This study aims to quantify the effect of process parameters on the anodizing of Al6061 aluminum. To achieve this, studies on layer thickness, the porosity of the anodized surface, electrochemical techniques, X-ray diffraction, grain size estimation, and statistical analysis were conducted for three different atmospheres (without air, air, and oxygen). Parameter levels were established as follows: temperature (30 °C, 45 °C, and 60 °C), time (20 min, 40 min, and 60 min), electrolyte concentration (0.5 M), voltage (9 V), and current intensity (0.600 A). A 3³ experimental design (three factors, three levels) was proposed, and mathematical models were obtained using general factorial design. The experimental design was used to determine the three most important variables in the optimal condition. A total of 27 tests were conducted using sulfuric acid electrolytic solutions, of which 12 samples were selected by the factorial design method, which simultaneously evaluates the effects of factors and their interactions in a single experiment. Measurement of porosity and oxide layer thickness was performed using scanning electron microscopy. The purity of the anodic layer formed was characterized using X-ray diffraction techniques with a vertical goniometer X-ray diffractometer. The electrochemical behavior is presented through potentiodynamic polarization curves for the anodic layer. A general factorial design and an analysis of variance (ANOVA) were conducted to establish the significant factors for layer thickness, grain size, and reaction rate. Finally, the best results and their parameters for each response are presented.

The influence of double continuous cold rolling followed by annealing on the texture evolution and mechanical properties of a commercial low-carbon ferritic steel was investigated. Ultrathin sheets (final thickness 0.22 mm) were produced through a two-stage cold rolling process with intermediate and final annealing at 690 °C for 35 s, followed by light temper rolling at 100 °C for 20 s. Texture evolution was characterized using Electron Backscatter Diffraction (EBSD) with Orientation Imaging Microscopy (OIM), producing pole figures and orientation distribution functions (ODFs). Mechanical properties were evaluated through Vickers microhardness and ultimate tensile strength measurements obtained from three independent locations per sample. Quantitative ODF analysis (φ₂ = 45°) revealed that γ-fiber ({111}//ND) intensity increased after each cold reduction stage and decreased after annealing due to recrystallization. The α-fiber (110/RD) and cube components (001//RD) showed a slight increase after annealing. The final ultrathin sheet exhibited moderate γ-fiber intensity (≈3 M.R.D), low Vickers microhardness (100–150 HV), and tensile strength (400–450 MPa). These results demonstrate controlled evolution of texture and microstructure during double cold rolling and annealing, providing a basis for future studies on forming-related behavior without directly assessing formability.