The applications of magnetron sputtering technology on the surface coating of fabrics have attracted more and more attention from researchers. Over the past 15 years, researches on magnetron sputtering coated fabrics have been mainly focused on electromagnetic shielding, bacterial resistance, hydrophilic and hydrophobic properties and structural color etc. In this review, recent progress of the technology is discussed in detail, and the common target materials, technologies and functions and characterization of coated fabrics are summarized and analyzed. Finally, the existing problems and future prospects of this developing field are briefly proposed and discussed.

Wool fibers usually need shrinkproofing finishing. The enzyme process is an eco-friendly technology but the traditional exhaustion treatment usually takes excessive time. This study developed a novel multiple padding shrinkproofing process of wool with Savinase 16L and an organic phosphine compound {[HO(CH₂)_n]₃P, n ∈ (1, 10)}. SEM and XPS analyses were employed to compare the wool treated respectively by exhaustion and by padding to reveal the effect of multiple padding. The results showed that treated wool fiber achieved the requirement of machine-washable (area shrinkage less than 8% according to standard TM 31 5 × 5A) in 2.5 min by the padding process. The padding process can control the adsorbance of enzyme on wool, which makes treatment more uniform and avoids strong damage of the wool. Also, the removal efficiency of the disulfide bond was about 15 times as much as in the exhaustion treatment in 2.5 min. The average catalytic rate of the padding process was 14 times faster than the exhaustion process, and the process time (2.5 min) decreased by 32.5 min compared with the exhaustion process (35 min). Multiple padding techniques can achieve continuous production and replace the environmentally harmful chlorination process. Our results provide the underlying insights needed to guide the research of the enzyme process application.

Much research has focused on improvement of the structural and mechanical properties of regenerated keratin materials by physical or chemical methods in recent years. In this research, regenerated keratin materials were modified with graphene oxide (GO). The properties of modified keratin films and the mechanism of interaction between GO and keratin macromolecules were studied. The SEM and XRD test results showed that the orientation of keratin macromolecules could be effectively improved by GO, which favored improvement of the keratin material’s crystallinity and made the films more uniform and compact. The thermal stability and mechanical properties of GO-modified keratin films were also improved significantly. At the same time, the reaction mechanism between keratin and GO materials was analyzed by sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE), FT-IR, and Raman spectroscopy. It was shown that there was no chemical reaction between GO and keratin molecules, and the interaction between them was mainly via hydrogen bonding and van der Waals forces.

TPU-coated polyester fabric was used as the substrate of a flexible temperature sensor and Ag nanoparticles were deposited on its surface as the temperature sensing layer by the magnetron sputtering method. The effects of sputtering powers and heat treatment on properties of the sensing layers, such as the temperature coefficient of resistance (TCR), linearity, hysteresis, drift, reliability, and bending resistance, were mainly studied. The results showed that the TCR (0.00234 °C⁻¹) was the highest when sputtering power was 90 W and sputtering pressure was 0.8 Pa. The crystallinity of Ag particles would improve, as the TCR was improved to 0.00262 °C⁻¹ under heat treatment condition at 160°. The Ag layer obtained excellent linearity, lower hysteresis and drift value, as well as good reliability and bending resistance when the sputtering power was 90 W. The flexible temperature sensor based on the coated polyester fabric improved the softness and comfortableness of sensor, which can be further applied in intelligent wearable products.