Foam insulation materials are widely used in the construction industry due to their low thermal conductivity attributable to their microstructures and their low-conductivity blowing agents and affordability. In this study, we evaluate how the thermal performance of foam insulation materials used for the exterior walls of buildings, viz., extruded polystyrene (XPS), polyisocyanurate (PIR), and phenolic foam (PF), age over the life cycle of a building. To compare the aging of thermal performance during the life cycle of a building, each material was tested at 70 and 110 °C and with slicing acceleration according to EN and ISO standards. The thermal conductivity of each foam insulation material was measured using a heat flow meter at an operating temperature of 23 °C and converted into thermal resistance values. Different foam insulation materials have different aging procedures according to material-specific EN standards, while ISO 11561 applies the same procedure to all material classifications. Upon comparing the aged values according to ISO and EN standards to the initial values, the analysis showed a change rate of 23 to 26% in PIR and 18 to 20% in PF. In XPS, a rate of change of 10 to 23.8% was calculated. Our results indicated that the slicing acceleration induced a thermal resistance reduction rate about three times faster than aging at 70 °C. However, the long-term changed thermal resistance values of the foam insulation material applied via the calculating procedure specified in the ISO and EN standards were similar.

Green remodeling and retrofitting are effective strategies for enhancing the sustainability of existing buildings. While green remodeling involves significant structural modifications, green retrofitting typically focuses on improving energy efficiency and reducing environmental impact. However, easy-to-implement green retrofit technologies can be particularly valuable for low-income communities, offering a more affordable way to upgrade residences without extensive renovations. This paper analyzed the effectiveness of newly developed, easy-to-implement green retrofit technologies for windows in reducing heating energy use and greenhouse gas emissions. We conducted experiments using secondary glazing and windproof materials to enhance the thermal insulation and air-tightness performance of a residential building. Subsequently, we simulated the effectiveness of these green retrofit technologies under various conditions for residential buildings. In addition, we analyzed utility bills using data collected from residents. Our findings demonstrated an average reduction of 10–15% in heating energy consumption through the implementation of these green retrofit technologies for windows in older residential buildings.

International standards for vacuum insulation panels (VIPs) include an accelerated test method and a minimum quality standard for evaluating their long-term thermal performance after 25 years. The accelerated test method consists of various tests according to the characteristics of the core material and requires six months (180 days) at minimum. Herein, we propose an accelerated method for determining the long-term thermal performance of fumed-silica VIPs by shortening the required time and simplifying the procedure. Highly accelerated conditions (80 °C and 70% Relative humidity (RH)) were set for the evaluation method, using the maximum temperature (80 °C) cited in international standards and compared with the accelerated test method under accelerated conditions (50 °C and 70% RH). The inner-pressure increase rate of the VIP samples after conditioning for approximately 70 days was similar to that after conditioning for 180 days under highly accelerated and accelerated conditions, respectively. In addition, the estimated long-term thermal conductivities of the fumed-silica VIP were derived as 0.0076 and 0.0054 W/m·K under highly accelerated and accelerated conditions, respectively. These accelerated methods can be used to produce fumed-silica VIPs with similar long-term thermal conductivities. Therefore, the accelerated test method for long-term thermal performance using the highly accelerated conditions can be evaluated using a test that involves conditioning the sample for approximately 70 days under 80 °C and 70% RH.

Although foamed plastic insulation is widely used in construction in the Korean market, it is vulnerable to fire. To improve the flame retardancy, the method of flame-retardant coating with the EG in water-soluble state on the surface of expanded polystyrene (EPS) beads has been widely used. However, polystyrene beads coated with a water-soluble flame retardant easily separate the coated flame retardant in manufacturing. In this study is devised a flame-retardant coating and two steps of coating process for adhering the flame-retardant coating film evenly to the surface of the polystyrene bead without exfoliation. It was analyzed whether a flame-retardant EPS (FR-EPS) with excellent flame retardancy could be manufactured using polystyrene beads coated in this way. Ten FR-EPS samples satisfied the HF-1 and V-0 levels in horizontal and vertical burning tests, respectively. The THR of eight FR-EPS samples for ten minutes did not exceed 8 MJ∙m⁻² and the maximum HRR did not exceed 200 kW∙m⁻² for more than ten consecutive seconds. FR-EPS passed the building material standard of semi-nonflammability in Korean regulations, in contrast to commercial EPS, which have not passed the semi-nonflammability standard. It was also analyzed how effective the designed coating is in this study, comparing it with composites that were planned to improve the flame resistance of polystyrene, as reported in the literature. Flame Retardancy Index (FRI) values of FR-EPS proved the “excellent” level and had higher values compared with other polystyrene composites. These results demonstrated that the coated EPS containing a water-soluble flame retardant manufactured from EG and two steps of application with the coating solution achieved fire safety standard regulations.

Various studies on the envelope renovation of existing residential buildings have quantified energy savings effects across various climate conditions and building types yet have also reported discrepancies between predicted and actual energy savings performance. Given that identical technical improvements can yield substantially different actual outcomes depending on occupants’ behavioral adaptation patterns, renovation effect evaluation requires a multifaceted approach incorporating occupant behavioral changes. This case study empirically analyzed the effects of envelope renovation on occupants’ actual heating operation patterns. Envelope renovation effects applied to a 30-year-old apartment were analyzed by subdividing temperature conditions, with comparative evaluation using a non-renovated adjacent unit within the same building as a reference. While recognizing the inherent limitations of single-case analysis, this study presents a novel methodological framework for capturing subtle behavioral shifts through high-resolution temperature-specific analysis. Change-point models utilizing utility billing data were employed to analyze threshold temperature changes, and daily heating water-consumption estimation algorithms were applied to track heating pattern changes according to outdoor temperature variations. Results showed heating energy reduction despite more severe climate conditions post-renovation, with particularly pronounced savings under mild conditions. The upper limit of temperature ranges showing high heating dependency shifted downward from pre-renovation levels, improving to levels lower than the reference unit’s upper limit, demonstrating envelope performance enhancement effects. These results provide quantitative evidence that envelope improvements directly influence occupants’ heating decision-making criteria, though broader validation across multiple cases would strengthen these findings. This study quantifies envelope renovation effects not only in terms of energy savings, but also from the perspectives of occupant behavioral changes and comparison with reference units, presenting a novel evaluation methodology for effective energy efficiency improvements in aging buildings.