Wool fibers usually need shrinkproofing finishing. The enzyme process is an eco-friendly technology but the traditional exhaustion treatment usually takes excessive time. This study developed a novel multiple padding shrinkproofing process of wool with Savinase 16L and an organic phosphine compound {[HO(CH₂)_n]₃P, n ∈ (1, 10)}. SEM and XPS analyses were employed to compare the wool treated respectively by exhaustion and by padding to reveal the effect of multiple padding. The results showed that treated wool fiber achieved the requirement of machine-washable (area shrinkage less than 8% according to standard TM 31 5 × 5A) in 2.5 min by the padding process. The padding process can control the adsorbance of enzyme on wool, which makes treatment more uniform and avoids strong damage of the wool. Also, the removal efficiency of the disulfide bond was about 15 times as much as in the exhaustion treatment in 2.5 min. The average catalytic rate of the padding process was 14 times faster than the exhaustion process, and the process time (2.5 min) decreased by 32.5 min compared with the exhaustion process (35 min). Multiple padding techniques can achieve continuous production and replace the environmentally harmful chlorination process. Our results provide the underlying insights needed to guide the research of the enzyme process application.

The mechanical behavior of phase-change microcapsules (microPCMs) is of vital significance for practical applications in thermal energy storage. Hence, a new type of microPCMs based on an n-octadecane (C18) core and a melamine-urea-formaldehyde (MUF)/diatomite hybrid shell was developed through in situ polymerization. Based on SEM micrographs, most microPCMs exhibited a nearly spherical and smooth microstructure, with broadened particle size distributions. It was confirmed by Fourier transform infrared (FTIR) that successful polymerization of diatomite into the microPCMs occurred, and that additional diatomite had no effect on the core coated by the shell. In addition, the results of the differential scanning calorimeter (DSC) and Atomic Force Microscopy (AFM) demonstrated that the mechanical properties of the microPCMs were remarkably improved by the addition of a moderate amount of diatomite, but that the heat enthalpy and encapsulated efficiency (η) decreased slightly. The incorporation of 2 wt % diatomite resulted in the average Young’s modulus of microPCMs, which was 1.64 times greater than those of microPCMs without diatomite. Furthermore, the melting and crystallization enthalpies and the encapsulated efficiency of the microPCMs were as high as 237.6 J/g, 234.4 J/g and 77.90%, respectively. The microPCMs with a polymer/diatomite hybrid shell may become the potential materials in the application of thermal energy storage.

Much research has focused on improvement of the structural and mechanical properties of regenerated keratin materials by physical or chemical methods in recent years. In this research, regenerated keratin materials were modified with graphene oxide (GO). The properties of modified keratin films and the mechanism of interaction between GO and keratin macromolecules were studied. The SEM and XRD test results showed that the orientation of keratin macromolecules could be effectively improved by GO, which favored improvement of the keratin material’s crystallinity and made the films more uniform and compact. The thermal stability and mechanical properties of GO-modified keratin films were also improved significantly. At the same time, the reaction mechanism between keratin and GO materials was analyzed by sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE), FT-IR, and Raman spectroscopy. It was shown that there was no chemical reaction between GO and keratin molecules, and the interaction between them was mainly via hydrogen bonding and van der Waals forces.

Based on active heating materials (the phase change microcapsules (microPCMs)) and passive insulating materials (SiO₂ aerogel), a new-type multilayer low temperature protective composite fabric (MPF) was designed and manufactured to meet the demands of protection and operation in a short time under a low-temperature environment. Results showed that the MPF consisted of three layers including the fabric layer, the microPCM function layer, and the SiO₂ aerogel thermal insulation layer. The differential scanning calorimeter (DSC) results demonstrated that the phase transition enthalpy of the composite was 96.2 J/g during the cooling process. The low-temperature resistance and thermal insulation performance at −50 °C were investigated. The results also demonstrated that the low-temperature resistance time of the MPF was 660 s and the power consumption of the MPFs needed to maintain 37 °C for 10 and 20 min were 629 J and 1872 J, respectively. Compared with the microPCM function layer and the thermal insulation layer, which have the same thickness as the MPF, the low-temperature resistance time of the MPF was prolonged for about 2 and 3 min, respectively. The MPF could provide effective protection of the low-temperature work in a short time and could be applied as potential materials in low-temperature protection.