High-modulus asphalt mixture (HMAM) is one of the most effective materials to enhance the rutting resistance of asphalt pavement and upgrade pavement sustainability. The objectives of this study are to investigate the modulus properties of different HMAMs and their correlation with the rutting resistance, to propose reasonable modulus evaluation indicators, and to analyze the rutting resistance mechanisms of different materials (hard asphalt, polyethylene, dissolved polyolefin). The effect of three HMAMs and two styrene-butadiene-styrene (SBS) modifiers on asphalt mixtures’ rutting resistance were evaluated by dynamic modulus test and wheel track test, and the results were simulated and further analyzed via ABAQUS. The results indicate that the dynamic modulus of the mixtures showed a gradual increase and decrease with the increase of loading frequency and testing temperature, respectively. The ratio of dynamic modulus in low frequency to that in high frequency correlates well with dynamic stability under high-temperature conditions, and the wider the frequency coverage, the higher the correlation between this ratio and dynamic stability. The rutting resistance of asphalt pavements can be improved by reducing the frequency sensitivity of HMAMs under high temperatures or by increasing the modulus’ absolute value of the pavement structural layer. Therefore, two indicators, the absolute value of the modulus and the ratio of 0.1 Hz dynamic modulus to 25 Hz dynamic modulus at 55 °C, are recommended for the evaluation of rutting resistance of HMAMs. Based on the evaluation indexes proposed in this paper, a comparative analysis of the rutting resistance mechanism of HMAMs prepared with different materials was carried out, and it was concluded that the mixture with high-modulus agents had the best rutting resistance, which is consistent with the test road observations, thus verifying the feasibility of the modulus evaluation indexes recommended in this paper for the evaluation of the rutting resistance of different types of HMAMs.

This paper reviews the research progress and development of aluminate long afterglow luminescent materials in the field of road marking, especially the study of rare earth ion-activated strontium aluminate (SrAl₂O₄: Eu²⁺, Dy³⁺)-based long afterglow powders. This article begins by describing the importance of road markings and the need to improve their visibility and durability at night and in adverse weather conditions. Subsequently, the current passive and active methods for improving the visibility of marking materials are discussed in detail, focusing on the advantages of aluminate long afterglow materials and challenges related to their hydrolysis and thermal stability. Through the application of organic–inorganic composite coating technology, the water resistance and thermal stability of the materials can be improved, thus enhancing the performance of road markings. This article also summarizes the current research status of different types of long afterglow road marking coatings. It analyzes the luminescence mechanism of aluminate long afterglow materials. Additionally, this article discusses future research directions and application prospects. The aim is to provide technical references and support for the wide application of long afterglow self-luminous road marking coatings.

Pavement cracking is a primary cause of early damage in asphalt pavements, and fiber-reinforcement technology is an effective method for enhancing the anti-cracking performance of pavement mixtures. However, due to the multi-scale dispersed structure of pavement mixtures, it is challenging to address cracking and damage with a single fiber type or fibers of the same scale. To investigate the toughening mechanisms and damage behavior of hybrid-fiber-modified mixtures, we analyzed the fracture process and damage behavior of these mixtures using a combination of basalt fiber and calcium sulfate whisker hybrid fiber modification, along with semicircular bending tests. Additionally, digital imaging was employed to examine the fracture interface characteristics, revealing the toughening mechanisms at play. The results demonstrated that basalt fibers effectively broaden the toughness range of the modified mixture at the same temperature, reduce mixture stiffness, increase residual load at the same displacement, and improve crack resistance in the mixture matrix. While calcium sulfate whiskers enhanced the peak load of the mixture, their high stiffness modulus was found to be detrimental to the mixture’s crack toughness. The fracture interface analysis indicated that the three-dimensionally distributed fibers form a spatial network within the mixture, restricting the relative movement of cement and aggregate, delaying crack propagation, and significantly improving the overall crack resistance of the mixture.