological development, energy consumption has increased exponentially. The global energy crisis opens up many hotly debated topics regarding energy generation and consumption. Not only is energy production in short supply due to limited energy resources but efficient and sustainable storage has become a very important goal. Currently, there are energy storage devices such as batteries, capacitors, and super-capacitors. Supercapacitors or electrochemical capacitors can be very advantageous replacements for batteries and capacitors because they can achieve higher power density and energy density characteristics. The evolution and progress of society demand the use of innovative and composite nanostructured metal oxide materials, which fulfill the requirements of high-performance technologies. This review mainly addresses the synthesis techniques and properties of 2D and 3D metal oxide nanostructured materials, especially based on Ti, Fe, Ga, and Sn ions, electrochemical methods used for the characterization and application of 2D, and 3D nanostructured metal oxide structures in electrochemical storage systems of energy.

This study investigated a hybrid electrode based on titanium/titanium dioxide nanowires/reduced graphene oxide (Ti-TiO₂(NW)/rGO) that was developed in two stages. The Ti-TiO₂(NW)/rGO was obtained by hydrothermal treatment in a mixed solution of H₂O₂ and melamine for Ti-TiO₂ support, followed by a simple spin-coating deposition method and thermal oxidation in a controlled atmosphere of nitrogen gas (99%). The as-prepared structures of electrodes were characterized using ultraviolet-visible spectroscopy (UV-Vis), X-ray diffraction (XRD), Raman spectroscopy, and scanning electron microscopy (SEM). In addition, the electrochemical behavior was assessed by cyclic voltammetry (CV) in a 1M HNO₃-supporting electrolyte and in the presence of 4 mM K₄Fe(CN)₆ 3H₂O to determine the electroactive surface area and apparent diffusion coefficient of the hybrid electrode. The development of the Ti-TiO₂(NW)/rGO hybrid electrode provides a sensitive method for photo-electrooxidation of doxorubicin due to exploiting the synergistic and remarkable properties of the nanowires of TiO₂ and of reduced graphene oxide (rGO) layer on the electrode surface.

Recently, a new class of materials with very high porosity and ultra-lightweight, namely, semiconductor aero-materials, has attracted the attention of many researchers. Semiconductor aero-materials, due to their special properties, can be used in the development of devices applied in biomedical, electronics, optoelectronic, energy conversion and storage, sensors, biosensors, catalysis, automotive, and aeronautic industries. Although aero-materials and aerogels are similar, different methods of obtaining them are used. Aerogels are synthesized from organic, inorganic, or hybrid precursors, the main characteristic being that they are gel-like solids with a high air content (99.9%) in the structure. Thus, three-dimensional (3D) interconnected porous network chains are formed, resulting in light solid-state structures with very high porosity due to the large number of air pores in the network. On the other hand, to obtain aero-materials with controlled properties such as morphology, shape, or the formation of 3D hollow structures, sacrificial templates are used. Thus, sacrificial structures (which can be easily removed) can be obtained depending on the morphology of the 3D structure to be obtained. Therefore, this review paper offers a comprehensive coverage of the synthesis methods of different types of semiconductor aero-materials that use ZnO tetrapod, ZnO(T), as a sacrificial template, related to the present and future perspectives. These ZnO(T) sacrificial substrates offer several advantages, including diverse synthesis processes and easy removal methods that occur simultaneously with the growth of the desired aero-materials.

The nanoporous copper (NPC)-copper oxides (Cu₂O/CuO)/reduced graphene oxide (rGO) composite structure was synthesized by combining the dealloying process of Cu₄₈Zr₄₇Al₅ amorphous ribbons with a microwave-assisted hydrothermal technique at a temperature of 200 °C. The main advantage of the microwave-assisted hydrothermal process is the oxidation of nanoporous copper together with the in situ reduction of graphene oxide to form rGO. The integration of rGO with NPC improves electrical conductivity and streamlines the process of electron transfer. This composite exhibit considerable potential in electrochemical catalysis application, due to the combined catalytic activity of NPC and the chemical reactivity of rGO. Our study relates the transition to n-type rGO in microwave-assisted hydrothermal reactions, and also the development of an electrode material suitable for electrochemical applications based on the p-p-n junction NPC-Cu₂O/CuO/rGO heterostructure. To confirm the formation of the composite structure, structural, morphological, and optical techniques as XRD, SEM/EDX, UV-Vis and Raman spectroscopy were used. The composite’s electrochemical properties were measured by EIS and Mott-Schottky analyses, showing a charge transfer resistance (Rp) of 250 Ω and indicating the type of the semiconductor properties. The calculated carrier densities of 4.2 × 10¹⁸ cm⁻³ confirms n-type semiconductor characteristic for rGO, and 7.22 × 10¹⁸ cm⁻³ for Cu₂O/CuO indicating p-type characteristic.

This research demonstrates, for the first time, the integration of aero-titania material in sensor devices. An innovative approach for the practical application of aero-titania (aero-TiO₂) materials in photodetectors and the characterization under ultraviolet irradiation was assessed. The fabrication of aero-materials was carried out through the atomic layer deposition (ALD) of titanium dioxide ultrathin layers on a sacrificial network consisting of zinc oxide micro-tetrapods. This process was followed by a selective etching of the sacrificial ZnO template and formation of aero-titania hollow micro-tetrapods. The obtained material has been characterized using UV-Vis spectroscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis. The development of photodetectors was achieved through the sequential spin-coating deposition of aero-TiO₂ onto an interdigitated ceramic electrode. The obtained results show that, for high-intensity ultraviolet, the maximum sensitivity was reached for the two-deposited-layer aero-TiO₂ sensor at about 23, since for the low-intensity UV the highest sensitivity was recorded for the one-deposited-layer aero-TiO₂ sensor at about 12. In terms of the responsivity, the highest response was obtained for the one-deposited-layer aero-TiO₂ sensor under low-intensity illumination, reaching about 1.23 × 10⁻⁴ A W⁻¹ cm⁻². Thus, the aero-TiO₂ structure demonstrates the practical viability and application potential of this emerging class of materials in advanced sensing technologies.