New types of materials were produced by gradual heating of a conducting polymer, polypyrrole, to elevated temperatures.

Common latex coatings suffer from poor water resistance, which often limits their practical application. This paper reports on the preparation of polyacrylate latexes using various approaches to tune the water resistance, wettability, and surface properties of their coating films. The mutual effects of fluorinated monomer copolymerization, emulsifier type (polymerizable and general), and intra- or interparticle covalent crosslinking (due to allyl methacrylate copolymerization and a keto-hydrazide reaction, respectively) were studied. The polyacrylate latexes were synthesized through a two-step semicontinuous emulsion polymerization of 2,2,2-trifluoroethyl methacrylate, butyl acrylate, methyl methacrylate, and methacrylic acid as the basic monomers. The fluorinated monomer was incorporated into the second-step polymer (at a content of 30 wt.% based on the second-step monomer feeds). The water resistance, wettability, and surface properties of the coating films were evaluated with focus on the water absorption, water whitening, water contact angle, and surface topography using atomic force microscopy. It was found that highly water-resistant and hydrophobic coatings that possessed a self-healing ability were prepared, provided that the polymerizable emulsifier and the fluorinated monomer were involved in the latex synthesis, along with the intra- and interparticle covalent crosslinking.

This work addresses the possibilities of using synthesized novel magnesium complex dyes in zinc pigmented organic coatings based on epoxyester resin to reduce the zinc content in these coatings while maintaining or increasing the anticorrosive efficiency of them. The magnesium complexes Mg-Dye-I (C₃₄H₂₆MgN₈O₆), Mg-Dye-II (C₂₆H₁₉MgN₃O₅), Mg-Dye-III (C₁₇H₁₀MgN₂O₃), and Mg-Dye-IV (C₂₅H₁₈MgN₄O₆) with a series of azo carboxylate ligands were prepared from the diazo-coupling reaction of anthranilic acid with 5-methyl-2-phenyl-3-pyrazolone (Dye I; C₁₇H₁₄N₄O₃), anthranilic acid with naphthol AS-PH (Dye II; C₂₆H₂₁N₃O₅), anthranilic acid with 2-naphthol (Dye III; C₁₇H₁₂N₂O₃), and 2-amino-5-nitrophenol with naphthol AS-PH (Dye IV; C₂₅H₂₀N₄O₆). The synthesized novel magnesium complex dyes were characterized by analytical methods. Model coatings containing these dyes at pigment volume concentrations (PVCs) = 1, 3, 5 and 10% and zinc at a ratio of pigment volume concentration/critical pigment volume concentration (PVC/CPVC) = 0.60 were formulated to study the inhibitory properties of the individual synthesized magnesium complex dyes. Model coatings containing inorganic pigments (MgO and Ca-Mg-HPO₄) at PVCs = 1%, 3%, 5% and 10% and zinc at PVC/CPVC = 0.60 were also formulated. The coating pigmented only by zinc at PVC/CPVC = 0.60 was prepared as a standard organic coating. Corrosion resistance was also evaluated by potentiodynamic polarization studies and electrochemical impedance spectroscopy. The properties of organic coatings were also tested using other standardized and derived corrosion tests. In addition, the mechanical properties of the studied organic coatings were determined using standard tests. The aim of the work was to verify the possible synergistic efficiency of novel magnesium complex dyes by improving the mechanical, anti-corrosion, and chemical properties of zinc pigmented organic coatings.